[Spectral characteristics of Ce3+ in alkali-alkaline earth borate system].
Guang Pu Xue Yu Guang Pu Fen Xi
; 30(3): 735-7, 2010 Mar.
Article
en Zh
| MEDLINE
| ID: mdl-20496698
ABSTRACT
Alkali-alkaline earth borate LiCaBO3 Ce3+, LiSrBO3 Ce3+ and LiBaBO3 Ce3+ were investigated by solid-state method. CaCO3 (99.9%), SrCO3 (99.9%), BaCO3 (99.9%), Li2 CO3 (99.9%), Na2 CO3 (99.9%), K2 CO3 (99.9%), H3BO3 (99.9%) and CeO2 (99.9%) were used as starting materials, After these individual materials were blended and ground thoroughly in an agate mortar, the homogeneous mixture was heated at 700 degrees C for 2 h in a reduced atmosphere (5 95 (H2/N2)), and these three phosphors were obtained. The excitation and emission spectra of these phosphors were measured by a SHIMADZU RF-540 fluorescence spectrophotometer. The spectral characteristics of Ce3+ in alkali-alkaline earth borate LiCaBO3, LiSrBO3 and LiBaBO3 were investigated. The emission spectra of Ce3+ in these three phosphors all exhibited a dissymmetrical band, and the emission peaks were located at 428, 436 and 440 nm, respectively. The excitation spectra for 428, 436 and 440 nm emission of these three phosphors showed a dissymmetrical band at 364, 369 and 370 nm, respectively. The effects of Li+, Na+ and K+ on the emission intensities of these three phosphors were studied. The results show that the emission intensities of these phosphors were enhanced, and the maximal emission intensity of doping Li+ is higher than that of Na+ and K+.
Buscar en Google
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
Zh
Revista:
Guang Pu Xue Yu Guang Pu Fen Xi
Año:
2010
Tipo del documento:
Article
País de afiliación:
China