Electrochemical dissolution of nickel-titanium instrument fragments in root canals of extracted human maxillary molars using a small reservoir of electrolyte.

AIM: To evaluate the viability of the electrochemical dissolution of fragments of fractured NiTi instruments in root canals of extracted human maxillary molars, using two electrodes and the solution restricted to a small reservoir coupled to the pulp chamber. The primary hypothesis was that this method enables the reduction of fragment volume and re-establishment of the root canal path with a size 08 K-file, both in simulated canals and in extracted human maxillary molars. METHODOLOGY: Fragments of F1 ProTaper instruments were polarized in simulated root canals and in distobuccal root canals of extracted maxillary molars using a new method, with the solution restricted to a small acrylic microcell coupled to each resin block or pulp chamber. Two electrodes were used, where one was kept in contact with the intracanal fragment and another was positioned in the solution present in the acrylic microcell. After the tests, a size 08 K-file was used passively to verify the possibility of bypassing the fragment, which was also confirmed by radiographic analysis. Micro-CT analysis of the teeth was used before and after fragment dissolution to evaluate the volume, length and porosity of the fragments. The D'Agostino-Pearson normality test was used to verify the distribution of the data. A paired t-test (P < 0.05) was used to compare the volume, length and porosity of the fragments before and after the dissolution tests. RESULTS: After dissolution, all fragments could be bypassed with a size 08 K-file in both simulated canals and in extracted teeth. The dissolution process did not result in significant reduction of neither the fragment length nor the fragment porosity. However, it resulted in a significant reduction of fragment volume (paired t-test, P < 0.05). CONCLUSION: The electrochemical dissolution of fragments of NiTi files in root canals of extracted human maxillary molars using two electrodes, and the solution restricted to a small reservoir coupled to the pulp chamber resulted in a significant reduction of fragment volume. The re-establishment of the root canal path with the passive insertion of size 08 K-files was possible in all samples after the tests, both in simulated canals and in extracted teeth.

Evaluation of the effects of the solution used for electrochemical dissolution of nickel-titanium endodontic files on dentine structure, microhardness and cell viability.

AIM: To evaluate the effects of the [NaF 12 g L-1  + NaCl 1 g L-1 ] solution used in the electrochemical dissolution process of fractured endodontic files, as well as its NiTi-containing product, on dentine hardness, topography and human fibroblast viability. METHODOLOGY: Sixty single-rooted human teeth were evaluated for dentine microhardness using the Vickers hardness test and the area and number of dentinal tubules by scanning electron microscopy. The samples were divided according to the dentine surface treatment: distilled water; 17% EDTA; [NaF 12 g L-1  + NaCl 1 g L-1 ]; and 17% EDTA + [NaF 12 g L-1  + NaCl 1 g L-1 ]. Thirty-six single-rooted human teeth were divided according to the irrigation protocol: Dulbecco's Modified Eagle's Medium + 10% foetal bovine serum; 5.25% NaOCl; [NaF 12 g L-1  + NaCl 1 g L-1 ]; and [NaF 12 g L-1  + NaCl 1 g L-1  + NiTi]. The extracts in contact with the apical foramen were used in the MTT assay to evaluate human fibroblast viability, with dilutions of 100%, 50%, 25% and 12.5%. Statistical tests used were paired t-tests, one-way anova, Tukey's test, Kruskal-Wallis test and Dunn's post-test. RESULTS: The [NaF 12 g L-1  + NaCl 1 g L-1 ] solution did not modify dentine microhardness or the average dentinal tubule area. However, EDTA induced changes in dentine structure and microhardness (P < 0.05). The [NaF 12 g L-1  + NaCl 1 g L-1 ] solution, and its NiTi-containing product had lower cytotoxicity than NaOCl at dilutions of 25% and 50% (P < 0.01). CONCLUSIONS: The [NaF 12 g L-1  + NaCl 1 g L-1 ] solution did not alter dentine microhardness or damage the dentine structure. It also demonstrated lower cytotoxicity than NaOCl.

Influence of clinical use on physical-structural surface properties and electrochemical potential of NiTi endodontic instruments.

AIM: To investigate the surface morphology and electrochemical potential of superelastic (SE), M-Wire (MW) and shape memory technology (SMT) NiTi instruments before and after single clinical use in vivo. METHODOLOGY: A total of 60 ProTaper Universal F2 (PTU-SE), ProTaper Next X2 (PTN-MW), Typhoon (TYP), Hyflex (HF) and Vortex Blue (VB), the last three SMT, and size 25, .06 taper (n = 6 of each type) files were examined. Scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS) and electrochemical potential analysis were employed before and after clinical use. Statistical analysis was performed with one-way analysis of variance and Bonferroni's post hoc test. Significance was determined at the 95% confidence level for both tests. RESULTS: SEM observations of new instruments indicated the presence of marks left by the machining process during manufacturing and EDS revealed the existence of an oxide coating on shape memory instruments. After clinical use, the five types were associated with propagation of transverse cracks 3 mm from the tip. The surface oxide layer of TYP, HF and VB instruments had microcracks in multiple directions, whilst TYP and HF had fragmentation in chip form of the oxide layer. EDS analysis demonstrated a significant reduction of the oxide layer in shape memory instruments, except for VB. Electrochemical potentials were higher for shape memory instruments than for M-Wire and superelastic NiTi instruments, respectively (P < 0.05). CONCLUSIONS: It appears that shape memory technology NiTi instruments have a dysfunctional oxide layer after clinical use. Additionally, they featured higher electrochemical potential relative to NiTi instruments manufactured from M-Wire, and conventional superelastic NiTi alloy.

Electrochemical-induced dissolution of stainless steel files.

AIM: To investigate the effectiveness of the dissolution process when hand stainless steel files are polarized in solutions containing chloride and fluoride to promote their dissolution. METHODOLOGY: Redox curves and anodic polarization curves were obtained to determine the conditions necessary for the dissolution of stainless steel endodontic files. Anodic polarization of sizes 20 and 30 files was performed, and a t-test (P < 0.05) was used to compare the weight loss, the time of dissolution and the electrical charge generated by both groups of files. Fragments were polarized in simulated root canals to evaluate the dissolution process. After the tests, a size 10 K-file was used to verify the possibility of bypassing the fragment. Radiographic analysis of the simulated canals was used before and after the tests to verify fragment dissolution. RESULTS: A progressive consumption of the sizes 20 and 30 files was observed with total polarization times of 7.0 and 9.0 min, respectively. Files with the larger diameters exhibited greater weight loss, longer times of dissolution and generated a greater electrical charge during the active dissolution process (t-test, P < 0.05). After 60 min, the anodic polarization of file fragments in simulated root canals resulted in their partial dissolution. CONCLUSION: A 60-min anodic polarization of stainless steel K-file fragments in simulated root canals resulted in their partial dissolution. The fragments could be bypassed after the test.

Hypertension favors the inflammatory process in rats with experimentally induced periodontitis.

BACKGROUND AND OBJECTIVE: Cardiovascular diseases are significantly correlated with chronic periodontitis. The aim of this study was to evaluate bone-loss level, neutrophil migration, CXCL2/CINC-2α, CXCL5/LIX, CCL20/MIP-3α and tumor necrosis factor-α (TNF-α) production, inducible nitric oxide synthase (iNOS) expression and C-reactive protein (CRP) release in spontaneously hypertensive rats (SHRs) and normotensive (WTK) rats after experimental induction of periodontal disease. MATERIAL AND METHODS: Periodontitis was induced by placement of silk yarn ligatures around the first molar counterparts. The levels of CRP, CCL20/MIP-3α and CXCL5/LIX were evaluated in the peripheral blood, and bone-loss level, neutrophil recruitment, the production of myeloperoxidase, CXCL2, CXCL5, CCL20 and TNF-α, and the expression of iNOS were evaluated in the gingival tissue. Histological sections were taken to evaluate and measure bone resorption and neutrophil recruitment in the furcation region. RESULTS: Rats with periodontitis had alveolar bone resorption. SHRs with periodontitis showed marked bone loss and increased neutrophil infiltration in comparison with WTK rats. SHRs with periodontitis showed increased levels of TNF-α and CXCL2, and a slight tendency for increased levels of CXCL5, in the gingival tissue but no increase in the level of CCL20. In SHRs, even without periodontitis, the levels of TNF-α, CXCL2, CXCL5 and CCL20 showed a slight tendency to increase. In the WTK rats, TNF-α, CXCL2 and CXCL5 levels were increased with periodontitis, but the level of CCL20 was not. iNOS was expressed in the gingival tissue of WTK rats and SHRs with periodontitis; however, SHRs appeared to express a higher level of iNOS than did WKT rats. The CRP level was elevated in both types of rats with periodontitis; however, the CRP level was higher in SHRs with periodontitis than in WTK rats with periodontitis. CONCLUSION: In SHRs, the hypertensive condition per se seems to favor the inflammatory processes that become potentiated with periodontitis, when compared with WKT rats.