ABSTRACT
Nitrogen (15N) and carbon (12C) ion implantations with implant energy of 100 keV for different doses were performed on nanosized diamond (ND) particles. Magnetic measurements on the doped ND show ferromagnetic hysteresis behavior at room temperature. The saturation magnetization (M(s)) in the case of 15N implanted samples was found to be higher compared to the 12C implanted samples for dose sizes greater than 10(14) cm(-2). The role of structural modification or defects along with the carbon-nitrogen (C-N) bonding states for the observed enhanced ferromagnetic ordering in 15N doped samples is explained on the basis of x-ray photoelectron spectroscopy measurements.
ABSTRACT
Neutron diffraction in Fe(Al) reveals incommensurate spin density waves (SDWs) in alloys known to be spin glasses. The wave vectors for crystals of Fe(34Al), Fe(40Al), and Fe(43Al) show n varying from 11 to 6 for q-->=2pi(h+/-1/n,k+/-1/n,l+/-1/n)/a(0), where (h,k,l) and a(0) characterize the parent bcc lattice of the CsCl structure. The magnetic reflections are present far above the spin-glass freezing temperatures. These SDWs keep the spins on nearest-neighbor Fe atoms close to parallel, in contrast with SDWs in Cr, which keep nearest-neighbor spins close to antiparallel.