RESUMO
Consumption of acidic beverages and foods could provoke erosive damage, both for teeth and for restorative materials. Temperatures of consumption could influence the erosive effects of these products. The aim of this in vitro study is to assess the influence of an acidic challenge on the weight loss of different restorative materials. Resin composites and glass-ionomer cements (GIC) were tested. The medium of storage was Coca-Cola (Coca-Cola, Coca-Cola Company, Milano, Italy) at two different temperatures, 4 and 37 °C, respectively for Group A and Group B. For each group, nine specimens were prepared for each material tested. After 7 days, weight was assessed for each sample, and the percentage weight loss was calculated. For all the resin composites (Groups 1−13), no significant weight losses were noticed. (<1%). Conversely, GICs (Groups 14 and 15) showed significant weight loss during the acidic challenge, which was reduced in the case of these materials that included a protective layer applied above. Significant differences were registered with intra-group analysis; weight loss for specimens immersed in Coca Cola at 37 °C was significantly higher for almost all materials tested when compared to specimens exposed to a cooler medium. In conclusion, all the resin composites showed reliable behaviour when exposed to acidic erosion, whereas glass-ionomer cements generally tended to solubilize.
RESUMO
In the present study, we evaluated the influence of bovine enamel exposure to acidic drinks (Coca-Cola, Coca-Cola Company, Milano, Italy, pH = 2.37) on shear bond strength of three sealants (Fissurit; Grandio Seal and Admira Fusion-Voco Gmbh, Cuxhaven, Germany). For each sealant, two adhesive techniques were tested to investigate the impact of the adhesive application on shear bond strength of sealants after immersion in acidic drink and in the control: Group 1-Control: enamel surface was not in contact with acid drinks, acid etching application and self-adhesive technique for fissure sealant; Group 2-enamel surface was not in contact with acid drinks, acid etching, and adhesive applications, an etch-and-rinse technique for fissure sealant; Group 3-enamel surface was immersed in acid drink, acid etching application and self-adhesive technique for fissure sealant; Group 4-enamel surface was immersed in acid drink, acid etching, and adhesive applications, an etch-and-rinse technique for fissure sealant. For each specimen, the sealant composite resin was applied to the enamel surface and tested with a universal testing machine. Shear bond strength was measured in MPa and with an optical microscope to determine failure modes, quantified with adhesive remnant index (ARI). Enamel acidification variably influenced bond strength values of the different sealants. When no enamel pretreatment was applied, no significant differences were found among the sealants (p > 0.05). However, the mere application of acid etching without adhesive procedures resulted in lower bond strength (p < 0.001). The acid pretreatment affected significantly the bond strength of all sealants tested (p < 0.001), but no significant differences were recorded between the subgroups.
RESUMO
The aim of the present study was to evaluate and compare the cytotoxic effects of eight composite resins on immortalized human gingival fibroblasts. Composite resins were eluted in cell culture medium for 48 or 72 h at 37 °C. Immortalized human gingival fibroblast-1 (HGF-1) cell lines were seeded in 96-well (1 × 104) plates and incubated for 24 h at 37 °C with the obtained extraction medium. The percentage of viable cells in each well (MTT test) was calculated relative to control cells, which were set to 100%. Data observed were not normally distributed, and nonparametric statistical methods were used for statistical analysis. The Wilcoxon test was used for intragroup comparison, and the Kruskal-Wallis test was used for intergroup multiple comparisons. Significance value was set as p < 0.05. All materials tested showed cytotoxic effects on gingival fibroblasts, recordable as noncytotoxic, mildly cytotoxic or severely cytotoxic, depending on the percentage of cell viability. The Wilcoxon test for intragroup comparison showed that the percentage of viable cells decreased significantly for extracts, for all composite resins tested. The composite resins contained monomers that displayed cytotoxic properties. BisGMA, TEGDMA and UDMA had inhibitory effects and induced apoptotic proteins in pulp fibroblast. Composite resins that contained lower percentages of unbound free monomers-and that released less ions-possessed superior biocompatibility in vitro.
RESUMO
BACKGROUND: The aim of this study was to evaluate and compare the surface roughness of six esthetic restorative materials (Gradia Direct Anterior, GC Corporation, Tokyo, Japan; Filtek Supreme XTE, 3M ESPE, St. Paul, MN, USA; Ceram.X Universal, Dentsply DeTrey, Konstanz, Germany; Essentia enamel, GC Corporation, Tokyo, Japan; Admira Fusion, Voco, Cuxhaven, Germany; and Estelite, Tokuyama Dental corporation, Taitou-ku, Tokyo, Japan) achieved using three different finishing and polishing techniques. MATERIALS AND METHODS: In this in vitro study Forty specimens of each material (6 mm in diameter, 2 mm high) were created and divided into four groups, one per each finishing and polishing procedure and a control group, only cured and not polished. All specimen preparation and finishing and polishing procedures were performed by the same investigator, to reduce variability, following strictly the manufacturer's instructions. Specimens were analyzed using a profilometer to measure the mean surface roughness (Ra, µm), and microscopy images were taken during the measurements through the microscope of the profilometer. Two-way ANOVA test was applied to determine significant differences with respect to material, finishing/polishing technique, and interaction between both variables. Post hoc comparison was done using Tukey's honestly significant difference test. Significance for statistical tests was predetermined at P < 0.05. RESULTS: Finishing and polishing procedure using tungsten carbide burs provided the best values in terms of surface roughness. All materials of this study treated with this method have provided superimposable values, and no material can be considered more performing than the others. Similar values were also found in the control group. CONCLUSION: This study demonstrated that the finishing technique with carbide burs produced an excellent surface smoothness, even if the best surface smoothness is achieved curing the restorative material under a polyester matrix.
RESUMO
BACKGROUND: Acidic beverages, such as soft drinks (orange juice and cola), can produce erosion of resin composites. The aim of this in vitro study was to evaluate the effect of immersion in acidic drink on the Vickers microhardness (VK) of different esthetic restorative materials (one nanohybrid Ormocer-based composite, one nanoceramic composite, one nanofilled composite, and one microfilled hybrid composite). MATERIALS AND METHODS: In this in vitro study, thirty specimens of each esthetic restorative material were divided into three subgroups (n = 10): specimens of group 1 were used as control, specimens of group 2 were immersed in 50 ml of acidic drink for 1 day, specimens of group 3 were immersed in 50 ml of acidic drink for 7 days. Data were analyzed by Shapiro-Wilk test to assess the normality of the distributions followed by nonparametric Kruskal-Wallis analysis of variance and Mann-Whitney U-test comparison test among groups. A significant level of α = 0.05 was set for comparison between the groups. RESULTS: Mann-Whitney U-test showed that each material showed lower microhardness values after immersion in acidic solution (P < 0.05). Paired t-test confirmed that microhardness for each composite did not change after immersion in distilled water (Control group) (P > 0.05). Significant changes were registered for all restorative materials after immersion in acidic solution for 1 day and 7 days (P < 0.05). CONCLUSION: The Filtek Supreme XTE, a nanofilled composite, and Admira Fusion, a nanohybrid ormocer-based composite, showed the best behavior. The Ceram X Universal (nanoceramic composite) although reached lower hardness values than the previous materials, but resisted well to the 1 week immersion in soft-drink. Finally, the Gradia Direct achieved the most disappointing results: Low microhardness values are justified by the nature of its filling (microfilled hybrid composite).
RESUMO
BACKGROUND: The aim of this study was to evaluate the influence of dentin pretreatment with NaOCl on shear bond strength of four one-step self-etch adhesives with different pH values. MATERIAL AND METHODS: Bovine permanent incisors were used. Four one-step self-etch adhesives were tested: Adper™ Easy Bond, Futurabond NR, G-aenial Bond, Clearfil S3 Bond. One two-step self-etch adhesive (Clearfil SE Bond) was used as control. Group 1- no pretreatment; group 2- pretratment with 5,25 % NaOCl; group 3- pretreatment with 37 % H3PO4 etching and 5,25 % NaOCl. A hybrid composite resin was inserted into the dentin surface. The specimens were tested in a universal testing machine. The examiners evaluated the fractured surfaces in optical microscope to determine failure modes, quantified with adhesive remnant index (ARI). RESULTS: Dentin pretreatment variably influenced bond strength values of the different adhesive systems. When no dentin pretreatment was applied, no significant differences were found (P >.05) among four adhesives tested. No significant differences were recorded when comparing NaOCl pretreatment with H3PO4 + NaOCl pretreatment for all adhesive tested (P >.05) except Clearfil S3 Bond that showed higher shear bond strength values when H3PO4 was applied. Frequencies of ARI scores were calculated. CONCLUSIONS: The influence of dentin pretreatment with NaOCl depends on the composition of each adhesive system used. There was no difference in bond strength values among self-etch adhesives with different pH values. Key words:Dentin, pretreatment, self-etch adhesives.
RESUMO
OBJECTIVE: To evaluate the color stability of different esthetic restorative materials after surface finishing/polishing with different procedures. MATERIALS AND METHODS: All materials were polymerized into silicone rubber rings to obtain specimens identical in size. Samples were randomly assigned into four groups (10 specimens of each composite for each group), and they were finished with different procedures: Control group (Group 1), three or two polishers interspersed with diamond grit (Groups 3 and 2, respectively), and one tungsten carbide bur + one polisher interspersed with diamond grit (Group 4). After staining process in coffee, a colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, and 28 days. Shapiro-Wilk test and Kruskal-Wallis analysis of variance were applied to assess significant differences among restorative materials. Means of the different polishing/finishing groups were compared with Scheffe's multiple comparison test at the 0.05 level of significance. RESULTS: In control group, significant lower discolorations were recorded for Essentia, Admira Fusion, and Estelite. After finishing, Filtek Supreme XTE and Ceram.X Universal showed a significantly lower degree of staining. The finishing technique used for Group 4 produced higher color changes. CONCLUSIONS: Tungsten carbide burs produced the higher color variations; after finishing, the nanofilled composites showed lower discoloration than nanohybrid ones, and the time of exposure to the staining agent and the polishing/finishing technique influenced the color change.
RESUMO
OBJECTIVES: This study compared the amount of apically extruded bacteria during the glide-path preparation by using multi-file and single-file glide-path establishing nickel-titanium (NiTi) rotary systems. MATERIALS AND METHODS: Sixty mandibular first molar teeth were used to prepare the test apparatus. They were decoronated, blocked into glass vials, sterilized in ethylene oxide gas, infected with a pure culture of Enterococcus faecalis, randomly assigned to 5 experimental groups, and then prepared using manual stainless-steel files (group KF) and glide-path establishing NiTi rotary files (group PF with PathFiles, group GF with G-Files, group PG with ProGlider, and group OG with One G). At the end of canal preparation, 0.01 mL NaCl solution was taken from the experimental vials. The suspension was plated on brain heart infusion agar and colonies of bacteria were counted, and the results were given as number of colony-forming units (CFU). RESULTS: The manual instrumentation technique tested in group KF extruded the highest number of bacteria compared to the other 4 groups (p < 0.05). The 4 groups using rotary glide-path establishing instruments extruded similar amounts of bacteria. CONCLUSIONS: All glide-path establishment instrument systems tested caused a measurable apical extrusion of bacteria. The manual glide-path preparation showed the highest number of bacteria extruded compared to the other NiTi glide-path establishing instruments.
RESUMO
BACKGROUND: The aim of the present in vitro study was to evaluate the protective effects of a zinc-hydroxyapatite toothpaste on repairing enamel erosion produced by a soft drink (Coca-Cola) compared to toothpastes with and without fluoride using Scanning Electron Microscopy (SEM). MATERIAL AND METHODS: Fifty specimens were assigned to 5 groups of 10 specimens each. (Group 1: no erosive challenge, no toothpaste treatment, group 2: erosive challenge, no toothpaste treatment, 3: erosive challenge, toothpaste without fluoride, group 4: erosive challenge, fluoride toothpaste treatment, group 5: erosive challenge, zinc-hydroxyapatite toothpaste treatment). Repeated erosive challenges were provided by immersing bovine enamel specimens (10 per group) in a soft drink for 2 min (6mL, room temperature) at 0, 8, 24 and 32 h. After each erosive challenge, the toothpastes were applied neat onto the surface of specimens for 3 min without brushing and removed with distilled water. Between treatments the specimens were kept in artificial saliva. The surface of each specimen was imaged by SEM. RESULTS: Statistically significant differences were found between the samples used as control and those immersed in Coca-Cola (group 1 and 2): indeed among all groups the highest grade of damage was found in group 2. Instead the lowest grade was recorded in the samples of group 5 (Zinc hydroxyapatite toothpaste). CONCLUSIONS: The results of this study confirmed the potential benefit the Zn-HAP technology could provide in protecting enamel from erosive acid challenges. The treatment of erosively challenged enamel with Zn-Hap toothpaste showed a clear protective effect. Key words:Dental erosion, enamel, SEM, toothpaste.
RESUMO
OBJECTIVE: A crucial property of esthetic restorative materials is their long-term color stability. The aim of this in vitro study was to evaluate the color stability of esthetic restorative materials (one microfilled flowable composite, one nanofilled composite, one nanoybrid composite, one microfilled composite, and one nanoybrid ormocer-based composite) after surface roughening with cola and exposure to different staining solutions (coffee and red wine). MATERIALS AND METHODS: All materials were polymerized into silicone rubber rings (2 mm × 6 mm × 8 mm) to obtain 150 specimens identical in size. Seventy-five specimens of Group A were first exposed to cola for 24 h, and then samples were immersed in coffee or red wine over a 28-day test period. A colorimetric evaluation, according to the CIE L*a*b* system, was performed at 7, 14, 21, 28 days. Shapiro-Wilk test and Kruskal-Wallis analysis of variance were applied to assess significant differences among restorative materials. Means were compared with Scheffe's multiple comparison test at the 0.05 level of significance. RESULTS: Specimens of Group A showed higher variations when compared with Group B's specimens (P < 0.05). After 28 days, the immersion protocols caused a clinically perceivable color change for all materials tested (P < 0.05). CeramX Universal and Admira Fusion showed the lowest ΔE variations (P < 0.05). CONCLUSIONS: Staining beverages caused significant discolorations for all the materials tested. The first exposure to cola enhanced the subsequent staining with coffee or red wine. Nanohybrid composites reported the lowest color variations.
RESUMO
AIM: The aim of the present study was to evaluate radiographically the technical quality of root canal filling performed by postgraduate students with a new single-file Nickel-Titanium System (F6 Skytaper Komet) in clinical practice. METHODS: Records of 74 patients who had received endodontic treatment by postgraduate students at the School of Dentistry, Faculty of Medicine, University of Pavia in the period between September 2015 and April 2016 were collected and examined: the final sample consisted 114 teeth and 204 root canals. The quality of endodontic treatment was evaluated by examining the length of the filling in relation to the radiographic apex, the density of the obturation according to the presence of voids and the taper of root canal filling. Chi-squared analysis was used to determine statistically significant differences between the technical quality of root fillings according to tooth's type, position and curvature. RESULTS: The results showed that 75,49%, 82,84% and 90,69% of root filled canals had adequate length, density and taper respectively. CONCLUSIONS: Overall, the technical quality of root canal fillings performed by postgraduates students was acceptable in 60,78% of the cases.
RESUMO
The aim of this in vitro study was to evaluate and compare the color stability of different esthetic restorative materials (one microfilled composite, one nanofilled composite, one nanoceramic composite, one microfilled hybrid composite, one microfilled hybrid composite, one nanohybrid Ormocer based composite and one supra-nano spherical hybrid composite) after exposure to different staining solutions (physiological saline, red wine, coffee). All materials were prepared and polymerized into silicon rings (2 mm × 6 mm × 8 mm) to obtain specimens identical in size. Thirty cylindrical specimens of each material were prepared. Specimens were immersed in staining solutions (physiological saline, coffee and red wine) over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. The Shapiro-Wilk test and ANOVA were applied to assess significant differences among restorative materials. A paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. All restorative materials showed significant color differences after immersion in coffee. Coffee caused a significant color change in all types of tested composite resins. Only Filtek Supreme XTE demonstrated a staining susceptibility to red wine; no other significant differences among the materials were demonstrated. Long-term exposure to some food dyes (coffee in particular) can significantly affect the color stability of modern esthetic restorative materials regardless of materials' different compositions.
RESUMO
Objective: The purpose of the present study was to compare bond strength of different universal adhesives under three different testing conditions: when no pretreatment was applied, after 37% phosphoric acid etching and after glycine application. Materials and methods: One hundred and fifty bovine permanent mandibular incisors were used as a substitute for human teeth. Five different universal adhesives were tested: Futurabond M+, Scotchbond Universal, Clearfil Universal Bond, G-Premio BOND, Peak Universal Bond. The adhesive systems were applied following each manufacturer's instructions. The teeth were randomly assigned to three different dentin surface pretreatments: no pretreatment agent (control), 37% phosphoric acid etching, glycine pretreatment. The specimens were placed in a universal testing machine in order to measure and compare bond strength values. Results: The Kruskal-Wallis analysis of variance and the Mann-Whitney test were applied to assess significant differences among the groups. Dentin pretreatments provided different bond strength values for the adhesives tested, while similar values were registered in groups without dentin pretreatment. Conclusions: In the present report, dentin surface pretreatment did not provide significant differences in shear bond strength values of almost all groups. Acid pretreatment lowered bond strength values of Futurabond and Peak Universal Adhesives, whereas glycine pretreatment increased bond strength values of G Praemio Bond adhesive system.
RESUMO
BACKGROUND: The objective of this in vitro study was to evaluate the over time color stability of one resin infiltrant (Icon) upon exposure to staining solutions (coffee and wine) compared with one nano-hybrid sealant (Grandio Seal), one transparent fissure sealant with fluoride (Control Seal) and one nanofilled composite (Filtek Supreme XTE). MATERIAL AND METHODS: All materials were polymerized according to manufacturers' instructions into silicon rings (height 1 mm; internal diameter 6 mm; external diameter 8 mm) to obtain specimens identical in size. The specimens were immersed in staining solutions at room temperature over a 28-day test period. The control samples have not been subjected to the staining process. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. Shapiro Wilk test and Kruskal Wallis ANOVA were applied to assess significant differences among different materials. Means were compared with Scheffe's multiple-comparison test at the 0.05 level of significance. RESULTS: In the case of all materials, immersion in solutions resulted in clinically perceivable color changes after 1 week (∆E < 3.3). Lowest CIE L* variation was registered for Control Seal and Grandio Seal both after 1 week and after 1 month, while Icon showed significantly higher variation (P < 0.05). Color coordinate CIE a* varied significantly more for Icon samples (P > 0.05). Color coordinate CIE b* varied similarly for all materials tested (P > 0.05). CONCLUSIONS: Immersion in coffee or red wine resulted in clinically perceivable color changes for all materials tested. Icon showed the highest color variations both after 1 week and 1 month. Icon can fix the initial esthetic problem associated with white spot lesions, but the resin may become more discolored than other materials over time. Key words:CIE Lab, color stability, resin infiltrant.
RESUMO
BACKGROUND: The aim of this study was to evaluate the ability to identify the contiguity between the root of the mandibular third molar and the mandibular canal (MC) in panoramic radiographs compared with Cone Beam-CT. MATERIAL AND METHODS: Panoramic radiographs of 326 third molars and CBCT radiographs of 86 cases indicated for surgery and considered at risk were evaluated. The following signs were assessed in panoramic radiographs as risk factors: radiolucent band, loss of MC border, change in MC direction, MC narrowing, root narrowing, root deviation, bifid apex, superimposition, and contact between the root third molar and the MC. RESULTS: Radiographic signs associated with absence of MC cortical bone are: radiolucent band, loss of MC border, change in MC direction, and superimposition. The number of risk factors was significantly increased with an increasing depth of inclusion. CBCT revealed a significant association between the absence of MC cortical bone and a lingual or interradicular position of the MC. CONCLUSIONS: In cases in which panoramic radiographs do not exclude contiguity between the MC and tooth, careful assessment the signs and risks on CBCT radiographs is indicated for proper identification of the relationships between anatomic structures. Key words:Panoramic radiography, Cone-Beam computed tomography, third molar, mandibular nerve.
RESUMO
BACKGROUND: The aim of this in vitro study was to evaluate the color stability of CAD/CAM Zirconia ceramics following exposure to acidic drink (Coca Cola) and after exposure to staining solution (coffee). MATERIAL AND METHODS: All the samples were immersed in different staining solutions over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. Shapiro Wilk test and Kruskal-Wallis ANOVA were applied to assess significant differences among restorative materials. Paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. RESULTS: One week immersion in acidic drink did not cause a perceivable discoloration for all restorative materials (ΔE < 3.3). Subsequent immersion in coffee affected color stability of all Zirconia samples, even if Kruskal-Wallis ANOVA found significant differences among the various restorative materials. CONCLUSIONS: The ∆Es of CAD/CAM Zirconia ceramics after immersion in coffee varied among the products, but color integrity is not affected by contact with acidic drinks. Key words:CAD/CAM restorative materials, CIE Lab, Zirconia ceramics.
RESUMO
This study assessed the antimicrobial efficacy and surface tension of established irrigating solutions with a new experimental chelating solution in infected dentin tubes. Twenty-five specimens were randomly assigned to each of the irrigating solutions. Twenty specimens were used as negative and positive controls. After 21 days of contamination with E. faecalis, the irrigating solutions MTAD, QMiX and Tetraclean NA were delivered into each infected root canal. The solutions were removed and dentin samples were withdrawn from the root canals with sterile low-speed round burs with increasing ISO diameters. The dentin powder samples obtained with each bur were immediately collected in separate test tubes containing 3 mL of BHI broth. After that, 100 µL from each test tube was cultured on blood agar. The grown colonies were counted and recorded as colony-forming units (CFU). The surface tension of the irrigants was measured using a Cahn DCA-322 Dynamic Contact Angle Analyzer. A Kruskal Wallis nonparametric ANOVA and a Friedman test were used (p<0.05). Tetraclean NA showed lower surface tension and CFU values than MTAD and QMiX. Better antibacterial action and low surface tension were observed for Tetraclean NA, probably due to the improved penetration into the root canal and dentinal tubes.
Assuntos
Anti-Infecciosos/farmacologia , Quelantes/química , Tensão Superficial , Tensoativos/química , Animais , Bovinos , Enterobacter/efeitos dos fármacos , Irrigantes do Canal RadicularRESUMO
This study evaluated the root canal dentine surface by scanning electron microscope (SEM) after shaping with two reciprocating single-file NiTi systems and two rotating single-file NiTi systems, in order to verify the presence/absence of the smear layer and the presence/absence of open tubules along the walls of each sample; Forty-eight single-rooted teeth were divided into four groups and shaped with OneShape (OS), F6 SkyTaper (F6), WaveOne (WO) and Reciproc and irrigated using 5.25% NaOCl and 17% EDTA. Root canal walls were analyzed by SEM at a standard magnification of 2500×. The presence/absence of the smear layer and the presence/absence of open tubules at the coronal, middle, and apical third of each canal were estimated using a five-step scale for scores. Numeric data were analyzed using Kruskal-Wallis and Mann-Whitney U statistical tests and significance was predetermined at P < 0.05; The Kruskal-Wallis ANOVA for debris score showed significant differences among the NiTi systems (P < 0.05). The Mann-Whitney test confirmed that reciprocating systems presented significantly higher score values than rotating files. The same results were assessed considering the smear layer scores. ANOVA confirmed that the apical third of the canal maintained a higher quantity of debris and smear layer after preparation of all the samples; Single-use NiTi systems used in continuous rotation appeared to be more effective than reciprocating instruments in leaving clean walls. The reciprocating systems produced more debris and smear layer than rotating instruments.
RESUMO
Abstract This study assessed the antimicrobial efficacy and surface tension of established irrigating solutions with a new experimental chelating solution in infected dentin tubes. Twenty-five specimens were randomly assigned to each of the irrigating solutions. Twenty specimens were used as negative and positive controls. After 21 days of contamination with E. faecalis, the irrigating solutions MTAD, QMiX and Tetraclean NA were delivered into each infected root canal. The solutions were removed and dentin samples were withdrawn from the root canals with sterile low-speed round burs with increasing ISO diameters. The dentin powder samples obtained with each bur were immediately collected in separate test tubes containing 3 mL of BHI broth. After that, 100 μL from each test tube was cultured on blood agar. The grown colonies were counted and recorded as colony-forming units (CFU). The surface tension of the irrigants was measured using a Cahn DCA-322 Dynamic Contact Angle Analyzer. A Kruskal Wallis nonparametric ANOVA and a Friedman test were used (p<0.05). Tetraclean NA showed lower surface tension and CFU values than MTAD and QMiX. Better antibacterial action and low surface tension were observed for Tetraclean NA, probably due to the improved penetration into the root canal and dentinal tubes
Resumo Este estudo avaliou a eficácia antimicrobiana e tensão superficial de soluções irrigadoras e uma nova solução quelante em tubos de dentina infectada. Vinte e cinco espécimes foram aleatoriamente distribuídos conforme as soluções irrigantes. Decorrifdos 21 dias de contaminação com E. faecalis, a soluções de irrigação MTAD, QMiX e Tetraclean NA foram distribuídas em cada canal radicular infectado. As soluções foram removidas e as amostras de dentina foram retiradas dos canais radiculares com brocas esféricas de baixa velocidade com diâmetros ISO sucessivamente maiores. As amostras do pó de dentina obtidas com cada broca foram imediatamente colocadas em tubos de ensaio separados contendo 3 mL de caldo BHI. A seguir, 100 μL de cada amostra do tubo de teste foi cultivada em agar de sangue. As colônias crescidas foram contadas e registadas como unidades formadoras de colônias (UFC). A tensão superficial das soluções irrigantes foi medida utilizando o método de Wilhelmy. A análise não paramétrica de Kruskal-Wallis e o teste de Friedman foram utilizados (p<0,05). Tetraclean NA apresentou menor tensão de superfície e menores valores de UFC do que MTAD e QMiX. A melhor ação antibacteriana e baixa tensão superficial foram observadas para Tetraclean NA, provavelmente devido à melhor penetração no canal radicular e túbulos dentinários.
Assuntos
Animais , Bovinos , Anti-Infecciosos/farmacologia , Quelantes/química , Tensão Superficial , Tensoativos/química , Enterobacter/efeitos dos fármacos , Irrigantes do Canal RadicularRESUMO
BACKGROUND: The long-term capability of resin sealants and glass ionomer cements to release fluoride is associated to a reduction in pit and fissure caries. The regular use of fluoride varnishes/toothpastes can result in the absorption of fluoride into the sealant. The objective of the present study was to assess the fluoride release/uptake capacities of different fissure sealants. MATERIAL AND METHODS: Three different fissure sealants (Fuji Triage/GC, Fissurit FX/Voco and Grandio Seal/Voco) were examined. Ten discs of each material were prepared. Each disc was incubated with distilled water and then the solution analyzed for diluted for fluoride concentration, using a combination of fluoride electrode (OrionGP 1 S/N 13824, Orion Research Inc, Boston, MA, USA) connected to an expandable ion analyzer (Orion 720A, Orion Research Inc, Boston, MA, USA). Standard curves between 1 and 100 ppm F- were used to calibrate the electrode. Cumulative fluoride release was measured on days 1, 2, 3, 5, 7, 21, 35 and 49, then two different fluoride varnishes/pastes (Profluorid Varnish/Voco, MI Paste Plus/GC), were applied to the sealants tested, and fluoride release (after reuptake) was measured on days 56, 70 and 84. RESULTS: Kruskal Wallis test confirmed significant differences in fluoride release between Fuji Triage/GC and Fissurit FX/Voco and Grandio Seal/Voco from day 1 (P < 0.001). The application of fluoride varnish Profluorid Varnish enhanced the fluoride release for all sealants (P < 0.05). MI Paste Plus enhanced the fluoride release for all sealants except for Fuji Triage/GC (P > 0.05). CONCLUSIONS: The GIC-based sealant (Fuji Triage/GC) released significantly more fluoride than the resin sealants tested. The exposure to the fluoridated varnish (Profluorid Varnish) significantly recharged the sealants tested more than the CPP-ACPF toothpaste (MI Paste Plus). KEY WORDS: Fissure sealants, fluoride release, fluoride uptake, glass ionomer cements.