Effect of Salvadora persica on resin-dentin bond stability.

BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.

Radiopacity of Resin Cements Using Digital Radiography.

STATEMENT OF PROBLEM: Monitoring performance of glass-ceramic based indirect restorations using radiographic imaging might be difficult due to their low radiopacity. Therefore, materials used for their cementation must possess adequate radiopacity. PURPOSE: This study determined radiopacity of a group of resin-cements used for adhesive-cementation of glass-ceramic-based restorations using digital radiography. METHODS: Two specimens were prepared from a group of resin cements (VariolinkII-opaque, VariolinkII-opaque (base), VariolinkII-Transparent, VariolinkII-Transparent (base), Nexus, RelyX Unicem, RelyX ultimate, Duolink, Monocem and Resinomer) and longitudinal sections of same thickness were obtained from molar and premolar. Specimens were assigned to two groups one had molar section with 10 specimens whereas other had premolar with remaining 10 specimens. Each group was placed on digital radiograph sensor (Schick CDR, size 2) together with aluminum step-wedge. Sensor was exposed to X-ray using standard technique. Two images were obtained for each group. Pixel measurements were made using NIH Image-J software. Mean pixel measurements were converted into aluminum thickness equivalents. Data were statistically-analyzed using one-way ANOVA and Tukey's tests. RESULTS: ANOVA revealed significant difference in mean pixel values among cements (p < 0.001). VariolinkII-opaque showed highest mean aluminum equivalent (4.6 mm Al/1 mm) followed by VariolinkII-opaque-Base (4.5 mm Al/1 mm), VariolinkII-transparent (4.45 mm Al/1 mm), VariolinkII-transparent-Base (4.45 mm Al/1 mm), Nexus (2.95 mm Al/1 mm), Duolink (2.7 mm Al/1 mm), RelyX Unicem (2.2 mm Al/1 mm) and finally RelyX ultimate (2 mm Al/1 mm). All cements had mean radiopacity values higher than that of enamel whereas Monocem (1.25 mm Al/1 mm) and Resinomer (1.2 mm Al/1 mm) had means between those of enamel and dentin. CONCLUSIONS: All tested resin-cements showed radiopacity values higher than that of dentin which is adequate for diagnostic purposes according to ISO recommendation. CLINICAL SIGNIFICANCE: The use of resin cement with adequate radiopacity for adhesive cementation of glass-ceramic based restorations enables their radiographic monitoring. (J Esthet Restor Dent 29:215-221, 2017).