The longevity evaluation of multi-metal stabilization by MgO in Pb/Zn smelter-contaminated soils.
Environ Sci Pollut Res Int
; 31(19): 28153-28165, 2024 Apr.
Article
em En
| MEDLINE
| ID: mdl-38528219
ABSTRACT
The re-mobilization risks of potentially toxic elements (PTEs) during stabilization deserve to be considered. In this study, artificial simulation evaluation methods based on the environmental stress of freeze-thaw (F-T), acidification and variable pH were conducted to assess the long-term effectiveness of PTEs stabilized by MgO in Pb/Zn smelter contaminated soils. Among common stabilizing materials, MgO was considered as the best remediation material, since PTEs bioavailability reduced by 55.48% for As, 19.58% for Cd, 10.57% for Cu, and 26.33% for Mn, respectively. The stabilization effects of PTEs by MgO were best at the dosage of 5 wt%, but these studied PTEs would re-mobilize after 30 times F-T cycles. Acid and base buffering capacity results indicated that the basicity of contaminated soils with MgO treatment reduced under F-T action, and the leached PTEs concentrations would exceed the safety limits of surface water quality standard in China (GB3838-2002) after acidification of 2325 years. No significant changes were found in the pH-dependent patterns of PTEs before and after F-T cycles. However, after F-T cycles, the leaching concentrations of PTEs increased due to the destruction of soil microstructure and the functionality of hydration products formed by MgO, as indicated by scanning electron microscopy (SEM) coupled with energydispersive Xray spectroscopy (EDS) results. Hence, these findings would provide beneficial references for soil remediation assessments of contaminated soils under multi-environmental stress.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Solo
/
Poluentes do Solo
/
Zinco
/
Chumbo
/
Óxido de Magnésio
País/Região como assunto:
Asia
Idioma:
En
Revista:
Environ Sci Pollut Res Int
Assunto da revista:
SAUDE AMBIENTAL
/
TOXICOLOGIA
Ano de publicação:
2024
Tipo de documento:
Article