Effects of Partial-Contact Tool Tilt Angle on Friction Stir Welded AA1050 Aluminum Joint Properties.

This study aims to investigate the impact of partial-contact tool tilt angle (TTA) on the mechanical and microstructure properties of the AA1050 alloy friction stir weld (FSW). Three levels of partial-contact TTA were tested, 0°, 1.5°, and 3°, compared to previous studies on total-contact TTA. The weldments were evaluated using surface roughness, tensile tests, microhardness, microstructure, and fracture analysis. The results show that in partial-contact conditions, increasing TTA decreases the generated heat in the joint line and increases the possibility of FSW tool wear. This trend was the opposite of joints that were friction stir welded via total-contact TTA. The microstructure of the FSW sample was finer at higher partial-contact TTA, while the possibility of defect formation at the root of the stir zone in higher TTA was more than in lower TTA. The robust sample prepared at 0° TTA had 45% of AA1050 alloy strength. The maximum recorded heat in 0° TTA was 336 °C and the ultimate tensile strength of this sample was 33 MPa. The elongation of the 0° TTA welded sample was 75% base metal, and the average hardness of the stir zone was 25 Hv. The fracture surface analysis of the 0° TTA welded sample consisted of a small dimple, indicating the brittle fracture mode.

The Effects of Pin Profile on HDPE Thermomechanical Phenomena during FSW.

Friction stir welding (FSW) of polymeric materials has recently attracted significant attention. Herein, we present the effect of the tool pin profile on the FSW of high-density polyethylene (HDPE) joints through joint experimental analysis and thermomechanical simulations. For analysis of pin profile effects on the thermomechanical properties of HDPE joints, frustum (FPT), cubic (CPT), and triangular (TPT) pin shapes were selected in this study. This research investigated the heat generation of the parts of the different tools as well as heat flux (internal and surface). The results revealed that the heat generation in pins with more edges (cubic (96 °C) and triangular (94 °C)) was greater than in pins with a smooth shape (frustum (91 °C)). The higher heat generation caused the heat flux on the surface of the HDPE from the cubic pin profile to be greater than for other joints. Due to the properties of HDPE, higher heat generation caused higher material velocity in the stirring zone, where the velocity of the materials in TPT, CPT, and FPT pins were 0.41 m/s, 0.42 m/s, and 0.4 m/s, respectively. The simulation results show sharp-edged pins, such as triangular and cubic, lead to over-stirring action and internal voids formed along the joint line. Furthermore, the simulation results indicated that the size of the stirred zones (SZs) of the FPT, TPT, and CPT samples were 17 mm2, 19 mm2, and 21 mm2, respectively, which is around three times the corresponding values in the HAZ.

Effects of Underwater Friction Stir Welding Heat Generation on Residual Stress of AA6068-T6 Aluminum Alloy.

This article aims to study water-cooling effects on residual stress friction stir welding (FSW) of AA6068-T6 aluminum alloy. For this reason, the FSW and submerged FSW processes are simulated by computational fluid dynamic (CFD) method to study heat generation. The increment hole drilling technique was used to measure the residual stress of welded samples. The simulation results show that materials softening during the FSW process are more than submerged. This phenomenon caused the residual stress of the joint line in the submerged case to be lower than in the regular FSW joint. On the other hand, the results revealed that the maximum residual stresses in both cases are below the yielding strength of the AA6068-T6 aluminum alloy. The results indicated that the residual stress along the longitudinal direction of the joint line is much larger than the transverse direction in both samples.

Pin Angle Thermal Effects on Friction Stir Welding of AA5058 Aluminum Alloy: CFD Simulation and Experimental Validation.

The friction stir welding (FSW) of tool pin geometry plays a critical role in the final properties of the produced joint. The tool pin geometry directly affects the generation of heat and the flow of internal materials during the FSW process. The effects of the FSW tool pin angle on heat generation and internal flow have not been quantitatively investigated in detail. In this manuscript, a validated Computational Fluid Dynamic (CFD) model was implemented to analyze the effects of pin angle on the thermo-mechanical action during the FSW process of AA5058 Al-Mg alloy. Experimental test results validate the thermal outcomes of the used model. The obtained results revealed that, when the pin angle is increased, the heat generation decreases while the mechanical action of the tool increases. The internal heat distribution at a higher pin angle is symmetrical. The higher mechanical action of the tool decreases the viscosity of the internal materials and increases stirring action (materials flow) around the pin. Furthermore, plastic flow near the tool increased stirring action and formed a larger stir zone in the joint area.

Effect of Pin Shape on Thermal History of Aluminum-Steel Friction Stir Welded Joint: Computational Fluid Dynamic Modeling and Validation.

This article studied the effects of pin angle on heat generation and temperature distribution during friction stir welding (FSW) of AA1100 aluminum alloy and St-14 low carbon steel. A validated computational fluid dynamics (CFD) model was implemented to simulate the FSW process. Scanning electron microscopy (SEM) was employed in order to investigate internal materials' flow. Simulation results revealed that the mechanical work on the joint line increased with the pin angle and larger stir zone forms. The simulation results show that in the angled pin tool, more than 26% of the total heat is produced by the pin. Meanwhile, in other cases, the total heat produced by the pin was near 15% of the total generated heat. The thermo-mechanical cycle in the steel zone increased, and consequently, mechanical interlock between base metals increased. The simulation output demonstrated that the frictional heat generation with a tool without a pin angle is higher than an angled pin. The calculation result also shows that the maximum heat was generated on the steel side.