ABSTRACT
Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) remains the most investigated conjugated polymer in bioelectronics, due to its biocompatibility, high conductivity, and commercial availability. Despite these advantages, it suffers from structural and electronic instability, associated with the PSS component. Here, a graft copolymer based on ionised sulfonic modified PEDOT, poly(EDOTS-g-EDOT), was electrochemically synthesised with demonstrated structural and electronic stability and enhanced electrochemical performance. The graft copolymer was insoluble in water without crosslinking, and exhibited enhanced ion diffusion upon electrochemical switching, as revealed by its volumetric capacitance (159 ± 8 F cm-3), which was significantly higher than that of spin-coated PEDOT:PSS films (41 ± 5 F cm-3). Similarly, its performance as an active channel material in organic electrochemical transistors (OECTs) was superior to the spin-coated PEDOT:PSS, as shown for instance by its high normalised transconductance (273 ± 79 S cm-1) and a significantly high ION/IOFF ratio (19 345 ± 1205). Its short- and long-term electronic stability were also confirmed with no drop in its output drain current, despite its high swelling degree. In contrast, the spin-coated PEDOT:PSS experienced a significant deterioration in its performance over the same operational time. The facile synthesis and improved performance of poly(EDOTS-g-EDOT) highlight the importance of innovative material design in overcoming existing operational shortcomings in electronic devices.
ABSTRACT
Organic mixed ionic-electronic conductors (OMIECs) are being explored in applications such as bioelectronics, biosensors, energy conversion and storage, and optoelectronics. OMIECs are largely composed of conjugated polymers that couple ionic and electronic transport in their structure as well as synthetic flexibility. Despite extensive research, previous studies have mainly focused on either enhancing ion conduction or enabling synthetic modification. This limited the number of OMIECs that excel in both domains. Here, a series of OMIECs based on functionalized poly(3,4-ethylenedioxythiophene) (PEDOT) copolymers that combine efficient ion/electron transport with the versatility of post-functionalization were developed. EDOT monomers bearing sulfonic (EDOTS) and carboxylic acid (EDOTCOOH) groups were electrochemically copolymerized in different ratios on oxygen plasma-treated conductive substrates. The plasma treatment enabled the synthesis of copolymers containing high ratios of EDOTS (up to 68%), otherwise not possible with untreated substrates. This flexibility in synthesis resulted in the fabrication of copolymers with tunable properties in terms of conductivity (2-0.0019 S/cm) and ion/electron transport, for example, as revealed by their volumetric capacitances (122-11 F/cm3). The importance of the organic nature of the OMIECs that are amenable to synthetic modification was also demonstrated. EDOTCOOH was successfully post-functionalized without influencing the ionic and electronic transport of the copolymers. This opens a new way to tailor the properties of the OMIECs to specific applications, especially in the field of bioelectronics.
ABSTRACT
Conjugated polymers are enabling the development of flexible bioelectronics, largely driven by their organic nature which facilitates modification and tuning to suit a variety of applications. As organic semiconductors, conjugated polymers require a dopant to exhibit electrical conductivity, which in physiological conditions can result in dopant loss and thereby deterioration in electronic properties. To overcome this challenge, "self-doped" and self-acid-doped conjugated polymers having ionized pendant groups covalently bound to their backbone are being developed. The ionized group in a "self-doped" polymer behaves as the counterion that maintains electroneutrality, while an external dopant is required to induce charge transfer. The ionized group in a self-acid-doped polymer induces charge transfer and behaves as the counterion balancing the charges. Despite their doping processes being different, the two terms, self-doped and self-acid-doped, are often used interchangeably in the literature. Here, the differences are highlighted in the doping mechanisms of self-doped and self-acid-doped polymers, and it is proposed that the term "self-doped" should be replaced by "self-compensated," while reserving the term self-acid-doped for polymers that are intrinsically doped without the need of an external dopant. This is followed by a summary of examples of self-acid-doping in bioelectronics, highlighting their stability in the conductive state under physiological conditions.