ABSTRACT
Iron nitride (Fe3N) and iron carbide (Fe3C) nanoparticles can be prepared via sol-gel synthesis. While sol-gel methods are simple, it can be difficult to control the crystalline composition, i.e., to achieve a Rietveld-pure product. In a previous in situ synchrotron study of the sol-gel synthesis of Fe3N/Fe3C, we showed that the reaction proceeds as follows: Fe3O4 â FeOx â Fe3N â Fe3C. There was considerable overlap between the different phases, but we were unable to ascertain whether this was due to the experimental setup (side-on heating of a quartz capillary which could lead to thermal gradients) or whether individual particle reactions proceed at different rates. In this paper, we use in situ wide- and small-angle X-ray scattering (wide-angle X-ray scattering (WAXS) and small-angle X-ray scattering (SAXS)) to demonstrate that the overlapping phases are indeed due to variable reaction rates. While the initial oxide nanoparticles have a small range of diameters, the size range expands considerably and very rapidly during the oxide-nitride transition. This has implications for the isolation of Rietveld-pure Fe3N, and in an extensive laboratory study, we were indeed unable to isolate phase-pure Fe3N. However, we made the surprising discovery that Rietveld-pure Fe3C nanoparticles can be produced at 500 °C with a sufficient furnace dwell time. This is considerably lower than the previous reports of the sol-gel synthesis of Fe3C nanoparticles.
ABSTRACT
The sol-gel synthesis of iron carbide (Fe3C) nanoparticles proceeds through multiple intermediate crystalline phases, including iron oxide (FeOx) and iron nitride (Fe3N). The control of particle size is challenging, and most methods produce polydisperse Fe3C nanoparticles of 20-100 nm in diameter. Given the wide range of applications of Fe3C nanoparticles, it is essential that we understand the evolution of the system during the synthesis. Here, we report an in situ synchrotron total scattering study of the formation of Fe3C from gelatin and iron nitrate sol-gel precursors. A pair distribution function analysis reveals a dramatic increase in local ordering between 300 and 350 °C, indicating rapid nucleation and growth of iron oxide nanoparticles. The oxide intermediate remains stable until the emergence of Fe3N at 600 °C. Structural refinement of the high-temperature data revealed local distortion of the NFe6 octahedra, resulting in a change in the twist angle suggestive of a carbonitride intermediate. This work demonstrates the importance of intermediate phases in controlling the particle size of a sol-gel product. It is also, to the best of our knowledge, the first example of in situ total scattering analysis of a sol-gel system.
ABSTRACT
Materials with the apatite structure have a range of important applications in which their function is influenced by details of their local structure. Here, we describe an average and local structural study to probe the origins of high-temperature oxide ion mobility in La10(GeO4)6O3 and La8Bi2(GeO4)6O3 oxygen-excess materials, using the low-conductivity interstitial oxide-free La8Sr2(GeO4)6O2 as a benchmark. For La10 and La8Bi2, we locate the interstitial oxygen, Oint, responsible for conductivity by Rietveld refinement and relate the P63/m to P1Ì phase transitions on cooling to oxygen ordering. Local structural studies using neutron total scattering reveal that well-ordered GeO5 square pyramidal groups form in the structure at low temperature, but that Oint becomes significantly more disordered in the high-conductivity, high-temperature structures, with a transition to more trigonal-bipyramid-like average geometry. We relate the higher conductivity of Bi materials to the presence of several Oint sites of similar energy in the structure, which correlates with its less-distorted low-temperature average structure.