Effect of Different Adhesive Resin and Composite Veneering Materials on Adhesion to Polyetheretherketone.

OBJECTIVE: To evaluate the effect of different adhesives and veneering resins on the shear bond strength (SBS) of polyetheretherketone (PEEK). METHODS: A total of 138 PEEK specimens were randomly divided into 6 groups according to adhesive material application: Control (C, no application), Adhese Universal (A) (Ivoclar Vivadent, Schaan, Liechtenstein), Gluma Bond Universal (G) (Heraeus Kulzer, South Bend, IN, USA), G-PremioBOND (P) (GC Corporation, Tokyo, Japan), Single Bond Universal (S) (3M, Saint Paul, MN, USA) and visio.link (V) (Bredent, Senden, Germany). Each adhesive group was divided into two subgroups according to the type of veneering material: Estenia direct composite (D) and Gradia Plus indirect composite (IN) (both GC Corporation). After the veneering process, the specimens were aged by thermal cycling. Kruskal-Wallis and Mann-Whitney U tests were used for SBS analysis (P < 0.05). RESULTS: The highest SBS results were obtained in the VIN group, followed by the VD, PD, GIN, AIN, AD, SIN, SD, PIN, GD, CIN and CD groups, respectively (P = 0.001). There were no significant differences in terms of the type of veneering composite when the same adhesive was applied (P > 0.05), except for Gluma Bond Universal (P = 0.009). All the adhesives tested showed clinically acceptable SBS results. CONCLUSION: Visio.link offered the highest adhesion to PEEK, whereas the tested universal adhesives may be used as an alternative to visio.link in clinical settings. It was determined that changing the veneer type has no statistical difference when the same adhesive material is used.

Engineering Interfacial Integrity with Hydrolytic-Resistant, Self-Reinforcing Dentin Adhesive.

The leading cause of composite restoration failure is secondary caries, and although caries is a multifactorial problem, weak, damage-prone adhesives play a pivotal role in the high susceptibility of composite restorations to secondary caries. Our group has developed synthetic resins that capitalize on free-radical polymerization and sol-gel reactions to provide dental adhesives with enhanced properties. The resins contain γ-methacryloxypropyltrimethoxysilane (MPS) as the Si-based compound. This study investigated the properties of methacrylate-based resins containing methacryloxymethyltrimethoxysilane (MMeS) as a short-chain alternative. The degree of conversion (DC), polymerization kinetics, water sorption, mechanical properties, and leachates of MMeS- and MPS-resins with 55 and 30 wt% BisGMA-crosslinker were determined. The formulations were used as model adhesives, and the adhesive/dentin (a/d) interfaces were analyzed using chemometrics-assisted micro-Raman spectroscopy. The properties of the 55 wt% formulations were comparable. In the 30 wt% BisGMA formulations, the MMeS-resin exhibited faster polymerization, lower DC, reduced leachates, and increased storage and loss moduli, glass transition (Tg), crosslink density, and heterogeneity. The spectroscopic results indicated a comparable spatial distribution of resin, mineralized, and demineralized dentin across the a/d interfaces. The hydrolytically stable experimental short-chain-silane-monomer dental adhesive provides enhanced mechanical properties through autonomous strengthening and offers a promising strategy for the development of restorative dental materials with extended service life.

Salivary levels of eluents during Invisalign™ treatment with attachments: an in vivo investigation.

BACKGROUND: The aim of the present study was to investigate qualitatively and quantitatively the elution of substances from polyester-urethane (Invisalign™) aligners and resin composite attachments (Tetric EvoFlow) in vivo. METHODS: Patients (n = 11) treated with the aligners and attachments (16 per patient, without other composite restorations) for an average of 20 months, who were planned for attachment removed were enrolled in the study. Patients were instructed to rinse with 50 mL of distilled water upon entry and the rinsing solution was collected (before removal). Then, the attachments were removed with low-speed tungsten carbide burs for adhesive residue removal, a thorough water rinsing was performed immediately after the grinding process to discard grinding particle residues, and subsequently, after a second water-rinsing the solution was collected for analysis (after removal). The rinsing solutions were analyzed for targeted (LC-MS/MS: Bis-GMA, DCDMA, UDMA, BPA) and untargeted (LC-HRMS: screening of leached species and their degradation products) compounds. RESULTS: Targeted analysis revealed a significant reduction in BPA after attachment removal (4 times lower). Bis-GMA, DCDMA, UDMA were below the detection limit before removal but were all detectable after removal with Bis-GMA and UDMA at quantifiable levels. Untargeted analysis reviled the presence of mono-methacrylate transformation products of Bis-GMA (Bis-GMA-M1) and UDMA (UDMA-M1), UDMA without methacrylate moieties (UDMA-M2), and 4-(dimethylamino) benzoic acid (DMAB), the degradation product of the photo-initiator ethyl-4-(dimethylamino) benzoate (EDMAB), all after attachment removal. Several amino acids and endogenous metabolites were also found both before and after removal. CONCLUSIONS: Elevated levels of BPA were traced instantaneously in patients treated with Invisalign™ and flowable resin composite attachments for the testing period. BPA was reduced after attachment removal, but residual monomers and resin degradation products were found after removal. Alternative resin formulations and attachment materials may be utilized to reduce eluents.

Characterization of dental light-curing resin composites incorporating multiple modified low-shrink monomers.

OBJECTIVE: Polymerization shrinkage poses a significant challenge in dental resin composites. The objective of this study is to introduce spiroorthocarbonate monomer 3,9-dimethylene-1,3,5,7-tetraoxa-spiro[5,5]undecane (BMSOC) and epoxy resin monomer 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate (ECHM-ECHC) into bisphenol-S-bis(3-methacrylato-2-hydroxy propyl)ether (BisS-GMA) based resin composites to develop composites with reduced shrinkage properties. METHODS: BMSOC and BisS-GMA were synthesized and thoroughly mixed with ECHM-ECHC, followed by inorganic fillers and photoinitiators. Based on the composition of the resin matrix, five groups of experimental composites were prepared, with traditional bisphenol A-dimethacrylate glycidyl ester (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) based composite serving as the control. The polymerization properties, including degree of conversion (DC) and polymerization shrinkage (PS), as well as marginal microleakage, wettability, flexural strength (FS), flexural modulus (FM), and biocompatibility were evaluated. RESULTS: The results demonstrated that compared with the control group, the PS of BisS-GMA based composites containing BMSOC and ECHM-ECHC were significantly reduced (P < 0.05), and the lowest PS (0.96 ± 0.08 %) was observed when the ratio of BisS-GMA: (Epoxy + BMSOC) was 4:6. Additionally, the experimental composites also exhibited improved DC, minimal microleakage, low hydrophilicity, enhanced mechanical properties, qualified in vivo biocompatibility, and slight/moderate in vitro biocompatibility. SIGNIFICANCE: The resin composites incorporating multiple modified low-shrink monomers are promising for dental applications to prevent various clinical problems caused by PS and extend restoration longevity.

A comparative study on the mechanical and antibacterial properties of BPA-free dental resin composites.

OBJECTIVE: The commonly used base monomer utilized in resinous commercial dental restorative products is bis-GMA which is derived from bisphenol-A (BPA) - a well-known compound which may disrupt endocrine functions. To address concerns about its leaching into the oral environment and to optimize the quality of dental composites, a BPA-free alternative base monomer, fluorinated urethane dimethacrylate (FUDMA), was designed by modifying a UDMA monomer system. METHODS: Nine groups of composites were prepared by mixing the base monomers and TEGDMA in a ratio of 70/30 wt% to which were added silanized glass particles (mean diameter: 0.7 µm) in 3 different volume fractions (40, 45, and 50 vol%). Bis-GMA and UDMA base monomers were used as control groups in the same ratios. Various properties including degree of conversion (DC), flexural strength (FS) and flexural modulus (FM), water sorption (WS), solubility (SL), surface hardness and roughness, and initial adhesion property against S.mutans were investigated. One-way analysis of variance followed by Bonferroni test at α = 0.05 was used to analyze the results. RESULTS: A significant difference in FS between FUDMA-based composite with 40 vol% filler (120.3 ± 10.4 MPa) and Bis-GMA-based composite with the same filler fraction (105.8 ± 10.0 MPa) was observed but there was no significant difference among other groups. The UDMA based group exhibited the highest WS (1.3 ± 0.3 %). Bis-GMA showed greater initial bacterial adhesion but was not statistically different from the other groups (p = 0.082). SIGNIFICANCE: FUDMA-based resin composites exhibit comparable mechanical and bacterial adhesion properties compared with Bis-GMA and UDMA-based composites. The FUDMA composites show positive outcomes indicating they could be used as substitute composites to Bis-GMA-based composites.

Surface alterations and compound release from aligner attachments in vitro.

AIM: The aim of the present study was to assess the alterations in morphology, roughness, and composition of the surfaces of a conventional and a flowable composite attachment engaged with aligners, and to evaluate the release of resin monomers and their derivatives in an aqueous environment. METHODS: Zirconia tooth-arch frames (n = 20) and corresponding thermoformed PET-G aligners with bonded attachments comprising two composite materials (universal-C and flowable-F) were fabricated. The morphological features (stereomicroscopy), roughness (optical profilometry), and surface composition (ATR-FTIR) of the attachments were examined before and after immersion in water. To simulate intraoral use, the aligners were removed and re-seated to the frames four times per day for a 7-day immersion period. After testing, the eluents were analyzed by LC-MS/MS targeting the compounds Bis-GMA, UDMA, 2-HEMA, TEGDMA and BPA and by LC-HRMS for suspect screening of the leached dental material compounds and their degradation products. RESULTS: After testing, abrasion-induced defects were found on attachment surfaces such as scratches, marginal cracks, loss of surface texturing, and fractures. The morphological changes and debonding rate were greater in F. Comparisons (before-after testing) revealed a significantly lower Sc roughness parameter in F. The surface composition of the aligners after testing showed minor changes from the control, with insignificant differences in the degree of C = C conversion, except for few cases with strong evidence of hydrolytic degradation. Targeted analysis results revealed a significant difference in the compounds released between Days 1 and 7 in both materials. Insignificant differences were found when C was compared with F in both timeframes. Several degradation products were detected on Day 7, with a strong reduction in the concentration of the targeted compounds. CONCLUSIONS: The use of aligners affects the surface characteristics and degradation rate of composite attachments in an aqueous environment, releasing monomers, and monomer hydrolysates within 1-week simulated use.

Synthesis of polymerizable betulin maleic diester derivative for dental restorative resins with antibacterial activity.

OBJECTIVE: Bisphenol A glycidyl methacrylate (Bis-GMA) is of great importance for dental materials as the preferred monomer. However, the presence of bisphenol-A (BPA) core in Bis-GMA structure causes potential concerns since it is associated with endocrine diseases, developmental abnormalities, and cancer lesions. Therefore, it is desirable to develop an alternative replacement for Bis-GMA and explore the intrinsic relationship between monomer structure and resin properties. METHODS: Here, the betulin maleic diester derivative (MABet) was synthesized by a facile esterification reaction using plant-derived betulin and maleic anhydride as raw materials. Its chemical structure was confirmed by 1H and 13C NMR spectra, FT-IR spectra, and HR-MS, respectively. The as-synthesized MABet was then used as polymerizable comonomer to partially or completely substitute Bis-GMA in a 50:50 Bis-GMA: TEGDMA resin (5B5T) to formulate dental restorative resins. These were then determined for the viscosity behavior, light transmittance, real-time degree of conversion, residual monomers, mechanical performance, cytotoxicity, and antibacterial activity against Streptococcus mutans (S. mutans) in detail. RESULTS: Among all experimental resins, increasing the MABet concentration to 50 wt% made the resultant 5MABet5T resin have a maximum in viscosity and appear dark yellowish after polymerization. In contrast, the 1MABet4B5T resin with 10 wt% MABet possessed comparable shear viscosity and polymerization conversion (46.6 ± 1.0% in 60 s), higher flexural and compressive strength (89.7 ± 7.8 MPa; 345.5 ± 14.4 MPa) to those of the 5B5T control (48.5 ± 0.6%; 65.7 ± 6.7 MPa; 223.8 ± 57.1 MPa). This optimal resin also had significantly lower S. mutans colony counts (0.35 ×108 CFU/mL) than 5B5T (7.6 ×108 CFU/mL) without affecting cytocompatibility. SIGNIFICANCE: Introducing plant-derived polymerizable MABet monomer into dental restorative resins is an effective strategy for producing antibacterial dental materials with superior physicochemical property.

The chemical and optical stability evaluation of injectable restorative materials under wet challenge.

OBJECTIVES: To investigate and compare the chemical and optical stability of four restorative composite materials: two injectable resins, one flowable resin and one compomer. METHODS: Two injectable nano-filled composite resins: G-aenial Universal (GU) and Beautifil Injectable XSL (BI), a flowable composite resin: Filtek Supreme Flowable (FS) and a compomer: Dyract Flow (DF), in A2 shade were tested and compared. Water sorption and solubility were conducted according to ISO4049:2019 standard; ICP-OES and F-ion selective electrode were used to test the elemental release; Degree of conversion (DC) was obtained by using FTIR; water contact angle was obtained by static sessile drop method, and a spectrophotometer was used for optical properties (ΔE⁎, ΔL⁎ and TP). SPSS 28.0 was used for statistical analysis and the significant level was pre-set as α = 0.05. RESULTS: GU performed the best in water sorption and solubility, FS had the lowest elemental release, the best colour stability, and the highest DCIM and DC24-h. DF, the compomer had the lowest, and GU and BI, the injectable composites had the largest water contact angle, respectively. Correlations were found between water sorption and water solubility. CONCLUSIONS: The four composite restorative materials showed different chemical and optical behaviours. Overall, composite resins performed better than compomer, while additional laboratory and in vivo tests are necessary to obtain a more comprehensive comparison between injectable and flowable composite resins. Wsp and Wsl are influenced by many common factors, and the values are highly positively related. CLINICAL SIGNIFICANCE: A comprehensive understanding of materials is crucial before selecting materials for clinical practice. Composite resins rather than compomers are recommended because of their exceptional properties, which make them eligible for a wide range of clinical applications and an elongated lifespan.

Clinical performance of posterior restorations using a universal adhesive over moist and dry dentin: A 36-month double-blind split-mouth randomized clinical trial.

OBJECTIVES: To evaluate the influence of dentin moisture on the clinical behavior of a universal adhesive on posterior teeth after 36 months of follow-up. METHODS: Forty-five patients participated in this study. Following a split-mouth design, three operators placed 90 Class I/Class II restorations over moist dentin (MD) or dry (DD) (n = 45) with resin composite (Filtek Bulk Fill) and a universal adhesive used in the etch-and-rinse mode (Single Bond Universal). Each restoration was evaluated according to the FDI and USPHS criteria (postoperative sensitivity, fracture and retention, marginal staining, marginal adaptation, and recurrence of caries) at baseline and after 6-, 12-, and 36 months. For statistical analysis, Kruskal Wallis analysis of variance rank (α = 0.05) and Kaplan-Meier survival analysis were used. RESULTS: No significant difference between groups was observed in each FDI criterion after 36 months of clinical evaluation (p > 0.05). The retention rates (confidence interval 95 %) were 97.37 % (86.5 - 99.5) for both MD and DD without significant difference between them (p > 0.05). Eight restorations (MD = 4; DD = 4) showed minimal marginal staining defects (p > 0.05). Two restorations were lost (MD = 1; DD = 1). Fifteen restorations (MD = 8; DD = 7) presented minor marginal discrepancies according to the FDI criteria (p > 0.05). CONCLUSION: The clinical performance of the universal adhesive when applied in etch-and-rinse mode was not influenced by dentin moisture in posterior bulk-fill composite restorations. CLINICAL SIGNIFICANCE: The level of dentin moisture appears not to influence the clinical efficacy of a universal adhesive when applied using the etch-and-rinse technique in posterior composite resin restorations.

The influence of filler load in 3D printing resin-based composites.

OBJECTIVE: To evaluate the influence of the barium glass (BG) filler in 3D printing resin-based composites for restorative structures. METHODS: Experimental 3D printing resin-based composites were formulated with UDMA 70%wt, Bis-EMA 20%wt, and TEGDMA 10%wt. Photoinitiators TPO and DFI (2%wt) were used. BG was incorporated at 40%wt and 50%wt. 0%wt BG was used as negative control and the VarseoSmile Crownplus (Bego) was used as a commercial control. Specimens were printed using a 3D printer. Subsequently, specimens were washed and submitted to post-curing with 405 nm at 60ºC for 2 × 20 min at FormCure (FormLabs). 3D printing resin-based composites were evaluated by flexural strength, degree of conversion, softening in solvent, radiopacity, and cytotoxicity against gingival fibroblasts. Data were statistically analyzed using one-way ANOVA (α = 0.05). RESULTS: No significant differences in flexural strength were showed between BG40% (90.5 ± 5,4 MPa), BG50% (102.0 ± 11.7 MPa) and VA (105.2 ± 11.7 MPa). Addition of 40% and 50% of BG showed no influence in the degree of conversion compared to VA (p > 0.05). All groups showed softening in solvent after immersion in ethanol (p < 0.05). All groups showed more than 1mmAl of radiopacity. BG50% showed significantly higher radiopacity (2.8 ± 0.3 mmAl) than other groups (p < 0,05). Cytotoxicity evaluation showed gingival cell viability higher than 80% for all groups. SIGNIFICANCE: Addition of up to 50%wt of barium glass in experimental 3D printing resin-based composites showed promising results for long-term restorative structures.

Ion release mechanisms in composites containing CaP particles and hydrophilic monomers.

OBJECTIVE: To investigate the effect of hydrophilic/permeable polymer matrices on water sorption/solubility (WS/SL), Ca2+ release, mechanical properties and hydrolytic degradation of composites containing dicalcium phosphate dihydrate (DCPD) particles. METHODS: Six composites were tested, all with 10 vol% of glass particles and either 30 vol% or 40 vol% DCPD. Composites containing 1BisGMA:1TEGDMA in mols (at both inorganic levels) were considered controls. Four materials were formulated where 0.25 or 0.5 of the BisGMA/TEGDMA was replaced by pyromellitic dianhydride glycerol dimethacrylate (PMGDM)/ polyethylene glycol dimethacrylate (PEGDMA). Composites were tested for degree of conversion (FTIR spectroscopy), WS/SL (ISO 4049) and Ca2+ release (inductively coupled plasma optical emission spectroscopy). Fracture toughness (FT) and biaxial flexural strength/modulus (BFS/FM) were determined after 24 h and 60 days in water. The contributions of diffusional and relaxational mechanisms to Ca2+ release kinetics were analyzed using the semi-empirical Salim-Peppas model. Data were analysed by ANOVA/Tukey test (alpha: 0.05). RESULTS: WS/SL was higher for composites containing PMGDM/PEGDMA compared to the controls (p < 0.001). Only at 40% DCPD the 0.5 PMGDM/PEGDMA composite showed statistically higher Ca2+ release than the control. Relaxation diffusion was the main release mechanism. Initial FT was not negatively affected by matrix composition. BFS (both DCPD fractions) and FM (30% DCPD) were lower for composites with hydrophilic/permeable networks (p < 0.01). After 60 days in water, composites with PMGDM/PEGDMA presented significant reductions in FT, while all composites had reductions in BFS/FM. SIGNIFICANCE: Increasing matrix hydrophilicity/permeability significantly increased Ca2+ release only at a high DCPD fraction.

Clinical evaluation of Giomer and self-etch adhesive compared with nanofilled resin composite and etch-and-rinse adhesive - Results at 8 years.

OBJECTIVE: This study aimed to evaluate the long-term clinical performance of Giomer and a self-etch adhesive system compared with a nanofilled resin composite and etch-and-rinse adhesive system in Class I and Class II restorations. METHOD: The study was designed to be double-blinded with intra-individual control. 48 patients with 54 pairs of cavities (class I or class II) were recruited. Each pair of restorations was placed with either BEAUTIFIL II (BF) and FL-BOND II (FL) or Filtek Z350 (Z350) and Scotchbond Multi-Purpose (SMP). Clinical evaluation was performed at baseline, 6-month, 18-month, 4-year and 8-year after placement according to modified USPHS criteria. Kaplan-Meier survival analysis and log rank tests were performed (SPSS 20.0, IBM Corporation, US) to compare the survival probability of different restorations.A generalized linear mixed model (GLMM) was adopted to assess the performance of the materials. The McNemar test was used to show significant changes for all the evaluation criteria and difference between them. RESULTS: At the eight-year recall, 32 patients with 67 restorations were present. There were twelve restorations in total recorded as failure due to loss of retention, restoration fracture, secondary caries, tooth fracture or endodontic treatment due to pulp necrosis. The survival probabilities and calculated annual failure rate(AFR) of BF and Z350 restorations at 8-year were 87.2 % vs 87.8 % and 1.6 % vs 1.5 % respectively with no significant difference (p > 0.05)between the two materials. Over the recall time range of eight years, decreased possibility of alpha rating was observed for retention, marginal adaptation, marginal staining and surface roughness for both materials (p < 0.05). Decreased possibility of alpha rating was observed for surface staining and secondary caries for Z350 (p < 0.05) and restoration fracture for BF (p < 0.05), respectively. Comparing the two restorative systems over eight years, no significant difference was seen for linear decline of the possibility of alpha rating for any of the criteria evaluated (p > 0.05). CONCLUSION: Giomer material and the self-etch adhesive system had comparable clinical performance with nanofilled resin composite and etch-and-rinse adhesive system over the observation period of eight years.

Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

Evaluating flexure properties, hardness, roughness and microleakage of high-strength injectable dental composite: an in vitro study.

BACKGROUND: Recently, a new generation of high-strength flowable dental composites has been introduced by manufacturers. The manufacturers claim that these materials have enhanced mechanical and physical properties and are suitable for use in a wide range of direct anterior and posterior restorations, even in high-stress bearing areas. AIM: The objective of this study was to assess certain physical and mechanical properties of these recently introduced high-strength flowable composites in comparison to conventional multipurpose dental composites. METHODS: Four types of high-strength flowable composites (Genial Universal FLO, Gaenial Universal Injectable, Beautifil Injectable, and Beautifil Flow Plus) were tested in experimental groups, while a nanohybrid conventional composite (Filtek Z350 XT) was used as the control. For flexure properties, ten rectangular samples (2 × 2 × 25 mm) were prepared from each composite material and subjected to 5000 cycles of thermocycling. Samples were then subjected to flexural strength testing using the universal testing machine. Another twenty disc-shaped specimens of dimensions (5 mm diameter × 2 mm thickness) were fabricated from each composite material for surface roughness (Ra) (n = 10) and hardness (VHN) test (n = 10). All samples underwent 5000 cycles of thermocycling before testing. Additionally, microleakage testing was conducted on 60 standardized class V cavities prepared on molar teeth and divided randomly into five groups (n = 12). Cavities were then filled with composite according to the manufacturer's instructions and subjected to thermocycling for 1000 cycles before testing using methylene blue solution and a stereomicroscope. RESULTS: All tested materials were comparable to the control group in terms of flexural strength and surface roughness (p > 0.05), with Gaenial Universal FLO exhibiting significantly higher flexural strength compared to the other flowable composite materials tested. However, all tested materials demonstrated significantly lower elastic modulus and surface hardness than the control group (p < 0.05). The control group exhibited higher microleakage scores, while the lowest scores were observed in the Gaenial Universal FLO material (p < 0.05) CONCLUSION: The physical and mechanical behaviors of the different high-strength flowable composites investigated in this study varied. Some of these materials may serve as suitable alternatives to conventional composites in specific applications, emphasizing the importance of dentists being familiar with material properties before making material selections.

A new method of adhesive system application improves the bond strength between fiber post and root dentin.

This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

Effect of dentin surface conditions and curing mode of resin cement on the dentin bond strength.

This study investigates the effects of dentin's drying time, roughness, and curing modes of resin cement on bond strength. Forty human teeth were divided into eight groups based on three experimental factors: dentin's roughness by 240-or 600-grit SiC paper (coarse or fine), dentin wetness with air-drying time (5-s or 10-s), and Single Bond Universal adhesive's curing mode by co-curing with RelyX Ultimate cement or light-curing separately (co-curing or light-curing). The micro-tensile bond strength of fifteen resin-dentin stikcs per groups was measured. Failure mode and adhesive layers were observed using stereoscopic and confocal laser scanning microscopy, respectively. The curing mode of the adhesive layer affected the bond strength of the dentin-resin cement (p<0.05). In particular, the light-curing mode exhibited a significantly higher bond strength than the co-curing one (p<0.05). The bond strength between the resin cement and dentin was improved in the 5-s drying groups than in the 10-s drying groups.

Efficacy of seventh generation bonding agents as desensitizers in patients with dentin hypersensitivity: a randomized clinical trial.

BACKGROUND: Dentin hypersensitivity (DH) is one of the most challenging and persistent dental complaints characterized by transient, intense pain triggered by various stimuli. It affects a significant portion of the global population, predominantly those aged 20-40. This study aims to evaluate the desensitizing efficacy of seventh-generation dentin bonding agents (Single Bond Universal by 3 M ESPE and Xeno-V + by Dentsply) against a control group using Bifluorid 12 by Voco in mitigating DH within a month of the follow-up period. METHODS: This was a single-center, parallel-group, double-blind, controlled randomized clinical trial conducted at Dow University of Health Sciences, Karachi, Pakistan. A total of 105 patients with DH were allocated into three groups for this study. The patients were divided into three groups (Single Bond Universal by 3 M ESPE and Xeno-V + by Dentsply) and the control group containing fluoride varnish (Bifluorid 12 by Voco). Discomfort Interval Scale scores and Schiff Cold Air Sensitivity Scale scores were recorded at baseline, immediately after the intervention, after 01 weeks, and after 01 month. RESULTS: All the materials demonstrated a statistically significant reduction in discomfort and sensitivity (DIS scores p-value 0.01) immediately after 01 week and over a period of 01 month after treatment compared with the baseline scores before application, with no single material proving superior over the one-month observation period. The study also provided insights into dental hygiene practices, with a significant majority using a toothbrush and sensitivity patterns, with cold stimuli being the most common cause of sensitivity. CONCLUSION: The study demonstrates that Single Bond Universal, Xeno V+, and Bifluorid 12 are equally effective in reducing dentin hypersensitivity, with no distinct superiority observed over a one-month period. The findings highlight the potential of fluoride varnishes as a less technique-sensitive and cost-effective option for treating DH, offering valuable insights for future research and clinical practice. TRIAL REGISTRATION: NCT04225247 ( https://clinicaltrials.gov/study/NCT04225247 ), Date of Registration: 13/01/2020. (Retrospectively registered).

Toxicity and cytokine release from human dental pulp stem cells after exposure to universal dental adhesives cured by single peak and polywave LEDs.

OBJECTIVES: to assess the impact of universal adhesives, cured with single-peak and polywave LEDs, on the metabolic activity and cytokine release of human dental pulp stem cells (hDPSCs). In addition, analyze the degree of conversion (DC) of the adhesives cured with the different LEDs. METHODS: Discs (5 mm diameter, 1 mm thick) were prepared using three universal adhesives: Single Bond Universal (SBU, 3 M ESPE), Optibond Universal (OBU, Kerr), and Zipbond Universal (ZBU, SDI). These discs were cured for 40 s using a single-peak (DeepCure, 3 M ESPE) or a polywave light-emmiting diode (LED) curing unit (Valo Grand, Ultradent). After 24 h, the specimens were placed in 24-well culture plates, each containing 1 mL of culture medium for 24 h. hDPSCs (1.8 ×104) were seeded in 96-well plates and allowed to grow for 24 h. Subsequently, the cells were exposed to the extracts (culture medium containing eluates from the adhesive discs) for an additional 24 h. Cells not exposed to the extracts were used as a control group. The mitochondrial metabolism was assessed using the MTT assay and the cytokine release evaluated through MAGPIX. The degree of conversion of the adhesives was analyzed using FTIR (n = 5). The results were analyzed by ANOVA two-way and Tukey's test. RESULTS: OBU and ZBU eluates caused a statistically significant reduction in mitochondrial metabolism, regardless of the LED used, indicating their cytotoxicity. In contrast, SBU did not significantly affect the MTT results, resembling the control group. A higher release of cytokines IL-1, IL-6, IL-10, and TNF-α were found in association to ZBU. SBU, on the other hand, increased the release of IL-8. OBU did not influenced the cytokine release. SBU presented the higher DC, while OBU and ZBU had similar DC, lower than SBU. SIGNIFICANCE: In conclusion, universal adhesives exhibit toxicity towards hDPSCs, but the extent of toxicity varies depending on the adhesive material. ZBU was associated with increased cytokine release, particularly pro-inflammatory mediators, from hDPSCs. The different LEDs did not influenced the cytotoxicity of the evaluated adhesives.

Effects of different primers and colouring solutions on orthodontic bonding: shear bond strength and colour change.

OBJECTIVES: This in vitro study evaluated the effect of different colouring solutions and primer systems used in the bonding of brackets on enamel colour change and bond strength. MATERIALS AND METHODS: 120 premolar teeth were divided into four main groups; brackets were bonded with 37% orthophosphoric acid + Transbond XT Primer in Group 1, 3 M Single Bond Universal in Group 2, Transbond Plus SEP in Group 3, and G-Premio Bond in Group 4. Each group was divided into three subgroups, and the teeth were placed in a cup containing coffee and tea mixture, in a cup containing cola and in distilled water. A bond strength test was applied to all teeth. Colour measurements of all teeth were performed at 2 different times: before bonding and after the bond strength test. RESULTS: The average bond strength of the 37% orthophosphoric acid group was higher than that of the other groups. The effect of primer and solution groups on colour change was statistically significant (p = 0.001 and p = 0.023, respectively). CONCLUSIONS: In this study, the bond strength was clinically sufficient in all primer groups. The highest colour change was observed when the tea-coffee solution and Transbond Plus SEP primer were used. CLINICAL RELEVANCE: This study has identified enamel discoloration and bond strength from different colouring solutions and primer systems used for bonding braces, which can be used to inform clinicians and patients to achieve better treatment results.

Determination of fatty acid uptake and desaturase activity in mammalian cells by NMR-based stable isotope tracing.

BACKGROUND: Mammalian cells both import exogenous fatty acids and synthesize them de novo. Palmitate, the end product of fatty acid synthase (FASN) is a substrate for stearoyl-CoA desaturases (Δ-9 desaturases) that introduce a single double bond into fatty acyl-CoA substrates such as palmitoyl-CoA and stearoyl-CoA. This process is particularly upregulated in lipogenic tissues and cancer cells. Tracer methodology is needed to determine uptake versus de novo synthesis of lipids and subsequent chain elongation and desaturation. Here we describe an NMR method to determine the uptake of 13C-palmitate from the medium into HCT116 human colorectal cancer cells, and the subsequent desaturation and incorporation into complex lipids. RESULTS: Exogenous 13C16-palmitate was absorbed from the medium by HCT116 cells and incorporated primarily into complex glycerol lipids. Desaturase activity was determined from the quantification of double bonds in acyl chains, which was greatly reduced by ablation of the major desaturase SCD1. SIGNIFICANCE: The NMR approach requires minimal sample preparation, is non-destructive, and provides direct information about the level of saturation and incorporation of fatty acids into complex lipids.