RESUMO
The catalytic conversion of CO2 into valuable commodities has the potential to balance ongoing energy and environmental issues. To this end, the reverse water-gas shift (RWGS) reaction is a key process that converts CO2 into CO for various industrial processes. However, the competitive CO2 methanation reaction severely limits the CO production yield; therefore, a highly CO-selective catalyst is needed. To address this issue, we have developed a bimetallic nanocatalyst comprising Pd nanoparticles on the cobalt oxide support (denoted as CoPd) via a wet chemical reduction method. Furthermore, the as-prepared CoPd nanocatalyst was exposed to sub-millisecond laser irradiation with per-pulse energies of 1 mJ (denoted as CoPd-1) and 10 mJ (denoted as CoPd-10) for a fixed duration of 10 s to optimize the catalytic activity and selectivity. For the optimum case, the CoPd-10 nanocatalyst exhibited the highest CO production yield of â¼1667 µmol g-1catalyst, with a CO selectivity of â¼88% at a temperature of 573 K, which is a 41% improvement over pristine CoPd (~976 µmol g-1catalyst). The in-depth analysis of structural characterizations along with gas chromatography (GC) and electrochemical analysis suggested that such a high catalytic activity and selectivity of the CoPd-10 nanocatalyst originated from the sub-millisecond laser-irradiation-assisted facile surface restructure of cobalt oxide supported Pd nanoparticles, where atomic CoOx species were observed in the defect sites of the Pd nanoparticles. Such an atomic manipulation led to the formation of heteroatomic reaction sites, where atomic CoOx species and adjacent Pd domains, respectively, promoted the CO2 activation and H2 splitting steps. In addition, the cobalt oxide support helped to donate electrons to Pd, thereby enhancing its ability of H2 splitting. These results provide a strong foundation to use sub-millisecond laser irradiation for catalytic applications.
RESUMO
An effective approach for increasing the Noble metal-utilization by decorating the atomic Pt clusters (1 wt.%) on the CoO2@SnPd2 nanoparticle (denoted as CSPP) for oxygen reduction reaction (ORR) is demonstrated in this study. For the optimum case when the impregnation temperature for Co-crystal growth is 50 °C (denoted as CSPP-50), the CoPt nanoalloys and Pt-clusters decoration with multiple metal-to-metal oxide interfaces are formed. Such a nanocatalyst (NC) outperforms the commercial Johnson Matthey-Pt/C (J.M.-Pt/C; 20 wt.% Pt) catalyst by 78-folds with an outstanding mass activity (MA) of 4330 mA mgPt-1 at 0.85 V vs. RHE in an alkaline medium (0.1 M KOH). The results of physical structure inspections along with electrochemical analysis suggest that such a remarkable ORR performance is dominated by the potential synergism between the surface anchored Pt-clusters, CoPt-nanoalloys, and adjacent SnPd2 domain, where Pt-clusters offer ideal adsorption energy for O2 splitting and CoPt-nanoalloys along with SnPd2 domain boost the subsequent desorption of hydroxide ions (OH-).