Carbon black and chitin nanofibers for green tyres: Preparation and property evaluation.

This research highlights the synergistic use of carbon black (CB) and chitin nanofibers (CHNFs) for developing green tyres for the first time. The CHNFs (12-30 nm) were prepared from chitin powder with the help of steam explosion and mild oxalic acid hydrolysis. The CHNFs were uniformly dispersed in natural rubber (NR) latex, dried, and mixed with CB in a two-roll mill to form NR/CB/CHNF composites. The NR/CB/CHNF composite at 1 phr CHNF loading exhibited tensile and tear strengths that were about 47 and 160 % greater than the NR-Neat, respectively. The dynamic mechanical analysis showed that the loss tangent (tan δ) at 60 °C was 50 % lower for the NR/CB/CHNF 1.0 composite than for the NR/CB50 composite. The study succeeded in developing a new green tyre tread formulation that would be helpful for attaining sustainability and a circular economy.

Effect of oxalic acid and sulphuric acid hydrolysis on the preparation and properties of pineapple pomace derived cellulose nanofibers and nanopapers.

Nanocellulose is the "green magnet" which attracts a wide spectrum of industries towards it due to its availability, biodegradability, and possible smart applications. For the first time, pineapple pomace was being explored as an economic precursor for cellulose nanofibers. Nanofiber isolation was accomplished using a chemo-mechanical method and solution casting was adopted for the development of nanopapers. Moreover, the study examines the structural, optical, crystalline, dimensional, and thermal features of nanofibers isolated using different acid hydrolysis (oxalic acid and sulphuric acid) methods. Fourier-transform infra-red spectroscopy, 13C solid-state nuclear magnetic resonance spectroscopy, and X-ray diffraction analysis indicated the presence of type I cellulose. The transmittance, crystallinity index, and thermal stability of PPNFS (sulphuric acid treated fiber) were greater than PPNFO (oxalic acid treated fiber). The transmission electron microscopy and dynamic light scattering analysis confirmed the nanodimension of PPNFO and PPNFS. While comparing the optical and mechanical properties of nanopapers, PPNFS outperforms PPNFO. The tensile strength of the prepared nanopapers (64 MPa (PPNFO) and 68 MPa (PPNFS)) was found to be high compared to similar works reported in the literature. The prepared nanopaper is proposed to be used for food packaging applications.

Chlorine-free extraction and structural characterization of cellulose nanofibers from waste husk of millet (Pennisetum glaucum).

This study aims to extract cellulose nanofibers (CNFs) from a sustainable source, i.e. millet husk, which is an agro-waste worthy of consideration. Pre-treatments such as mercerisation, steam explosion, and peroxide bleaching (chlorine-free) were applied for the removal of non-cellulosic components. The bleached millet husk pulp was subjected to acid hydrolysis (5% oxalic acid) followed by homogenization to extract CNFs. The extracted CNFs were characterized using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Dynamic Light Scattering (DLS), Energy Dispersive X-ray Spectroscopy (EDX), Thermogravimetry (TG and DTG), Differential scanning calorimetry (DSC), and Solid state 13C nuclear magnetic resonance spectroscopy (solid state 13C NMR). The isolated CNFs show a typical cellulose type-I structure with a diameter of 10-12 nm and a crystallinity index of 58.5%. The appearance of the specific peak at 89.31 ppm in the solid state 13C NMR spectra validates the existence of the type-I cellulose phase in the prepared CNFs. The prepared CNFs had a maximum degradation temperature (Tmax) of 341 °C, that was 31 °C greater than raw millet husk (RMH). The outcome of the study implies that the nanofibers are prominent alternatives for synthetic fibers for assorted potential applications, especially in manufacturing green composites.

Thermoplastic starch nanocomposites using cellulose-rich Chrysopogon zizanioides nanofibers.

Green thermoplastic starch (TPS) nanocomposite films aided by cellulose nanofibers (CNFs) from Chrysopogon zizanioides roots were developed and characterized. When compared to other lignocellulosic fibers, Chrysopogon zizanioides roots revealed exceptionally high cellulose content (~48%). CNFs were separated using an environmentally friendly acid isolation technique that included three stages: (i) alkali treatment; (ii) bleaching; and (iii) mild acid hydrolysis using oxalic acid in an autoclave. Following that, green nanocomposite films were made from potato starch using the solution casting process, by which we used glycerol (30 wt%) to make thermoplastic starch. Then, cellulose nanofibers in different concentrations (0, 1, 2, 3, 4 wt%) were added to the thermoplastic starch matrix. The isolated CNFs had diameters in the range of 17-27 nm. Besides, these nanostructures presented a very high crystallinity index (~65%), thereby enhanced the thermal stability. TPS/CNF green nanocomposites containing 3 wt% CNFs had exceptional tensile strength (~161%), tensile modulus (~167%), thermal stability, and crystallinity. As a result, nanocomposite films made of starch and cellulose nanofibers (3 wt%) extracted from Chrysopogon zizanioides roots would be alternatives for sustainable packaging. It can be concluded that Chrysopogon zizanioides roots have high potential for polymer industry.

Cellulose Nanofibers Isolated from the Cuscuta Reflexa Plant as a Green Reinforcement of Natural Rubber.

In the present work, we used the steam explosion method for the isolation of cellulose nanofiber (CNF) from Cuscuta reflexa, a parasitic plant commonly seen in Kerala and we evaluated its reinforcing efficiency in natural rubber (NR). Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and Thermogravimetric analysis (TGA) techniques indicated that type I cellulose nanofibers, with diameter: 10-30 nm and a 67% crystallinity index were obtained by the proposed method. The results showed that application of CNF in NR based nanocomposites resulted in significant improvement of their processing and performance properties. It was observed that the tensile strength and tear strength of NR/CNF nanocomposites are found to be a maximum at 2 phr CNF loading, which corresponds with the studies of equilibrium swelling behavior. Dynamic mechanical analysis, thermogravimetric analysis, and morphological studies of tensile fractured samples also confirm that CNF isolated from Cuscuta reflexa plant can be considered as a promising green reinforcement for rubbers.