Chamber Protection of Zinc with Ethylhexanoic Acid.

Chamber protection is a promising and quickly developing method of vapor-phase protection of metals against atmospheric corrosion by inhibitors. It was shown that chamber treatment with 2-ethylhexanoic acid (EHA) efficiently inhibits the initiation of zinc corrosion. The optimum conditions (temperature and duration) of zinc treatment with vapors of this compound were determined. If these conditions are met, adsorption films of EHA with thicknesses up to 100 nm are formed on the metal surface. It was found that their protective properties increase during the first day as zinc is exposed to air after chamber treatment. The anticorrosive action of adsorption films is due both to the surface being shielded from the corrosive environment and to the inhibition of corrosion processes on the active surface of the metal. Corrosion inhibition was caused by the ability of EHA to convert zinc to the passive state and inhibit its local anionic depassivation.

Structuring of Surface Films Formed on Magnesium in Hot Chlorobenzotriazole Vapors.

Chamberprotection of metals from atmospheric corrosion is a variety of vapor-phase inhibition. It is based on the effect of adsorption films formed in the vapors of low-volatile corrosion inhibitors at elevated temperatures. The paper analyzes the specific features of the chamber protection of a magnesium alloy with chlorobenzotriazole. It has been found that the protective properties of surface films formed in hot vapors of this compound increase upon exposure of the metal to air. The processes of structuring of protective films that occur in this case have been studied by a set of corrosion, electrochemical and physical methods. It has been shown that chamber treatment of the alloy is accompanied by chlorobenzotriazole adsorption and uniform thickening of the surface oxide-hydroxide layer. In this case, the corrosion processes slow down by a factor of up to 10. Prolonged exposure of the samples in air after the chamber treatment results in additional oxidation of magnesium and hydroxylation of the oxide. However, the oxide-hydroxide layer does not grow on the entire surface, but as separate islets. Such a change in the structure of the surface films results in an additional 10-fold increase in the corrosion resistance of the magnesium alloy.