RESUMO
We report the results of synthesis of zinc selenide (ZnSe) nanocrystals into SiO2/Si track templates formed by irradiation with 200 MeV Xe ions up to a fluence of 107 ions/cm2. Zinc selenide nanocrystals were obtained by chemical deposition from the alkaline aqueous solution. Scanning electron microscopy, X-ray diffractometry, Raman and photoluminescence spectroscopy, and electrical measurements were used for characterization of synthesized ZnSe/SiO2nanoporous/Si nanocomposites. XRD data for as-deposited precipitates revealed the formation of ZnSe nanocrystals with cubic crystal structure, spatial syngony F-43m (216). According to non-empirical calculations using GGA-PBE and HSE06 functionals, ZnSe crystal is a direct-zone crystal with a minimum bandgap width of 2.36 eV and anisotropic electronic distribution. It was found that a thermal treatment of synthesized nanocomposites at 800 °C results in an increase in ZnSe nanocrystallites size as well as an increase in emission intensity of created precipitates in a broad UV-VIS spectra range. However, vacuum conditions of annealing still do not completely prevent the oxidation of zinc selenide, and a formation of hexagonal ZnO phase is registered in the annealed samples. The current-voltage characteristics of the synthesized nanocomposites proved to have n-type conductivity, as well as increased conductivity after annealing.
RESUMO
Electrochemical deposition into a prepared SiO2/Si-p ion track template was used to make orthorhombic SnO2 vertical nanowires (NWs) for this study. As a result, a SnO2-NWs/SiO2/Si nanoheterostructure with an orthorhombic crystal structure of SnO2 nanowires was obtained. Photoluminescence excited by light with a wavelength of 240 nm has a low intensity, arising mainly due to defects such as oxygen vacancies and interstitial tin or tin with damaged bonds. The current-voltage characteristic measurement showed that the SnO2-NWs/SiO2/Si nanoheterostructure made this way has many p-n junctions.
RESUMO
Samples of ZrO2 ceramics with different concentrations of impurity titanium ions were synthesized by mixing zirconium and titanium oxide powders in different mass ratios. The X-ray diffraction analysis was used to determine the phase composition, lattice parameters, and crystallite size of the ceramics with varying dopant concentrations. Upon irradiation of the samples with 220 MeV Xe ions to a fluence of 1010 ions/cm2, a decrease in the intensity of the pulsed cathodoluminescence band at 2.5 eV was observed. Additionally, ion irradiation resulted in the emergence of a new thermoluminescence peak at 450-650 K attributed to radiation-induced traps of charge carriers. Further analysis revealed that the thermoluminescence curves of samples irradiated with electrons and ions comprise a superposition of several elementary peaks. Notably, a complex non-monotonic dependence of cathodo- and thermoluminescence intensity on titanium concentration was observed, suggesting the influence of concentration quenching and the presence of tunneling transitions.
RESUMO
A synthetic single crystal of magnesium-aluminate spinel was irradiated perpendicularly to the (111) plane with swift heavy xenon ions with an energy of 220 MeV. The modified layer was attested based on Raman scattering spectra recorded while focusing on the surface. A decrease in surface crystallinity was observed, reflected in the changes in fundamental optical characteristics such as the band gap and the energies of static and dynamic disorder. In this study, we demonstrate, along with the modification of optical characteristics and the formation of a disordered layer, the creation of new optically active centers. The luminescent properties of these centers were analyzed. The effect of temperature flare-up in the 3.4 eV band of the excitation spectrum was determined. The low sensitivity of Cr3+ luminescence to SHI is demonstrated.
RESUMO
In In this study, the optical properties of magnesium-aluminate spinel were examined after being irradiated with 220 MeV Xe ions. The research aimed to simulate the impact of nuclear fuel fission fragments on the material. The following measurements were taken during the experiments: transmission spectra in the IR region (190-7000) nm, optical absorption spectra in the range (1.2-6.5) eV, and Raman spectra were measured along the depth of ion penetration from the surface to 30 µm. A peak with a broad shape at approximately 5.3 eV can be observed in the optical absorption spectrum of irradiated spinel crystals. This band is linked to the electronic color centers of F+ and F. Meanwhile, the band with a maximum at ~(3-4) eV is attributed to hole color centers. Apart from the typical Raman modes of an unirradiated crystal, additional modes, A1g* (720 cm-1), and Eg* (385 cm-1), manifested mainly as an asymmetric shoulder of the main Eg mode, are also observed. In addition, the Raman spectroscopy method showed that the greatest disordering of crystallinity occurs in the near-surface layer up to 4 µm thick. At the same time, Raman scattering spectroscopy is sensitive to structural changes almost up to the simulated value of the modified layer, which is an excellent express method for certifying the structural properties of crystals modified by swift heavy ions.