RESUMO
The separation of CO2 from N2 remains a highly challenging task in postcombustion CO2 capture processes, primarily due to the relatively low CO2 content (3-15%) compared to that of N2 (70%). This challenge is particularly prominent for carbon-based adsorbents that exhibit relatively low selectivity. In this study, we present a successfully implemented strategy to enhance the selectivity of composite aerogels made of reduced graphene oxide (rGO) and functionalized polymer particles. Considering that the CO2/N2 selectivity of the aerogels is affected on the one hand by the surface chemistry (offering more sites for CO2 capture) and fine-tuned microporosity (offering molecular sieve effect), both of these parameters were affected in situ during the synthesis process. The resulting aerogels exhibit improved CO2 adsorption capacity and a significant reduction in N2 adsorption at a temperature of 25 °C and 1 atm, leading to a more than 10-fold increase in selectivity compared to the reference material. This achievement represents the highest selectivity reported thus far for carbon-based adsorbents. Detailed characterization of the aerogel surfaces has revealed an increase in the quantity of surface oxygen functional groups, as well as an augmentation in the fractions of micropores (<2 nm) and small mesopores (<5 nm) as a result of the modified synthesis methodology. Additionally, it was found that the surface morphology of the aerogels has undergone important changes. The reference materials feature a surface rich in curved wrinkles with an approximate diameter of 100 nm, resulting in a selectivity range of 50-100. In contrast, the novel aerogels exhibit a higher degree of oxidation, rendering them stiffer and less elastic, resembling crumpled paper morphology. This transformation, along with the improved functionalization and augmented microporosity in the altered aerogels, has rendered the aerogels almost completely N2-phobic, with selectivity values ranging from 470 to 621. This finding provides experimental evidence for the theoretically predicted relationship between the elasticity of graphene-based adsorbents and their CO2/N2 selectivity performance. It introduces a new perspective on the issue of N2-phobicity. The outstanding performance achieved, including a CO2 adsorption capacity of nearly 2 mmol/g and the highest selectivity of 620, positions these composites as highly promising materials in the field of carbon capture and sequestration (CCS) postcombustion technology.
RESUMO
The main constraint on developing a full potential for CO2 adsorption of 3D composite monoliths made of reduced graphene oxide (rGO) and polymer materials is the lack of control of their textural properties, along with the diffusional limitation to the CO2 adsorption due to the pronounced polymers' microporosity. In this work, the textural properties of the composites were altered by employing highly crosslinked polymer particles, synthesized by emulsion polymerization in aqueous media. For that aim, waterborne methyl methacrylate (MMA) particles were prepared, in which the crosslinking was induced by using different quantities of divinyl benzene (DVB). Afterward, these particles were combined with rGO platelets and subjected to the reduction-induced self-assembly process. The resulting 3D monolithic porous materials certainly presented improved textural properties, in which the porosity and BET surface area were increased up to 100% with respect to noncrosslinked composites. The crosslinked density of MMA polymer particles was a key parameter controlling the porous properties of the composites. Consequently, higher CO2 uptake than that of neat GO structures and composites made of noncrosslinked MMA polymer particles was attained. This work demonstrates that a proper control of the microstructure of the polymer particles and their facile introduction within rGO self-assembly 3D structures is a powerful tool to tailor the textural properties of the composites toward improved CO2 capture performance.
RESUMO
There is a constant need for versatile technologies to reduce the continuously increasing concentration of CO2 in the atmosphere, able to provide effective solutions under different conditions (temperature, pressure) and composition of the flue gas. In this work, a combination of graphene oxide (GO) and functionalized waterborne polymer particles was investigated, as versatile and promising candidates for CO2 capture application, with the aim to develop an easily scalable, inexpensive, and environmentally friendly CO2 capture technology. There are huge possibilities of different functional monomers that can be selected to functionalize the polymer particles and to provide CO2-philicity to the composite nanostructures. Density functional theory (DFT) was employed to gain a deeper understanding of the interactions of these complex composite materials with CO2 and N2 molecules, and to build a basis for efficient screening for functional monomers. Estimation of the binding energy between CO2 and a set of GO/polymer composites, comprising copolymers of methyl methacrylate, n-butyl acrylate, and different functional monomers, shows that it depends strongly on the polymer functionalities. In some cases, there is a lack of cooperative effect of GO. It is explained by a remarkably strong GO-polymer binding, which induced less effective CO2-polymer interactions. When compared with experimental results, in the cases when the nanocomposite structures presented similar textural properties, the same trends for selective CO2 capture over N2 were attained. Besides novel functional materials for CO2 capture and a deeper understanding of the interactions between CO2 molecules with various materials, this study additionally demonstrates that DFT calculations can be a shorter route toward the efficient selection of the best functionalization of the composite materials for selective CO2 capture.
RESUMO
Because of its surface characteristics, once in the aquatic environment, graphene could act as a carrier of pollutants, such as polycyclic aromatic hydrocarbons (PAHs), to aquatic organisms. In this study we aimed to (1) assess the capacity of graphene oxide (GO) to sorb PAHs and (2) to evaluate the toxicity of GO alone and in combination with PAHs on zebrafish embryos and adults. GO showed a high sorption capacity for benzo(a)pyrene (B(a)P) (98% of B(a)P sorbed from a nominal concentration of 100 µg/L) and for other PAHs of the water accommodated fraction (WAF) of a naphthenic North Sea crude oil, depending on their log Kow (95.7% of phenanthrene, 84.4% of fluorene and 51.5% of acenaphthene). In embryos exposed to different GO nanomaterials alone and with PAHs, no significant mortality was recorded for any treatment. Nevertheless, malformation rate increased significantly in embryos exposed to the highest concentrations (5 or 10 mg/L) of GO and reduced GO (rGO) alone and with sorbed B(a)P (GO-B(a)P). On the other hand, adults were exposed for 21 days to 2 mg/L of GO, GO-B(a)P and GO co-exposed with WAF (GO + WAF) and to 100 µg/L B(a)P. Fish exposed to GO presented GO in the intestine lumen and liver vacuolisation. Transcription level of genes related to cell cycle regulation and oxidative stress was not altered, but the slight up-regulation of cyp1a measured in fish exposed to B(a)P for 3 days resulted in a significantly increased EROD activity. Fish exposed to GO-B(a)P and to B(a)P for 3 days and to GO + WAF for 21 days showed significantly higher catalase activity in the gills than control fish. Significantly lower acetylcholinesterase activity, indicating neurotoxic effects, was also observed in all fish treated for 21 days. Results demonstrated the capacity of GO to carry PAHs and to exert sublethal effects in zebrafish.
Assuntos
Grafite , Nanoestruturas , Hidrocarbonetos Policíclicos Aromáticos , Poluentes Químicos da Água , Animais , Grafite/toxicidade , Mar do Norte , Hidrocarbonetos Policíclicos Aromáticos/análise , Hidrocarbonetos Policíclicos Aromáticos/toxicidade , Poluentes Químicos da Água/toxicidade , Peixe-ZebraRESUMO
Polymer composite materials with hierarchical porous structure have been advancing in many different application fields due to excellent physico-chemical properties. However, their synthesis continues to be a highly energy-demanding and environmentally unfriendly process. This work reports a unique water based synthesis of monolithic 3D reduced graphene oxide (rGO) composite structures reinforced with poly(methyl methacrylate) polymer nanoparticles functionalized with epoxy functional groups. The method is based on reduction-induced self-assembly process performed at mild conditions. The textural properties and the surface chemistry of the monoliths were varied by changing the reaction conditions and quantity of added polymer to the structure. Moreover, the incorporation of the polymer into the structures improves the solvent resistance of the composites due to the formation of crosslinks between the polymer and the rGO. The monolithic composites were evaluated for selective capture of CO2. A balance between the specific surface area and the level of functionalization was found to be critical for obtaining high CO2 capacity and CO2/N2 selectivity. The polymer quantity affects the textural properties, thus lowering its amount the specific surface area and the amount of functional groups are higher. This affects positively the capacity for CO2 capture, thus, the maximum achieved was in the range 3.56-3.85 mmol/g at 1 atm and 25 °C.