The effect of alloying elements on the properties of pressed and non-pressed biodegradable Fe-Mn-Ag powder metallurgy alloys.

Current trends in the biodegradable scaffold industry call for powder metallurgy methods in which compression cannot be applied due to the nature of the scaffold template itself and the need to retain the shape of an underlying template throughout the fabrication process. Iron alloys have been shown to be good candidates for biomedical applications where load support is required. Fe-Mn alloys were researched extensively for this purpose. Current research shows that all metallurgical characterisation and corrosion test on Fe-Mn and Fe-Mn-Ag non pre-alloyed powder alloys are performed on alloys which are initially pressed into greens and subsequently sintered. In order to combine the cutting-edge field of biodegradable metallic alloys with scaffold production, metallurgical characterisation of pressed and non-pressed Fe, Fe-Mn and Fe-Mn-Ag sintered elemental powder compacts was carried out in this study. This was performed along with determination of the corrosion rate of the same alloys in in vitro mimicking solutions. These solutions were synthesised to mimic the osteo environment in which the final scaffolds are to be used. Both pressed and non-pressed alloys formed an austenite phase under the right sintering conditions. The corrosion rate of the non-pressed alloy was greater than that of its pressed counterpart. In a potentiodynamic testing scenario, addition of silver to the alloy formed a separate silver phase which galvanically increased the corrosion rate of the pressed alloy. This result wasn't replicated in the non-pressed alloys in which the corrosion rate was seen to remain similar to the non-silver-bearing alloy counterparts.

Assessment of corrosion resistance of cast cobalt- and nickel-chromium dental alloys in acidic environments.

BACKGROUND: The aim of this study was to compare the degradation resistance of nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloys used as a base material for partial dentures in contact with saliva. METHODS: Wiron® 99 and Wironit Extra-Hard® were selected as representative casting alloys for Ni-Cr and Co-Cr alloys, respectively. The alloys were tested in contact with deionized water, artificial saliva and acidified artificial saliva. Material characterization was performed by X-ray diffractometry (XRD) and microhardness and nanohardness testing. The corrosion properties of the materials were then analyzed using open circuit potential analysis and potentiodynamic analysis. Alloy leaching in solution was assessed by inductively coupled plasma mass spectrometry techniques. RESULTS: Co-Cr alloy was more stable than the Ni-Cr alloy in all solutions tested. Leaching of nickel and corrosion attack was higher in Ni-Cr alloy in artificial saliva compared with the acidified saliva. The corrosion resistance of the Co-Cr alloy was seen to be superior to that of the Ni-Cr alloy, with the former exhibiting a lower corrosion current in all test solutions. Microstructural topographical changes were observed for Ni-Cr alloy in contact with artificial saliva. The Ni-Cr alloy exhibited microstructural changes and lower corrosion resistance in artificial saliva. The acidic changes did not enhance the alloy degradation. CONCLUSIONS: Ni-Cr alloys are unstable in solution and leach nickel. Co-Cr alloys should be preferred for clinical use.

Influence of cold rolling on in vitro cytotoxicity and electrochemical behaviour of an Fe-Mn-C biodegradable alloy in physiological solutions.

The properties of cold-worked Fe-13Mn-1.2C steel, as candidate material for scaffolding and stenting applications, have been investigated. The study of the electrochemical corrosion susceptibility of Fe-13Mn-1.2C alloy in protein bearing and non-protein bearing physiological solutions, revealed that there were no differences between the as-received, 10% and 20% cold worked Fe-13Mn-1.2C samples. Although protein addition reduces the overall corrosion rate in static immersion degradation tests for both the cold worked and non-cold worked alloys, there were no discernible differences in the corrosion rates of samples with different percentages of cold work deformations. Similarly, potentiodynamic testing showed no differences between the corrosion rates in solutions with and without protein addition. Atomic absorption spectroscopy (AAS) results-post static immersion-showed similar values of Fe and Mn concentrations in the electrolyte for all the investigated conditions. Cold working was found to increase Grain Average Misorientation (GAM) and deformation twins within the steel, and, consequently, this led to an increase in the elastic modulus. Hence, cold-rolling may be used to achieve smaller sections (volumes) in order to support the equivalent load of the non-cold worked counterpart, giving a larger surface area to the volume ratio, thereby increasing the corrosion rate, and, in turn, rendering the degradation process shorter. When considering cytocompatibility in vitro, the collected supernatant particulate free Fe-13Mn-1.2C steel electrolytes were seen to be equally cytocompatible with no differences being observed between the different percentage cold work conditions. The presence of solid 80 µm size particles in the seeded elutions were seen to change the results and render the Fe-13Mn-1.2C steel non-cytocompatible.