RESUMO
Materials that exhibit highly nonlinear behaviour are intricate to study. This is due to their physical properties, as they possess a very large deformation. Silicone rubber is among the materials that can be classified as possessing such characteristics, despite their being soft and frequently applied in medical applications. Due to their low mechanical properties, however, it is believed that a filler addition could enhance them. This study, therefore, aims to investigate the effect of the addition of bamboo cellulosic filler to silicone rubber in terms of its compressive properties in order to quantify its material constants using the hyperelastic theory, specifically the Neo-Hookean and Mooney-Rivlin models. The specimens' compressive properties were also compared between specimens immersed in seawater and those not immersed in seawater. The findings showed that the compressive properties, stiffness, and compressive strength of the bamboo cellulosic fibre reinforced the silicone rubber biocomposites, improved with higher bamboo filler addition. Specimens immersed in seawater showed that they can withstand a compressive load of up to 83.16 kPa in comparison to specimens not immersed in seawater (up to 79.8 kPa). Using the hyperelastic constitutive models, the Mooney-Rivlin model displayed the most accurate performance curve fit with the experimental compression data with an R2 of up to 0.9999. The material constant values also revealed that the specimens immersed in seawater improved in stiffness property, as the C1 material constant values are higher than for the specimens not immersed in seawater. From these findings, this study has shown that bamboo cellulosic filler added into silicone rubber enhances the material's compressive properties and that the rubber further improves with immersion in seawater. Thus, these findings contribute significantly towards knowledge of bamboo cellulosic fibre-reinforced silicone rubber biocomposite materials.
Assuntos
Elastômeros de Silicone , Força Compressiva , Estresse MecânicoRESUMO
The development of environmentally benign silicone composites from sugar palm fibre and silicone rubber was carried out in this study. The mechanical, physical, and morphological properties of the composites with sugar palm (SP) filler contents ranging from 0% to 16% by weight (wt%) were investigated. Based on the uniaxial tensile tests, it was found that the increment in filler content led to higher stiffness. Via dynamic mechanical analysis (DMA), the viscoelastic properties of the silicone biocomposite showed that the storage modulus and loss modulus increased with the increment in filler content. The physical properties also revealed that the density and moisture absorption rate increased as the filler content increased. Inversely, the swelling effect of the highest filler content (16 wt%) revealed that its swelling ratio possessed the lowest rate as compared to the lower filler addition and pure silicone rubber. The morphological analysis via scanning electron microscopy (SEM) showed that the sugar palm filler was evenly dispersed and no agglomeration could be seen. Thus, it can be concluded that the addition of sugar palm filler enhanced the stiffness property of silicone rubber. These new findings could contribute positively to the employment of natural fibres as reinforcements for greener biocomposite materials.