Dyeing of polyacrylonitrile knitted fabric using liposomes.

In this study, it was aimed to analyze the effects of liposomes on the dyeing of polyacrylonitrile fabrics. For this purpose, firstly liposome synthesis was carried out, and then liposome production was confirmed by Fourier transform infrared spectroscopy analysis. Additionally, zeta potential measurements were carried out to see whether stable structures were formed. Then, a selected basic dye was encapsulated with a liposome and the possibilities of using these capsules as alternative to retarders in the dyeing of polyacrylonitrile fabrics were examined. According to results obtained, it can be said that the 1% solution of synthesized liposomes creates a more stable suspension with a polydispersity index of 0.472 and the average particle size of 165.2 nm. On the other hand, it has been revealed that if 1% liposome is used in dyeing, a kind of retarder effect can be achieved in the dyeing of polyacrylonitrile fabrics. Moreover, it can be said that the decrease in color efficiency, that is, the loss of yield, caused by the use of liposome at the end of dyeing is lower compared to the retarder. This is also a very important issue, because a good retarder is expected to slow down the dye uptake, but not reduce the dye intake too much at the end of the dyeing. Dyeing levelness (%) was found to be 96.1, 97.4, and 97.1 for dyeings without auxiliary, with 1% cationic retarder and with 1% liposome, respectively. Beyond this, no significant difference was observed in terms of fastness of dyeing.

Silver Abietate and ß-Cyclodextrin Inclusion Complex Doped Poly(vinyl alcohol) Nanowebs.

In this study, guesthost inclusion complexes of silver abietate with ß-cyclodextrin were prepared by kneading and physical mixing techniques, and analyzed via fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analyser (TGA). The 1:1 and 1:2 stoichiometry of the guesthost were prepared. Obtained FTIR and TGA results showed that formation of silver abietate:ß-cyclodextrin (Ag-A:ß-CD) inclusion complexes occurred at a mass ratio of both 1:1 and 1:2. Furthermore, prepared Ag-A:ß-CD (1:2) inclusion complex was doped in Poly(vinyl alcohol) nanofibers during electrospinning process for obtaining nanowebs. The formation of nanowebs were investigated under scanning electron microscope (SEM), X-Ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analyser (TGA). The results confirmed Ag-A:ß-CD inclusion complex containing Poly(vinyl alcohol) (PVA) nanoweb production.

Determination of the color removal efficiency of laccase enzyme depending on dye class and chromophore.

The aim of this article was to clarify which type of dye chromophores could be decolorized efficiently with the use of laccase enzyme. For this purpose, enzymatic degradation of different type of dye classes (4 reactive, 2 acid and 1 basic dye) having various chromophore groups was investigated by using commercial laccase from Cerrena unicolor. It was observed that the chromophore structure of dye is very important on enzymatic color removal efficiency. According to the experimental results, it was found that color removal efficiencies (20 mg/L initial dye) were 98.7% for RB220 (0.1 g/L enzyme after 6 h), 95.1% for RB19 (0.1 g/L enzyme after 48 h), 90.8% for AR42 (0.1 g/L enzyme after 48 h) while they were 60.9% for AR114 (0.25 g/L enzyme), 58.6% for RB21 (0.5 g/L enzyme), 39.7% for RR239 (0.25 g/L enzyme) even after seven days. As a result, it can be said that the highest decolorization rate was achieved for the reactive dye having formazan copper complex (RB220) chromophore. On the other hand, the enzymatic degradation of basic dye (BB9) was found to be rather difficult compared to the acid and reactive dyes used in this study and the maximum color removal was 42.8% after seven days.