Synthesis and characterization of magnetic bifunctional nano-catalyst for the production of biodiesel from Madhuca indica oil.

The reusable magnetic multimetal nano-catalyst (Fe3O4.Cs2O) was synthesized using co-precipitation and incipient wetness impregnation methods. It was used to esterify and transesterify Madhuca indica (M. indica) oil to produce biodiesel with methanol. The prepared catalyst, caesium oxide doped on the nano-magnetite core, was characterized using field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). Further, the activity of the catalyst was investigated by subjecting it to a biodiesel reaction. To maximize biodiesel conversion, studies were carried out by varying the process variables like catalyst concentration, methanol-to-oil molar ratio, reaction temperature, and reaction time. A maximum conversion of 97.4% was obtained at the holding conditions of 18:1 methanol-to-oil ratio, 7 wt% catalyst loading, 65 °C reaction temperature, and 300 min reaction time. Moreover, the catalyst recyclability study showed that it could be recycled up to 12 cycles with a conversion of 90% and above. The biodiesel's fuel properties were analysed and found to be within the limits of ASTM D6751 standard.

Storage of Na in 2D SnS for Na ion batteries: a DFT prediction.

The high demand for renewable and clean energy has driven the exploration of advanced energy storage systems. Sodium-ion batteries (SIBs) are considered to be potential substitutes for Li-ion batteries (LIBs) because they are manufactured from raw materials that are cheap, less toxic, and abundantly available. Recent developments have demonstrated that two-dimensional (2D) materials have gained increasing interest as electrode candidates for efficient SIBs because of their enormous surface area and sufficient accommodating sites for the storage of Na ions. Herein, we explore the binding and diffusion mechanisms of Na on a 2D SnS sheet using density functional theory (DFT). The outcomes reveal that Na has a strong binding strength with SnS as well as charge transfer from Na to SnS, which affirms an excellent electrochemical performance. A transition from semiconducting (1.4 eV band gap) to metallic has been noted in the electronic structure after loading a minor amount of Na. In addition, a low open-circuit voltage (OCV) of 0.87 V and a high storage capacity of 357 mA h g-1 show the suitability of the SnS monolayer for SIBs. In addition, the low activation barrier for Na migration (0.13 eV) is attractive for a fast sodiation/desodiation process. Henceforth, these encouraging outcomes suggest the application of the SnS sheet as an excellent anode for next-generation SIBs.

Spray-Deposited Rare Earth Metal Ion (Sm3+, Ce3+, Pr3+, La3+)-Doped CdO Thin Films for Enhanced Formaldehyde Gas Sensing Characteristics.

This study shows the electrical conductivity-dependent gas sensing characteristics of spray-deposited rare earth (RE) metal ion (Sm3+, Ce3+, Pr3+, La3+)-doped cadmium oxide (CdO) thin films on soda-lime microscope glass substrates at 300 °C. We examined the deposited films' structural, surface microstructural, DC electrical, and gas sensing features. The X-ray diffraction study indicates that all samples were polycrystalline, with the favored growth direction shifting from the (111) plane to the (200) plane. The highest root-mean-square values were obtained for the Pr-doped CdO thin film (5.86 nm). The surface microstructure of CdO thin films was significantly influenced by the RE metal ion dopant, with typical grain size values ranging from 64 nm to 134 nm depending on the dopant. The carrier concentration and resistivity of CdO films vary based on the RE metal ions used as dopants. Low resistivity (3.01 × 10-4 Ω.cm) was achieved for the CdO thin film doped with La. High gas sensitivity (71.42%) was achieved for CdO thin films doped with La. The donor dopant regulated the electrical conductivity and gas sensing capabilities of CdO thin films.

Vanadium Carbide (V4C3) MXene as an Efficient Anode for Li-Ion and Na-Ion Batteries.

Li-ion batteries (LIBs) and Na-ion batteries (SIBs) are deemed green and efficient electrochemical energy storage and generation devices; meanwhile, acquiring a competent anode remains a serious challenge. Herein, the density-functional theory (DFT) was employed to investigate the performance of V4C3 MXene as an anode for LIBs and SIBs. The results predict the outstanding electrical conductivity when Li/Na is loaded on V4C3. Both Li2xV4C3 and Na2xV4C3 (x = 0.125, 0.5, 1, 1.5, and 2) showed expected low-average open-circuit voltages of 0.38 V and 0.14 V, respectively, along with a good Li/Na storage capacity of (223 mAhg-1) and a good cycling performance. Furthermore, there was a low diffusion barrier of 0.048 eV for Li0.0625V4C3 and 0.023 eV for Na0.0625V4C3, implying the prompt intercalation/extraction of Li/Na. Based on the findings of the current study, V4C3-based materials may be utilized as an anode for Li/Na-ion batteries in future applications.