Effect of applying carbodiimide combined with a two-step self-etch adhesive durability.

BACKGROUND: This study investigated the effect of carbodiimide (EDC) combined with Clearfil SE self-etch adhesive on the shear bond strength (SBS), crosslinking degree, denaturation temperature, and enzyme activity of dentin in vitro. MATERIALS AND METHODS: Collected human sound third molars were randomly divided into different groups with or without EDC treatment (0.01-1 M). The specimens (n = 16)were stored for 24 h (immediate) or 12 months (aging) before testing the SBS. Fine dentin powder was obtained and treated with the same solutions. Then the crosslinking degree, denaturation temperature (Td), and enzyme activity were tested. Statistical analysis was performed using a one-way analysis of variance (ANOVA) to compare the differences of data between groups (α = 0.05). RESULTS: There was a significant drop in immediate SBS and more adhesive fracture of 1.0 M EDC group, while there were no significant differences among the other groups. SEM showed a homogeneous interface under all treatments. After 12 months of aging, the SBS significantly decreased. Less decreases of SBS in the 0.3 and 0.5 M groups were found. Due to thermal and enzymatical properties consideration, the 0.3 and 0.5 M treatments also showed higher cross-link degree and Td with lower enzyme activity. CONCLUSION: 0.3 and 0.5 M EDC may be favorable for delaying the aging of self-etch bond strength for 12 months. But it is still needed thoroughly study.

Comparative cell viability of dentin-bonding adhesive systems on human dental pulp stem cells: time-dependent analysis.

BACKGROUND: Restorative materials are in prolonged contact with living tissues such as oral mucosa, dentin, pulp, periodontal, and periapical tissues. Therefore, the potentially harmful effects of these materials and their components on oral tissues should be evaluated before clinical use. This study aimed to compare the cell viability of different adhesive systems (ASs) on human dental pulp stem cells (hDPSCs). METHODS: Three ASs that combining methacryloyloxydecyl dihydrogen phosphate (MDP) monomer with new hydrophilic amide monomers [Clearfil Universal Bond Quick(CUBQ), Kuraray Noritake], self-reinforcing 3D monomer [Bond Force II(BFII), Tokuyama)], and dual-cure property [Futurabond DC(FBDC), VOCO] were used. Three (n = 3) samples were prepared for each group. Dental pulp stem cells were isolated from ten patients' extracted third molar teeth. Samples were incubated in Dulbecco's modified Eagle's medium (DMEM) for 24 h (h), 72 h, and 7 days (d) to obtain extracts. For the control group, cells were cultured without DBA samples. Cell viability of ASs extracts was measured using a cell proliferation detection kit (WST-1, Roche). Statistical analysis was performed using two-way ANOVA and post-hoc (Duncan) tests (p < 0.05). RESULTS: At 24 and 72 h statistically significant differences were determined between control and BFII, control and FBDC groups (p < 0.05), while no differences between control and CUBQ groups (p > 0.05). On the 7th d, statistically significant differences were found between the control and experimental groups (p < 0.05), while no differences between experimental groups (p > 0.05). A statistically significant difference was detected for the BFII group over the three-time interval (p < 0.05). The lowest cell viability was observed for the FBDC group at 24 h, and the difference was statistically significant when compared with 72 h and 7th d (p < 0.05). CONCLUSION: All ASs showed different cell viability values at various exposure times. It should be taken into consideration that pH values, as well as the contents of ASs, have a significant effect on the cell viability.

Ultrasonic activation of adhesive systems increases bond strength and intratubular penetration of resin cement in root dentin subjected to radiation therapy.

OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.

The Influence of Erbium Laser Pretreatment on Dentin Shear Bond Strength and Bond Failure Modes: A Systematic Review and Network Meta-Analysis.

PURPOSE: To systematically review in-vitro studies that evaluated the influence of erbium laser pretreatment on dentin shear bond strength (SBS) and bond failure modes. MATERIALS AND METHODS: Electronic databases (PubMed, Cochrane Central, Embase, and Web of Science) were searched. Only in-vitro studies involving erbium laser irradiation of the dentin surface and SBS testing of the bonded resin block were included. The three common modes of bond failure (1. adhesive, 2. cohesive, and 3. mixed) were observed and analyzed. The network meta-analysis (NMA) was performed by Stata 15.0 software, the risk of bias was evaluated, and the certainty of the evidence was assessed by the Confidence in Network Meta-analysis (CINeMA). RESULTS: Forty studies with nine pretreatments (1. blank group: BL; 2. phosphoric acid etch-and-rinse: ER; 3. self-etch adhesive: SE; 4. Er:YAG laser: EL; 5. Er,Cr:YSGG laser: ECL; 6. ER+EL; 7. ER+ECL; 8. SE+EL; 9. SE+ECL) were included in this analysis. The NMA of SBS showed that ER+EL [SMD = 0.32, 95% CI (0.11, 0.98)] had the highest SBS next to ER, especially when using one of the 3M ESPE adhesives, followed by EL, ECL, SE and SE+EL. The Ivoclar Vivadent adhesives significantly increased the SBS of the ECL [SMD = 0.37, 95% CI (0.16,0.90)] and was higher than ER+EL [SMD = 0.25,95% CI (0.07,0.85)]. Finally, the surface under the cumulative ranking curve (SUCRA) value indicated that ER+EL (SUCRA = 71.0%) and EL (SUCRA = 62.9%) were the best treatments for enhancing dentin SBS besides ER. ER+EL (SUCRA = 85.3%), ER (SUCRA = 83.7%) and ER (SUCRA = 84.3%) had the highest probability of occurring in adhesive, cohesive and mixed failure modes, respectively. CONCLUSION: Er:YAG and Er,Cr:YSGG lasers improved dentin SBS compared to the blank group, especially when the acid etch-and-rinse pretreatment was combined with Er:YAG laser. Shear bond strength and failure mode do not appear to be directly related.

A new method of adhesive system application improves the bond strength between fiber post and root dentin.

This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

Can a dentin bonding agent prevent color change in regenerative endodontic procedures? An in vitro evaluation.

This in vitro study aimed to determine the efficacy of dentin bonding agents in preventing color changes following Regenerative Endodontic Procedures. One hundred twenty bovine incisors were endodontically prepared and randomly assigned to a two main factors design: application of a dentin bonding agent (Scotchbond Adper, 3M ESPE, St Paul, MN, USA) in the pulp chamber (Group 1, n=60) versus no bonding intervention (Group 2, n=60), and five levels of intracanal medication (n=12/subgroup): Triple antibiotic paste (TAP), double antibiotic paste (DAB), calcium hydroxide (CH), modified triple antibiotic paste (TAPM), and Control (CTL). Color changes were measured over 28 days at multiple time points (1, 3, 7, 14, 21, and 28 days) using the CIEDE2000 formula to calculate the color difference (ΔE00) from baseline (T0). The ΔE00 quantifies the perceptible color difference between the initial and final tooth color, with lower values indicating less discoloration. The results were analyzed using repeated measures ANOVA-2 and post-hoc Holm-Sidak tests. The TAP subgroups, both with and without the bonding agent, exhibited the highest color variation. However, a pulp chamber seal with a bonding agent showed a protective effect against discoloration compared to no seal, even though complete prevention was not achieved. All groups demonstrated ΔE00 values beyond acceptable interpretation thresholds for clinical application, primarily driven by a reduction in lightness (L*) and a decrease in redness (a* value, shifting towards green). In conclusion, while the pulp chamber seal with a bonding agent mitigated TAP-induced discoloration, it did not eliminate it.

Equivalence study of the resin-dentine interface of internal tunnel restorations when using an enamel infiltrant resin with ethanol-wet dentine bonding.

This preregistered ex vivo investigation examined the dentinal hybrid layer formation of a resinous infiltrant (Icon), with reference to both thickness (HLT) and homogeneity when combined with modified tunnel preparation (occlusal cavity only) and internal/external caries infiltration. The adhesives Syntac and Scotchbond MP were used as controls (Groups 1 and 3) or in combination with Icon (Groups 2 and 4). A split-tooth design using healthy third molars from 20 donors resulted in 20 prepared dentine cavities per experimental group. The cavity surfaces (n = 80) were etched (37% H3PO4), rinsed, and air-dried. Rewetting with ethanol was followed by application of the respective primers. After labeling with fluorescent dyes, either Syntac Adhesive/Heliobond or Scotchbond MP Adhesive was used alone or supplemented with Icon. HLT, as evaluated by scanning electron microscopy, did not significantly differ (P > 0.05), and confocal laser scanning microscopy revealed homogeneously mixed/polymerized resin-dentine interdiffusion zones in all groups. Icon can be successfully integrated into an ethanol-wet dentine bonding strategy, and will result in compact and homogeneous hybrid layers of comparable thickness considered equivalent to the non-Icon controls, thus allowing for preservation of the tooth's marginal ridge and interdental space in the case of internal/external infiltration of proximal caries.

Effect of dentin surface conditions and curing mode of resin cement on the dentin bond strength.

This study investigates the effects of dentin's drying time, roughness, and curing modes of resin cement on bond strength. Forty human teeth were divided into eight groups based on three experimental factors: dentin's roughness by 240-or 600-grit SiC paper (coarse or fine), dentin wetness with air-drying time (5-s or 10-s), and Single Bond Universal adhesive's curing mode by co-curing with RelyX Ultimate cement or light-curing separately (co-curing or light-curing). The micro-tensile bond strength of fifteen resin-dentin stikcs per groups was measured. Failure mode and adhesive layers were observed using stereoscopic and confocal laser scanning microscopy, respectively. The curing mode of the adhesive layer affected the bond strength of the dentin-resin cement (p<0.05). In particular, the light-curing mode exhibited a significantly higher bond strength than the co-curing one (p<0.05). The bond strength between the resin cement and dentin was improved in the 5-s drying groups than in the 10-s drying groups.

Effects of dentin bonding agents and silanization on bond strength between 3D printed resin and composite resin.

This study aimed to evaluate the effects of dentin bonding agents and silanization on the bond strength between 3D printed resin and composite resin and compare it with a conventional composite resin. 3D printed resin cylinders (PCB) and composite resin substrates (Z250) were prepared and divided into eight subgroups based on the bonding agents used (n=12). The shear bond strength was measured using a universal testing machine, and the failure modes were evaluated. The bond strength was found to vary significantly among the bonding agents and substrate types. Silane application did not significantly improve the bond strength. Among the bonding agents, the universal adhesives exhibited the highest bond strengths for both substrates. Compared to PCB, Z250 demonstrated stronger bonds and exhibited more cohesive failures. Further research is needed to optimize the surface treatments and resin formulations for enhanced bond strength and durability between 3D printed and composite resins.

Bond strength and marginal adaptation of resin composites and correlations with clinical results.

OBJECTIVES: Due to innumerable confounding factors and a high number of types and brands of dental restorative materials, the clinical performance of restorative materials are sought predicted by various in vitro tests. However, only few such tests have been found to correlate well with clinical findings. Thus, the present study determined the in vitro dentin bond strength and marginal adaptation of Class II restorations and correlated the results to their clinical outcomes. METHODS: Dentin bond strength (µTBS and µSBS) and marginal gap formation of Class II restorations (replica technique and SEM) were measured after 24 h and 6 m water storage using eight combinations of adhesive and resin composite. Clinical outcomes (mean survival time, Hazard Ratio, annual failure rate; n = 10.695) were gained from a data set of a retrospective multicenter study of direct restorations. RESULTS: Significant differences were found for dentin bond strength and marginal gap formation between the restorative material groups, and negative effects of long-term storage were observed. µTBS correlated significantly with certain clinical outcomes of Class I restorations, while µSBS correlated with certain clinical outcomes of Class II, III, IV and V restorations. Marginal gap formation in enamel and number of paramarginal fractures correlated with certain clinical outcomes of Class II restorations. SIGNIFICANCE: Using the same restorative materials in vitro as in vivo, gave significant, but weak correlations between in vitro bond strength or marginal adaptation and clinical outcomes, lending support to the use of in vitro tests in early stages of material selection.

Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

Micro-shear Bond Strength of an Alternative Self-etch Application of "No Wait" Universal Adhesive to Caries-affected and Sound Dentin in Permanent and Primary Teeth.

OBJECTIVE: This study aimed to compare the micro-shear bond strength (µSBS) of caries-affected dentin (CAD) and sound dentin (SoD) in primary and permanent teeth using an alternative self-etch application of "no wait" universal adhesive. METHODS AND MATERIALS: Flat midcoronal dentin surfaces from 72 permanent third molars and 72 second primary molars were distributed randomly into 12 groups according to the substrate SoD and artificially-created CAD (pH cycling for 14 days) and the adhesive system (GLUMA Bond5, a two-step etch & rinse adhesive, GLUMA Bond, a one-step self-etch adhesive, and Tokuyama Universal Bond, a one-step self-etch adhesive) (n=12). Bonded dentin resin discs were put through micro-shear bond strength testing after 10,000 thermocycles. The results were evaluated using two-way ANOVA and the Bonferroni test with a significance level of α = 0.05. RESULTS: When compared to SoD, the etch & rinse system's test results on artificially created CAD showed a statistically significant poorer bonding performance in both permanent and primary teeth in all groups (p<0.05). While the bond strengths of permanent teeth using total-etch adhesive on sound dentin were statistically significantly higher than those using Tokuyama Universal Bond adhesive (p<0.05), there was no significant difference in sound dentin in primary teeth (p>0.05). CONCLUSIONS: The etch & rinse system performed the poorest of all adhesive systems on CAD. The Tokuyama Universal Bond's adhesive strength was similar in SoD and CAD on primary teeth. The use of Tokuyama Universal Adhesives can speed up restorative treatment in pediatric dentistry.

A scoping review of the influence of clinical contaminants on bond strength in direct adhesive restorative procedures.

OBJECTIVE: Clinical contamination during direct adhesive restorative procedures can affect various adhesive interfaces differently and contribute to bulk failure of the restorations. This review aims to summarise the current knowledge on the influence of a variety of clinical contaminants on the bond strength at various adhesive interfaces during adhesive restorative procedures and identify gaps in the literature for future research. DATA AND SOURCES: An electronic database search was performed in PubMed and EMBASE to identify articles that investigated the influence of contaminants on direct restorative bonding procedures. A data-charting form was developed by two researchers to capture the key characteristics of each eligible study. STUDY SELECTION: The initial search yielded 1,428 articles. Fifty-seven articles published between 1 Jan 2007 and 25 Oct 2023 were included in the final review. Thirty-three of the articles examined the influence of saliva contamination, twelve articles examined the influence of blood contamination, and twenty-five articles examined the influence of other contaminants. CONCLUSION: Saliva contamination exerted less influence on the decrease in bond strength when self-etch systems were used, compared to when etch-and-rinse systems were used. Blood contamination adversely affected the bond strength at the interface between resin composite and dentine, and resin composite and resin-modified glass ionomer cement. Treating contaminated surfaces with water spray for 10-30 s followed by air drying could be effective in recovering bond strength following saliva and blood contamination. CLINICAL SIGNIFICANCE: This scoping review provides a valuable overview of the range of potential clinical contaminants that can influence the bond strength between different interfaces in direct adhesive restorative procedures. Additionally, it identifies potential decontamination protocols that can be followed to restore and enhance bond strength.

Evaluation of Microbiological Susceptibility and Long-term Adhesive Properties to Dentin of Primers with Terminalia catappa Linn.

PURPOSE: To investigate the antibacterial effects of Terminalia catappa Linn (TCL) leaf extracts at different concentrations and the effects of these extracts used as primers on the long-term adhesive properties of two universal adhesives. MATERIALS AND METHODS: After extract preparation, the antimicrobial and antibacterial activities of TCL against Streptococcus mutans (UA 159) were assessed in microdilution assays to provide the minimal inhibitory concentration (MIC) and minimal bactericidal concentration (MBC). Additionally, to provide quantitative data on the ability of TCL extract to reduce cell viability, colony forming units (CFU) were counted. To examine adhesive properties, 288 human molars were randomly assigned to 32 experimental conditions (n = 9) according to the following variables: (1) treatment agent: negative control (untreated surface), and primers at concentrations of 1xMIC, 5xMIC, and 10xMIC; (2) adhesives: Scotchbond Universal (SBU) and Futurabond Universal (FBU); (3) adhesive strategy: etch-and-rinse (ER) or self-etch (SE); and (4) storage time: 24 h or after 2 years. Primers were applied for 60 s, upon which the teeth were incrementally restored and sectioned into adhesive-dentin bonded sticks. These were tested for microtensile bond strength (µTBS) and nanoleakage (NL) after 24-h and 2-year water storage, as well as in-situ degree of conversion (DC) at 24 h. The chemical profile of the hybrid layer was determined via micro-Raman spectroscopy. Biofilm assay data were analyzed using the Kruskal-Wallis test; the pH of culture media and the chemical profile were analyzed by one-way ANOVA. The adhesive properties (µTBS, NL, DC) were evaluated using a four-way ANOVA and Tukey's test. Significance was set at 5%. RESULTS: Similar values of MIC and MBC were observed (2 mg/ml), showing bactericidal potential. CFU analysis demonstrated that concentrations of 5xMIC and 10xMIC significantly inhibited biofilm formation (p < 0.001). The application of the TCL primer at all concentrations significantly increased the immediate µTBS and DC, and decreased the immediate NL values when compared to the control group (p < 0.05), regardless of the adhesive and adhesive strategies. Despite an increase in the NL values for all groups after 2 years (p > 0.05), in groups where the TCL primer was applied, the µTBS remained constant after 2 years for both adhesives, while a decrease in the µTBS was observed in the control groups (p < 0.05). Usually, 10xMIC showed better results than 1xMIC and 5xMIC (p < 0.05). The application of TCL promoted cross-linking; cross-linking rates increased proportionally to the concentration of TCL (p < 0.05). CONCLUSION: Primers containing TCL promoted bactericidal and bacteriostatic action, as well as cross-linking with dentin, while maintaining the adhesive properties of the adhesive-dentin interface after 2 years of water storage.

Use of marine occurrent extracts to enhance the stability of dentin extracellular matrix.

Chitosan (CS) and phloroglucinol (PhG), two extracts abundantly found in marine life, were investigated for their ability to biomodify demineralized dentin by enhancing collagen crosslinks and improving dentin extracellular matrix (ECM) mechanical and biochemical stability. Dentin obtained from non-carious extracted human molars were demineralized with phosphoric acid. Baseline Fourier-transform infrared (FTIR) spectra, apparent flexural elastic modulus (AE) and dry mass (DM) of each specimen were independently acquired. Specimens were randomly incubated for 5 min into either ultrapure water (no-treatment), 1% glutaraldehyde (GA), 1% CS or 1% PhG. Water and GA were used, respectively, as a negative and positive control for collagen crosslinks. Specimens' post-treatment FTIR spectra, AE, and DM were obtained and compared with correspondent baseline measurements. Additionally, the host-derived proteolytic activity of dentin ECM was assessed using hydroxyproline assay (HYP) and spectrofluorometric analysis of a fluorescent-quenched substrate specific for matrix metalloproteinases (MMPs). Finally, the bond strength of an etch-and-rinse adhesive was evaluated after application of marine compounds as non-rinsing dentin primers. Dentin specimens FTIR spectral profile changed remarkably, and their AE increased significantly after treatment with marine compounds. DM variation, HYP assay and fluorogenic substrate analysis concurrently indicated the biodegradation of CS- and PhG-treated specimens was significantly lesser in comparison with untreated specimens. CS and PhG treatments enhanced biomechanical/biochemical stability of demineralized dentin. These novel results show that PhG is a primer with the capacity to biomodify demineralized dentin, hence rendering it less susceptible to biodegradation by host-proteases.

Assessment of physical properties of bioactive glass-modified universal multimode adhesive and its bonding potential to artificially induced caries affected dentin.

BACKGROUND: To evaluate the physical properties of bioactive glass-modified universal multimode adhesive and its micro-tensile bond strength (µTBS) to artificially induced caries-affected dentin. METHODS: All bond universal adhesive was used in the study. Specimens were divided into 2 main groups: control unmodified adhesive and 5 wt% BAG modified adhesive. The degree of conversion, pH, bioactivity, and viscosity of the adhesives were tested with n = 5 for each test. Micro-tensile bond strength evaluation was done in etch & rinse (ER) and selective-etch (SE) modes, where 24 human molar teeth were used (n = 3), 12 teeth for immediate bond strength, and the other 12 were tested after 6 months of storage in simulated body fluid (SBF). RESULTS: No significant difference was found between the control and the 5wt% BAG groups regarding the degree of conversion (61.01 ± 0.43 and 60.44 ± 0.61 respectively) and the viscosity (109.77 ± 22.3 and 124.3 ± 9.92 respectively). The control group revealed significantly lower pH values than the 5wt% BAG group (3.16 ± 0.5 and 4.26 ± 0.09 respectively). Immediate bond strength results revealed that the 5wt% BAG in the ER mode had the highest bond strength followed by the control group in the ER mode (44.16 ± 7.53 and 44.00 ± 7.96 respectively). SE groups showed that the immediate strength of the 5wt% BAG group was higher than the control group (42.09 ± 6.02 and 39.29 ± 6.64 respectively). After 6 months of storage, bond strength results revealed a decrease in bond strength values for the control groups but not for the 5wt% BAG in both application modes. CONCLUSIONS: The incorporation of BAG (5wt%) improved the universal adhesive micro-tensile bond strength and bond durability for both adhesive application modes without affecting its degree of conversion or viscosity.

Effect of Salvadora persica on resin-dentin bond stability.

BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.

Promoting bond durability by a novel fabricated bioactive dentin adhesive.

OBJECTIVE: To prepare a bioactive dentin adhesive and investigate its effect on promoting bonding durability of dentin. METHODS: The mineralization of the bioactive glass with high phosphorus (10.8 mol% P2O5-54.2 mol% SiO2-35 mol% CaO, named PSC) and its ability to induce type I collagen mineralization were observed by SEM and TEM. The Control-Bond and the bioactive dentin adhesive containing 20 wt% PSC particles (PSC-Bond) were prepared, and their degree of conversion (DC), microtensile bond strength (µTBS), film thickness and mineralization performance were evaluated. To evaluate the bonding durability, dentin bonding samples were prepared by Control-Bond and PSC-Bond, and mineralizated in simulated body fluid for 24 h, 3 months, and 6 months. Then, the long-term bond strength and microleakage at the adhesive interface of dentin bonding samples were evaluated by microtensile testing and semiquantitative ELIASA respectively. RESULTS: The PSC showed superior mineralization at 24 h and induced type I collagen mineralization to some extent under weakly alkaline conditions. For PSC-Bond, DC was 62.65 ± 1.20%, µTBS was 39.25 ± 4.24 MPa and film thickness was 17.00 ± 2.61 µm. PSC-Bond also formed hydroxyapatite and maintained good mineralization at the bonding interface. At 24 h, no significant differences in µTBS and interface microleakage were observed between the Control-Bond and PSC-Bond groups. After 6 months of aging, the µTBS was significantly higher and the interface microleakage was significantly lower of PSC-Bond group than those of Control-Bond group. SIGNIFICANCE: PSC-Bond maintained bond strength stability and reduced interface microleakage to some extent, possibly reducing the occurrence of secondary caries, while maintaining long-term effectiveness of adhesive restorations.

Comparisons of ammonia- and water-based silver-containing solutions on dentin bonding and enzymatic activity: 1-yr evaluation.

OBJECTIVE: To evaluate the effects of an ammonia-based and a water-based silver-containing solutions on bonding performance and matrix-metalloproteinases (MMPs) activity of a universal adhesive to dentin after 1 year of artificial aging. METHODS: Mid-coronal dentin surfaces of 60 sound human molars were exposed and the following groups were formed according to the surface pre-treatment and etching mode of the universal adhesive (Zipbond Universal, SDI) (n = 10): G1) Zipbond in the self-etch mode (ZSE); G2) Riva Star (SDI) applied before ZSE; G3) Riva Star Aqua (SDI) applied before ZSE; G4) Zipbond in the etch-and-rinse mode (ZER); G5) Riva Star applied before ZER; G6) Riva Star Aqua applied before ZER. The specimens were sectioned and subjected to microtensile bond strength (µTBS) test at baseline (T0) and after 12 months (T12) of artificial storage. Scanning electron microscope (SEM) and energy dispersive spectroscopy analysis (EDS) were also conducted. Three additional molars per group were processed for the in situ zymography analysis at T0 and T12. Data were statistically analyzed (p < 0.05). RESULTS: Dentin pre-treatments and aging decreased bonding values, regardless of the etching mode (p < 0.05). No differences in µTBS were observed between the two silver-containing solutions, both at T0 and T12. Riva Star Aqua and etching significantly increased the MMPs activity, independent of the storage period (p < 0.05). SIGNIFICANCE: Dentin surface pre-treatment with silver-containing solutions negatively affects the bonding performances of resin composite restorations placed with a universal adhesive. However, the ammonia-based product Riva Star might show better stability in the long term, due to lower activation of MMPs.

Influence of different immediate dentin sealing strategies on bond strength of indirect resin nanoceramic restorations.

In this study, we evaluated the effect of four different strategies for bonding a CAD/CAM resin nanoceramic restoration (Lava Ultimate, 3M) to the dentin surface using a universal adhesive (Scotch Bond Universal, 3M) and adhesive resin cement (RelyX Ultimate, 3M) on the shear bond strength (SBS) and failure mode. The strategies comprised: (i) immediate sealing, immediate bonding; (ii) immediate sealing, bonding after 2 weeks with provisional restoration; (iii) immediate sealing with flowable resin composite reinforcement and bonding after 2 weeks with provisional restoration; and (iv) no immediate sealing, and bonding after 2 weeks with provisional restoration. After bonding, all the specimens were thermocycled, shear tests were performed using a universal testing machine, and failure modes were determined using stereomicroscope and scanning electron microscopy. The highest mean SBS was recorded with immediate sealing, immediate bonding strategy. Most adhesive failures with exposed dentinal tubules were noted in specimens exposed to bonding after 2 weeks with no immediate sealing, which was associated with the lowest SBS. Mixed failures predominated in all immediate dentin sealing groups. Immediate sealing with universal adhesives improves SBS, particularly in the single-visit approach, which has shown significantly better performance, whereas the provisional phase has a negative effect.