Dataset of PY53 Nickel-Titanate yellow pigments for plastic, enamel and ceramic glaze applications.

This dataset shows the change in color tone in plastic (masterbatch), enamel, and ceramic (glaze) colored with PY53 Nickel-Titanate-Pigment calcined with different NiO ratios by solid-state reaction. The pigments were mixed with milled frits and applied to the metal and ceramic substance for enamel and ceramic glaze applications, respectively. For the plastic application, the pigments were mixed with melted polypropylene (PP) and formed into plastic plates. The CIELAB color space approach was used to assess L*, a*, b* values over applications created for plastic, ceramic, and enamel trials. These data can be used to evaluate the color of PY53 Nickel-Titanate pigments with different NiO ratios in the applications.

Effect of Al2O3 and ZrO2 Filler Material on the Microstructural, Thermal and Dielectric Properties of Borosilicate Glass-Ceramics.

Various glass-ceramics are widely used or considered for use as components of microelectronic materials due to their promising properties. In this study, borosilicate glass was prepared using the powder metallurgical route and then mixed with different amounts of Al2O3 and ZrO2 filler materials. Glass-ceramics are produced by high-energy ball milling and conventional sintering process under Ar or air. In this study, the effects of different filler materials and different atmospheres on the microstructural, thermal and dielectric properties were investigated. The data showed that ZrO2 filler material led to better results than Al2O3 under identical working conditions and similar composite structures. ZrO2 filler material significantly enhanced the densification process of glass-ceramics (100% relative density) and led to a thermal conductivity of 2.904 W/K.m, a dielectric constant of 3.97 (at 5 MHz) and a dielectric loss of 0.0340 (at 5 MHz) for the glass with 30 wt.% ZrO2 sample. This paper suggests that prepared borosilicate glass-ceramics have strong sinterability, high thermal conductivity, and low dielectric constants, making them promising candidates for microelectronic devices.

Enhanced Sinterability, Thermal Conductivity and Dielectric Constant of Glass-Ceramics with PVA and BN Additions.

With the rapid development of the microelectronics industry, many efforts have been made to improve glass-ceramics' sinterability, thermal conductivity, and dielectric properties, which are essential components of electronic materials. In this study, low-alkali borosilicate glass-ceramics with PVA addition and glass-BN composites were prepared and successfully sintered at 770 °C. The phase composition, density, microstructure, thermal conductivity, and dielectric constant were investigated. It was shown that PVA addition contributes to the densification process of glass-ceramics (~88% relative density, with closed/open pores in the microstructure) and improves the thermal conductivity of glass material from 1.489 to 2.453 W/K.m. On the other hand, increasing BN addition improves microstructures by decreasing porosities and thus increasing relative densities. A glass-12 wt. % BN composite sample exhibited almost full densification after sintering and presented apparent and open pores of 2.6 and 0.08%, respectively. A high thermal conductivity value of 3.955 W/K.m and a low dielectric constant of 3.00 (at 5 MHz) were observed in this material. Overall, the resulting glass-ceramic samples showed dielectric constants in the range of 2.40-4.43, providing a potential candidate for various electronic applications.

Waste recycling of cathode ray tube glass through industrial production of transparent ceramic frits.

Cathode ray tube (CRT) glass contains significant amounts of alkali and alkaline earth oxides, making it a useful by-product for use in the ceramics industry. Among the various alkali oxides present, those of strontium (SrO), calcium (CaO), and magnesium (MgO) are well known flux materials used widely in the ceramics industry. The most effective flux, SrO, is also a limited resource. In this study, we aimed to develop an environmentally friendly, low-cost method for recycling CRT waste by using it to produce transparent ceramic frits on an industrial scale. Four different samples were fabricated containing between 13 and 25 wt.% CRT panel glass. The color values, sintering behaviors, phases, and microstructural properties of the corresponding samples were analyzed and compared. The results indicate that a composition containing 25 wt.% CRT panel glass could pass the ISO 10545 test. Thus, the results confirm that CRT glass can be used to inexpensively produce transparent ceramic frits at an industrial scale. Implications: The recycling of electronic waste (e-waste), including CRT waste, has increased by high rates of computer and TV consumption. This increase in consumption is likely to increase the rate at which CRTs are discarded. However, CRTs cannot be recycled in the desired amount. Owing to the high silicate, barium and strontium content of CRTs, it has great potential for glass ceramics such as frits. CRT panel glass to produce commercial transparent frit at low cost through an industrial production route for use in single-fire sintered products. Thus, CRT wastes can be recycled cost-effective, sustainable and environmentally friendly.