RESUMO
Soluble and transparent wholly aromatic polyamides (PAs) were synthesized from an unsymmetrical diamine monomer having trifluoromethyl (CF3) groups, 4-(4'-aminophenoxy)-3,5-bis(trifluoromethyl)aniline. The monomer was polymerized with several dicarboxylic acid monomers via the Yamazaki-Higashi polycondensation method. All of the synthesized polyamides have an amorphous morphology, and they are soluble in many polar organic solvents at room temperature. Flexible and transparent films of the polyamides were prepared by solution casting and these polymer films show good optical transparencies with cut-off wavelengths of 337-367 nm and transparencies of 88%-90% at 550 nm. In addition, all the polymers were thermally stable over 400 °C and exhibited glass transition temperatures (Tg) higher than 300 °C. Unsymmetrically inserted trifluoromethyl groups on polyamides improves the solubility as well as the transparency of the polymers while maintaining good thermal properties. They also showed low refractive indices around 1.5333~1.5833 at 633 nm owing to the existence of low polarizable trifluoromethyl groups.
RESUMO
A series of soluble aromatic poly(amide-imide)s (PAIs) was prepared from a new diamide-diamine monomer having biphenyl units with two CF3 groups. The diamide-diamine monomer was polymerized with 2,2'-bis(trifluoromethyl)benzidine and pyromelltic dianhydride through an imidization reaction to prepare PAIs with a controlled imide/amide bond ratio in the main chains. While the PAIs with the highest imide bond content showed a limited solubility, other PAIs were soluble in polar organic solvents and can be solution-cast into flexible freestanding films. All PAIs exhibited high thermal stability with 5% weight loss temperature (Td5) from 464 to 497 °C in air, and no appearance of glass transition up to 400 °C. Notably, the linear coefficient of thermal expansion (CTE) value of the PAI films was linearly decreased with the imide bond content and varied from 44.8 to 7.8 ppm/°C.
RESUMO
The key component currently missing for the next generation of transparent and flexible displays is a high-performance polymer material that is flexible, while showing optical and thermal properties of glass. It must be transparent to visible light and show a low coefficient of thermal expansion (CTE). While specialty plastics such as aromatic polyimides are promising, reducing their CTE and improving transparency simultaneously proved challenging, with increasing coloration the main problem to be resolved. We report a new poly(amide-imide) material that is flexible and displays glass-like behavior with a CTE value of 4 parts per million/°C. This novel polymer was successfully used as a substrate to fabricate transparent and flexible indium-gallium-zinc oxide thin-film transistors.