The effect of carbon black reinforcement on the dynamic fatigue and creep of polyisobutylene-based biomaterials.

This paper investigates the structure-property relationship of a new generation of poly(styrene-b-isobutylene-b-styrene) (SIBS) block copolymers with a branched (dendritic) polyisobutylene core with poly(isobutylene-b-para-methylstyrene) end blocks (D_IBS), and their carbon black (CB) composites. These materials display thermoplastic elastomeric (TPE) properties, and are promising new biomaterials. It is shown that CB reinforced the block copolymer TPEs, effectively delayed the oxidative thermal degradation of the D_IBS materials, and greatly improved their dynamic fatigue performance. Specifically, the dynamic creep of a CB composite was comparable to that of chemically crosslinked and silica-reinforced medical grade silicone rubber, used as a benchmark biomaterial.

Investigation of structure-property relationships of polyisobutylene-based biomaterials: Morphology, thermal, quasi-static tensile and long-term dynamic fatigue behavior.

This study examines the morphology, thermal, quasi-static and long-term dynamic creep properties of one linear and three arborescent polyisobutylene-based block copolymers (L_SIBS31, D_IBS16, D_IBS27 and D_IBS33). Silicone rubber, a common biopolymer, was considered as a benchmark material for comparison. A unique hysteretic testing methodology of Stepwise Increasing Load Test (SILT) and Single Load Test (SLT) was used in this study to evaluate the long-term dynamic fatigue performance of these materials. Our experimental findings revealed that the molecular weight of polyisobutylene (PIB) and polystyrene (PS) arms [M(n)(PIB(arm)) and M(n)(PS(arm))], respectively had a profound influence on the nano-scaled phase separation, quasi-static tensile, thermal transition, and dynamic creep resistance behaviors of these PIB-based block copolymers. However, silicone rubber outperformed the PIB-based block copolymers in terms of dynamic creep properties due to its chemically crosslinked structure. This indicates a need for a material strategy to improve the dynamic fatigue and creep of this class of biopolymers to be considered as alternative to silicone rubber for biomedical devices.

Comparative study of a block copolymer morphology by transmission electron microscopy and scanning force microscopy.

Using transmission electron microscopy (TEM) and scanning force microscopy (SFM) together, it was possible to verify important structural features of a nanostructured bulk material such as the kp-morphology in an ABC triblock copolymer. By applying suitable imaging techniques during the SFM measurements it was possible to determine the morphology without additional manipulation steps in between. In comparison, TEM investigations on this type of material usually require selective staining procedures prior to the measurement. Also electron beam damage is often encountered during TEM measurements especially if components such as poly(methacrylates) are present. In contrast, SFM measurements can be assumed not to significantly change the phase dimensions of the components.