Effect of Al2O3/Ga2O3 ratio on the structure and luminescence properties of Sm3+ doped SrO-Nb2O5-Al2O3-Ga2O3-SiO2 glasses.

ABSTRACT

The Sm3+ doped SrO-Nb2O5-Al2O3-Ga2O3-SiO2 glasses in this work were prepared using the conventional melt quenching method. The effects of Al2O3/Ga2O3 ratio on the structure and orange light emission properties were studied by XRD, Raman spectroscopy, spectrophotometer and J-O theory, respectively. With the increase of Al2O3 content, the absorption coefficient of the glass sample gradually increases, which might be attributed to an increase in non-bridged oxygen bonds caused by a change in the glass network structure. Under 403 nm excitation, the emission spectra show clear peaks at 602 nm and 649 nm, representing the 4G5/2 â†’ 6H7/2, and 4G5/2 â†’ 6H9/2 transitions, respectively. When the Al2O3/Ga2O3 ratio is 0.25, the sample luminescence intensity is the highest, and the emission cross section of A2 glass sample is 4.34 × 10-22 cm2. The CIE color coordinates, color purity, and color temperature values of all samples were determined, and they were all located in the orange-red light region. The experiments results reveal that the prepared silica-aluminum-gallium glasses has a potential application prospect in orange-red LEDs, solid state lasers and other fields.