Mechanophysical and Anti-Adhesive Properties of a Nanoclay-Containing PMMA Denture Resin.

Poly(methyl methacrylate) (PMMA) is commonly used for dental dentures, but it has the drawback of promoting oral health risks due to oral bacterial adhesion. Recently, various nanoparticles have been incorporated into PMMA to tackle these issues. This study aims to investigate the mechanophysical and antimicrobial adhesive properties of a denture resin by incorporating of nanoclay into PMMA. Specimens were prepared by adding 0, 1, 2, and 4 wt % surface-modified nanoclay (Sigma) to self-polymerizing PMMA denture resin. These specimens were then evaluated using FTIR, TGA/DTG, and FE-SEM with EDS. Various mechanical and surface physical properties, including nanoindentation, were measured and compared with those of pure PMMA. Antiadhesion experiments were conducted by applying a Candida albicans (ATCC 11006) suspension to the surface of the specimens. The antiadhesion activity of C. albicans was confirmed through a yeast-wall component (mannan) and mRNA-seq analysis. The bulk mechanical properties of nanoclay-PMMA composites were decreased compared to those of pure PMMA, while the flexural strength and modulus met the ISO 20795-1 requirement. However, there were no significant differences in the nanoindentation hardness and elastic modulus. The surface energy revealed a significant decrease at 4 wt % nanoclay-PMMA. The antiadhesion effect of Candida albicans was evident along with nanoclay content in the nanocomposites and confirmed by the reduced attachment of mannan on nanoclay-PMMA composites. mRNA-seq analysis supported overall transcriptome changes in altering attachment and metabolism behaviors on the surface. The nanoclay-PMMA materials showed a lower surface energy as the content increased, leading to an antiadhesion effect against Candida albicans. These findings indicate that incorporating nanoclay into PMMA surfaces could be a valuable strategy for preventing the fungal biofilm formation of denture base materials.

Through-hole composite membrane with an ultrathin oxide shell for highly robust and transparent air filters.

Exploring pore structures that are optically transparent and have high filtration efficiency for ultrafine dust is very important for realizing passive window filters for indoor air purification. Herein, a polyester track-etched (PETE) membrane with vertically perforated micropores is investigated as a cost-effective candidate for transparent window filters. The pore size, which governs transparency and filtration efficiency, can be precisely tuned by conformally depositing an ultrathin oxide layer on the PETE membrane via atomic layer deposition. The maximum visible light transmittance (∼81.2 %) was achieved with an alumina layer of approximately 55 nm, and the resulting composite membrane exhibited competitive filtration efficiency compared to commercial products. The chemically inert alumina layer also increased resistance to various external stimuli and enabled simple cleaning of the contaminated membrane surface with a solvent. The membrane installed on an insect screen effectively maintained its filtration performance (∼85 % for PM2.5) even after 10 reuse cycles under extremely harsh conditions (PM2.5 concentration: ∼5000 µg cm-3). The proposed through-hole composite membrane can expand the choice of aesthetic window filters to situations that require high outside visibility and daylighting.

Hyperelastic, shape-memorable, and ultra-cell-adhesive degradable polycaprolactone-polyurethane copolymer for tissue regeneration.

Novel polycaprolactone-based polyurethane (PCL-PU) copolymers with hyperelasticity, shape-memory, and ultra-cell-adhesion properties are reported as clinically applicable tissue-regenerative biomaterials. New isosorbide derivatives (propoxylated or ethoxylated ones) were developed to improve mechanical properties by enhanced reactivity in copolymer synthesis compared to the original isosorbide. Optimized PCL-PU with propoxylated isosorbide exhibited notable mechanical performance (50 MPa tensile strength and 1150% elongation with hyperelasticity under cyclic load). The shape-memory effect was also revealed in different forms (film, thread, and 3D scaffold) with 40%-80% recovery in tension or compression mode after plastic deformation. The ultra-cell-adhesive property was proven in various cell types which were reasoned to involve the heat shock protein-mediated integrin (α5 and αV) activation, as analyzed by RNA sequencing and inhibition tests. After the tissue regenerative potential (muscle and bone) was confirmed by the myogenic and osteogenic responses in vitro, biodegradability, compatible in vivo tissue response, and healing capacity were investigated with in vivo shape-memorable behavior. The currently exploited PCL-PU, with its multifunctional (hyperelastic, shape-memorable, ultra-cell-adhesive, and degradable) nature and biocompatibility, is considered a potential tissue-regenerative biomaterial, especially for minimally invasive surgery that requires small incisions to approach large defects with excellent regeneration capacity.

Characterization of Physical and Biological Properties of a Caries-Arresting Liquid Containing Copper Doped Bioglass Nanoparticles.

Silver diamine fluoride (SDF) is an outstanding dental material for arresting and preventing caries, but some drawbacks, such as high flowability due to low viscosity and cytotoxicity to the pulp, have been reported. To overcome these problems, copper-doped bioactive glass nanoparticles (CuBGns) were combined with SDF. After synthesis, CuBGns were examined by physical analysis and added in SDF at different weight/volume% (SDF@CuBGn). After assessing physical properties (viscosity and flowability) of SDF@CuBGn, physicochemical properties (morphology before and after simulated body fluid (SBF) immersion and ion release) of SDF@CuBGn-applied hydroxyapatite (HA) discs were evaluated. Biological properties were further evaluated by cytotoxicity test to pulp stem cells and antibacterial effect on cariogenic organisms (Streptococcus mutans and Staphylococcus aureus). Combining CuBGns in SDF increased the viscosity up to 3 times while lowering the flowability. More CuBGns and functional elements in SDF (Ag and F) were deposited on the HA substrate, even after SBF immersion test for 14 days, and they showed higher Cu, Ca, and Si release without changing F and Ag release. Cell viability test suggested lower cytotoxicity in SDF@CuBGn-applied HA, while CuBGns in SDF boosted antibacterial effect against S. aureus, ~27% in diameter of agar diffusion test. In conclusion, the addition of CuBGn to SDF enhances viscosity, Ag and F deposition, and antibacterial effects while reducing cell toxicity, highlighting the role of bioactive CuBGns for regulating physical and biological effects of dental materials.

Improvement of Biological Effects of Root-Filling Materials for Primary Teeth by Incorporating Sodium Iodide.

Therapeutic iodoform (CHI3) is commonly used as a root-filling material for primary teeth; however, the side effects of iodoform-containing materials, including early root resorption, have been reported. To overcome this problem, a water-soluble iodide (NaI)-incorporated root-filling material was developed. Calcium hydroxide, silicone oil, and NaI were incorporated in different weight proportions (30:30:X), and the resulting material was denoted DX (D5~D30), indicating the NaI content. As a control, iodoform instead of NaI was incorporated at a ratio of 30:30:30, and the material was denoted I30. The physicochemical (flow, film thickness, radiopacity, viscosity, water absorption, solubility, and ion releases) and biological (cytotoxicity, TRAP, ARS, and analysis of osteoclastic markers) properties were determined. The amount of iodine, sodium, and calcium ion releases and the pH were higher in D30 than I30, and the highest level of unknown extracted molecules was detected in I30. In the cell viability test, all groups except 100% D30 showed no cytotoxicity. In the 50% nontoxic extract, D30 showed decreased osteoclast formation compared with I30. In summary, NaI-incorporated materials showed adequate physicochemical properties and low osteoclast formation compared to their iodoform-counterpart. Thus, NaI-incorporated materials may be used as a substitute for iodoform-counterparts in root-filling materials after further (pre)clinical investigation.

Investigating the mechanophysical and biological characteristics of therapeutic dental cement incorporating copper doped bioglass nanoparticles.

OBJECTIVE: This study was investigated the mechanophysical properties of zinc phosphate cement (ZPC) with or without the copper doped bioglass nanoparticles (Cu-BGn) and their biological effect on dental pulp human cells and bacteria. MATERIALS AND METHODS: Cu-BGn were synthesized and characterized firstly and then, the experimental (Cu-ZPC) and control (ZPC) samples were fabricated with similar sizes and/or dimensions (diameter: 4 mm and height: 6 mm) based on the International Organization of Standards (ISO). Specifically, various concentrations of Cu-BGn were tested, and Cu-BGn concentration was optimized at 2.5 wt% based on the film thickness and overall setting time. Next, we evaluated the mechanophysical properties such as compressive strength, elastic modulus, hardness, and surface roughness. Furthermore, the biological behaviors including cell viability and odontoblastic differentiation by using dental pulp human cells as well as antibacterial properties were investigated on the Cu-ZPC. All data were analyzed statistically using SPSS® Statistics 20 (IBM®, USA). p < 0.05 (*) was considered significant, and 'NS' represents nonsignificant. RESULTS: Cu-BGn was obtained via a sol-gel method and added onto the ZPC for fabricating a Cu-ZPC composite and for comparison, the Cu-free-ZPC was used as a control. The film thickness (≤ 25 µm) and overall setting time (2.5-8 min) were investigated and the mechanophysical properties showed no significance ('NS') between Cu-ZPC and bare ZPC. However, cell viability and odontoblastic differentiation, alkaline phosphate (ALP) activity and alizarin red S (ARS) staining were highly stimulated in the extracts from the Cu-ZPC group compared to the ZPC group. Additionally, the antibacterial test showed that the Cu-ZPC extracts were more effective than the ZPC extracts (p < 0.05). SIGNIFICANCE: Cu-ZPC showed adequate mechanophysical properties (compressive strength, hardness, and surface roughness) and enhanced odontoblastic differentiation as well as antibacterial properties compared to the ZPC-only group. Based on the findings, the fabricated Cu-ZPC might have the potential for use in the field of dental medicine and clinical applications.

Comparison of Mechanical Properties of Chairside CAD/CAM Restorations Fabricated Using a Standardization Method.

The aim of this in vitro study was to investigate the fracture resistance, fracture failure pattern, and fractography of four types of chairside computer-aided design/computer-aided manufacturing (CAD/CAM) restoration materials in teeth and titanium abutments fabricated using a standardization method. An artificial mandibular left first premolar prepared for all-ceramic crown restoration was scanned. Forty extracted mandibular molars and cylindrical titanium specimens were milled into a standardized shape. A total of eighty CAD/CAM restoration blocks were milled into a crown and twenty pieces of each lithium disilicate (LS), polymer-infiltrated-ceramic-network (PICN), resin nano ceramic (RNC), and zirconia-reinforced lithium silicate (ZLS) materials were used. Crowns were bonded to abutments, and all specimens underwent thermal cycling treatment for 10,000 cycles. Fracture resistance was measured using a universal testing machine and fracture failure patterns were analyzed using optical microscopy and scanning electron microscopy. Statistical differences were analyzed using appropriate ANOVA, Tukey HSD post hoc tests, and independent sample t-tests (α = 0.05). The results indicated that, in both teeth abutments and titanium abutments, the fracture resistances showed significantly the highest values in LS and the second highest in ZLS (p < 0.05). The fracture resistances based on teeth abutments and titanium abutments were significantly different in all the CAD/CAM restoration materials (p < 0.05). There are statistically significant correlations between the types of materials and the types of abutments (p < 0.05). Each of the different materials showed different fracture failure patterns, and there was no noticeable difference in fractographic analysis. Lithium disilicates and zirconia-reinforced lithium silicates exhibited statistically high fracture resistance, indicating their suitability as restoration materials for natural teeth or implant abutments. There were no distinct differences in the fracture pattern based on the restoration and abutment materials showed that the fracture initiated at the groove where the ball indenter was toughed and propagated toward the axial wall.

Influence of Sequential CAD/CAM Milling on the Fitting Accuracy of Titanium Three-Unit Fixed Dental Prostheses.

This study investigated the fitting accuracy of titanium alloy fixed dental prostheses (FDP) after sequential CAD/CAM (Computer Aided Design/Computer Aided Manufacturing) fabrication. A three-unit FDP model connecting mandibular second premolars and molars was prepared and scanned to fabricate titanium FDPs by CAD/CAM milling. A total of six FDPs were sequentially milled in one titanium alloy disk using a new set of burs every time (n = 4). The fitting accuracy of FDPs was mesiodistally evaluated by a silicone replica technique and the measurement was triplicated at four different locations: MO (marginal opening), MG (marginal gap), AG (axial gap), and OG (occlusal gap). Data were statistically analyzed using ANOVA and Tukey's HSD test. The fitting accuracy of PMMA (polymethyl methacrylate) FDPs milled using the worn or new bur were evaluated by the same procedure (n = 6). The mean dimensions of titanium FDP for all measuring positions, except for AG, were significantly increased from the third milling. However, no difference was noted between the first FDP and the second FDP milled with the same set of burs. Severe edge chippings were observed in all milling burs. Detrimental effects of the worn burs on the fitting accuracy were demonstrated in the CAD/CAM-milled PMMA FDP. The results recommend proper changing frequency of cutting burs to achieve the quality of fit and predictable outcomes for dental CAD/CAM prostheses.

Calcium Silicate-Based Biocompatible Light-Curable Dental Material for Dental Pulpal Complex.

Dental caries causes tooth defects and clinical treatment is essential. To prevent further damage and protect healthy teeth, appropriate dental material is a need. However, the biocompatibility of dental material is needed to secure the oral environment. For this purpose, biocompatible materials were investigated for incorporated with dental capping material. Among them, nanomaterials are applied to dental materials to enhance their chemical, mechanical, and biological properties. This research aimed to study the physicochemical and mechanical properties and biocompatibility of a recently introduced light-curable mineral trioxide aggregate (MTA)-like material without bisphenol A-glycidyl methacrylate (Bis-GMA). To overcome the compromised mechanical properties in the absence of Bis-GMA, silica nanoparticles were synthesized and blended with a dental polymer for the formation of a nano-network. This material was compared with a conventional light-curable MTA-like material that contains Bis-GMA. Investigation of the physiochemical properties followed ISO 4049. Hydroxyl and calcium ion release from the materials was measured over 21 days. The Vickers hardness test and three-point flexural strength test were used to assess the mechanical properties. Specimens were immersed in solutions that mimicked human body plasma for seven days, and surface characteristics were analyzed. Biological properties were assessed by cytotoxicity and biomineralization tests. There was no significant difference between the tested materials with respect to overall physicochemical properties and released calcium ions. The newly produced material released more calcium ions on the third day, but 14 days later, the other material containing Bis-GMA released higher levels of calcium ions. The microhardness was reduced in a low pH environment, and differences between the specimens were observed. The flexural strength of the newly developed material was significantly higher, and different surface morphologies were detected. The recently produced extract showed higher cell viability at an extract concentration of 100%, while mineralization was clear at the conventional concentration of 25%. No significant changes in the physical properties between Bis-GMA incorporate material and nanoparticle incorporate materials.

Antibacterial, proangiogenic, and osteopromotive nanoglass paste coordinates regenerative process following bacterial infection in hard tissue.

Bacterial infection raises serious concerns in tissue repair settings involved with implantable biomaterials, devastating the regenerative process and even life-threatening. When hard tissues are infected with bacteria (called 'osteomyelitis'), often the cases in open fracture or chronic inflammation, a complete restoration of regenerative capacity is significantly challenging even with highly-dosed antibiotics or surgical intervention. The implantable biomaterials are thus needed to be armored to fight bacteria then to relay regenerative events. To this end, here we propose a nanoglass paste made of ~200-nm-sized silicate-glass (with Ca, Cu) particles that are hardened in contact with aqueous medium and multiple-therapeutic, i.e., anti-bacterial, pro-angiogenic and osteopromotive. The nanoglass paste self-hardened via networks of precipitated nano-islands from leached ions to exhibit ultrahigh surface area (~300 m2/g), amenable to fill tunable defects with active biomolecular interactions. Also, the nanoglass paste could release multiple ions (silicate, calcium, and copper) at therapeutically relevant doses and sustainably (for days to weeks), implying possible roles in surrounding cells/tissues as a therapeutic-ions reservoir. The osteopromotive effects of nanoglass paste were evidenced by the stimulated osteogenic differentiation of MSCs. Also, the nanoglass paste promoted angiogenesis of endothelial cells in vitro and vasculature formation in vivo. Furthermore, the significant bactericidal effect of nanoglass paste, as assessed with E. coli and S. aureus, highlighted the role of copper played in elevating ROS level and destroying homeostasis, which salvaged tissue cells from co-cultivated bacteria contamination. When administered topically to rat tibia osteomyelitis defects, the nanoglass paste enhanced in vivo bone healing and fracture resistance. The developed nanoglass paste, given its self-setting property and the coordinated therapeutic actions, is considered to be a promising drug-free inorganic biomaterial platform for the regenerative therapy of bacteria-infected hard tissues.