Fabrication of N and S co-doped lignin-based porous carbon aerogels loaded with FeCo alloys and their application to oxygen evolution and reduction reactions in Zn-air batteries.

ABSTRACT

Zn-air batteries are a highly promising clean energy sustainable conversion technology, and the design of dual-function electrocatalysts with excellent activity and stability is crucial for their development. In this work, FeCo alloy loaded biomass-based N and S co-doped carbon aerogels (FeCo@NS-LCA) were fabricated from chitosan and lignosulfonate-metal chelates via liquid nitrogen pre-frozen synergistic high-temperature carbonization with application in electrocatalytic reactions. The abundant oxygen-containing functional groups on lignosulfonates have a chelating effect on metal ions, which can avoid the aggregation of metal nanoparticles during carbonation and catalysis, facilitating the construction of a nanoconfinement catalytic system with biomass carbon as the domain-limiting body and FeCo nanoparticles as the active sites. FeCo@NS-LCA exhibited catalytic activity (E1/2 = 0.87 V, JL = 5.7 mA cm-2) comparable to the commercial Pt/C in the oxygen reduction reaction (ORR), excellent resistance to methanol toxicity and stability. Meanwhile, the overpotential of oxygen evolution reaction (OER) was 324 mV, close to that of commercial RuO2 catalysts (351 mV). This study utilizes the coordination action of lignosulfonate to provide a novel and environmentally friendly method for the preparation of confined nano-catalysts and provides a new perspective for the high-value utilization of biomass resources.