Integrative Modeling and Experimental Insights into 3D and 4D Printing Technologies.

This review focuses on advancements in polymer science as it relates to three-dimensional (3D) and four-dimensional (4D) printing technologies, with a specific emphasis on applications in the biomedical field. While acknowledging the breadth of 3D and 4D printing applications, this paper concentrates on the use of polymers in creating biomedical devices and the challenges associated with their implementation. It explores integrative modeling and experimental insights driving innovations in these fields, focusing on sustainable manufacturing with biodegradable polymers, a comparative analysis of 3D and 4D printing techniques, and applications in biomedical devices. Additionally, the review examines the materials used in both 3D and 4D printing, offering a detailed comparison of their properties and applications. By highlighting the transformative potential of these technologies in various industrial and medical applications, the paper underscores the importance of continued research and development. The scope of this review also includes an overview of future research directions to address current challenges, enhance material capabilities, and explore practical applications.

Effect of bioceramic inclusions on gel-cast aliphatic polymer membranes for bone tissue engineering applications: An in vitro study.

BACKGROUND: Polylactic acid (PLA) has been extensively used in tissue engineering. However, poor mechanical properties and low cell affinity have limited its pertinence in load bearing bone tissue regeneration (BTR) devices. OBJECTIVE: Augmenting PLA with ß-Tricalcium Phosphate (ß-TCP), a calcium phosphate-based ceramic, could potentially improve its mechanical properties and enhance its osteogenic potential. METHODS: Gels of PLA and ß-TCP were prepared of different % w/w ratios through polymer dissolution in acetone, after which polymer-ceramic membranes were synthesized using the gel casting workflow and subjected to characterization. RESULTS: Gel-cast polymer-ceramic constructs were associated with significantly higher osteogenic capacity and calcium deposition in differentiated osteoblasts compared to pure polymer counterparts. Immunocytochemistry revealed cell spreading over the gel-cast membrane surfaces, characterized by trapezoidal morphology, distinct rounded nuclei, and well-aligned actin filaments. However, groups with higher ceramic loading expressed significantly higher levels of osteogenic markers relative to pure PLA membranes. Rule of mixtures and finite element models indicated an increase in theoretical mechanical strength with an increase in ß-TCP concentration. CONCLUSION: This study potentiates the use of PLA/ß-TCP composites in load bearing BTR applications and the ability to be used as customized patient-specific shape memory membranes in guided bone regeneration.

Influence of Trabecular Bone Presence on Osseodensification Instrumentation: An In Vivo Study in Sheep.

Osseodensification enhances the stability of endosteal implants. However, pre-clinical studies utilizing osseodensification instrumentation do not account for the limited presence of trabeculae seen clinically. This study aimed to evaluate the effect of osseodensification instrumentation on osteotomy healing in scenarios with and without the presence of trabecular bone. A ~10 cm incision was made over the hip of twelve sheep. Trabecular bone was surgically removed from twelve sites (one site/animal; negative control (Neg. Ctrl)) and left intact at twelve sites (one site/animal; experimental group (Exp.)). All osteotomies were created using the osseodensification drilling protocol. Each osteotomy received an endosteal implant and was evaluated after 3 or 12 weeks of healing (n = 6 animals/time). Histology revealed increased woven and lamellar bone surrounding the implants in the Exp. group relative to the Neg. Ctrl group. The Exp. group demonstrated the presence of bone fragments, which acted as nucleating sites, thereby enhancing the bone formation and remodeling processes. Bone-to-implant contact (%BIC) and bone area fractional occupancy (%BAFO) were significantly higher in the Exp. group relative to the Neg. Ctrl group both at 3 weeks (p = 0.009 and p = 0.043) and 12 weeks (p = 0.010 and p = 0.008). Osseodensification instrumentation in the presence of trabecular bone significantly improved osseointegration. However, no negative influences such as necrosis, inflammation, microfractures, or dehiscence were observed in the absence/limited presence of trabeculae.

Schizophrenia diagnosis based on diverse epoch size resting-state EEG using machine learning.

Schizophrenia is a severe mental disorder that impairs a person's mental, social, and emotional faculties gradually. Detection in the early stages with an accurate diagnosis is crucial to remedying the patients. This study proposed a new method to classify schizophrenia disease in the rest state based on neurologic signals achieved from the brain by electroencephalography (EEG). The datasets used consisted of 28 subjects, 14 for each group, which are schizophrenia and healthy control. The data was collected from the scalps with 19 EEG channels using a 250 Hz frequency. Due to the brain signal variation, we have decomposed the EEG signals into five sub-bands using a band-pass filter, ensuring the best signal clarity and eliminating artifacts. This work was performed with several scenarios: First, traditional techniques were applied. Secondly, augmented data (additive white Gaussian noise and stretched signals) were utilized. Additionally, we assessed Minimum Redundancy Maximum Relevance (MRMR) as the features reduction method. All these data scenarios are applied with three different window sizes (epochs): 1, 2, and 5 s, utilizing six algorithms to extract features: Fast Fourier Transform (FFT), Approximate Entropy (ApEn), Log Energy entropy (LogEn), Shannon Entropy (ShnEn), and kurtosis. The L2-normalization method was applied to the derived features, positively affecting the results. In terms of classification, we applied four algorithms: K-nearest neighbor (KNN), support vector machine (SVM), quadratic discriminant analysis (QDA), and ensemble classifier (EC). From all the scenarios, our evaluation showed that SVM had remarkable results in all evaluation metrics with LogEn features utilizing a 1-s window size, impacting the diagnosis of Schizophrenia disease. This indicates that an accurate diagnosis of schizophrenia can be achieved through the right features and classification model selection. Finally, we contrasted our results to recently published works using the same and a different dataset, where our method showed a notable improvement.

Three-Dimensional Bioprinting: A Comprehensive Review for Applications in Tissue Engineering and Regenerative Medicine.

Since three-dimensional (3D) bioprinting has emerged, it has continuously to evolved as a revolutionary technology in surgery, offering new paradigms for reconstructive and regenerative medical applications. This review highlights the integration of 3D printing, specifically bioprinting, across several surgical disciplines over the last five years. The methods employed encompass a review of recent literature focusing on innovations and applications of 3D-bioprinted tissues and/or organs. The findings reveal significant advances in the creation of complex, customized, multi-tissue constructs that mimic natural tissue characteristics, which are crucial for surgical interventions and patient-specific treatments. Despite the technological advances, the paper introduces and discusses several challenges that remain, such as the vascularization of bioprinted tissues, integration with the host tissue, and the long-term viability of bioprinted organs. The review concludes that while 3D bioprinting holds substantial promise for transforming surgical practices and enhancing patient outcomes, ongoing research, development, and a clear regulatory framework are essential to fully realize potential future clinical applications.

Surface Pre-Reacted Glass-Ionomer Eluate Suppresses Osteoclastogenesis through Downregulation of the MAPK Signaling Pathway.

Surface pre-reacted glass-ionomer (S-PRG) is a new bioactive filler utilized for the restoration of decayed teeth by its ability to release six bioactive ions that prevent the adhesion of dental plaque to the tooth surface. Since ionic liquids are reported to facilitate transepithelial penetration, we reasoned that S-PRG applied to root caries could impact the osteoclasts (OCs) in the proximal alveolar bone. Therefore, this study aimed to investigate the effect of S-PRG eluate solution on RANKL-induced OC-genesis and mineral dissolution in vitro. Using RAW264.7 cells as OC precursor cells (OPCs), TRAP staining and pit formation assays were conducted to monitor OC-genesis and mineral dissolution, respectively, while OC-genesis-associated gene expression was measured using quantitative real-time PCR (qPCR). Expression of NFATc1, a master regulator of OC differentiation, and the phosphorylation of MAPK signaling molecules were measured using Western blotting. S-PRG eluate dilutions at 1/200 and 1/400 showed no cytotoxicity to RAW264.7 cells but did significantly suppress both OC-genesis and mineral dissolution. The same concentrations of S-PRG eluate downregulated the RANKL-mediated induction of OCSTAMP and CATK mRNAs, as well as the expression of NFATc1 protein and the phosphorylation of ERK, JNK, and p38. These results demonstrate that S-PRG eluate can downregulate RANKL-induced OC-genesis and mineral dissolution, suggesting that its application to root caries might prevent alveolar bone resorption.

Calcium Sulfate Disks for Sustained-Release of Amoxicillin and Moxifloxacin for the Treatment of Osteomyelitis.

The purpose of this in vitro study was to develop calcium sulfate (CS)-based disks infused with an antimicrobial drug, which can be used as a post-surgical treatment modality for osteomyelitis. CS powder was embedded with 10% antibiotic, amoxicillin (AMX) or moxifloxacin (MFX), to form composite disks 11 mm in diameter that were tested for their degradation and antibiotic release profiles. For the disk degradation study portion, the single drug-loaded disks were placed in individual meshes, subsequently submerged in phosphate-buffered saline (PBS), and incubated at 37 °C. The disks were weighed once every seven days and analyzed via Fourier-transform infrared spectroscopy, X-ray diffraction, energy dispersive X-ray spectroscopy, and scanning electron microscopy. During the antibiotic release analysis, composite disks were placed in PBS solution, which was changed every 3 days, and analyzed for antibiotic activity and efficacy. The antibacterial effects of these sustained-release composites were tested by agar diffusion assay using Streptococcus mutans (S. mutans) UA 159 as an indicator strain. The degradation data showed significant increases in the degradation of all disks with the addition of antibiotics. Following PBS incubation, there were significant increases in the amount of phosphate and decreases in the amount of sulfate. The agar diffusion assay demonstrated that the released concentrations of the respective antibiotics from the disks were significantly higher than the minimum inhibitory concentration exhibited against S. mutans over a 2-3-week period. In conclusion, CS-antibiotic composite disks can potentially serve as a resorbable, osteoconductive, and antibacterial therapy in the treatment of bone defects and osteomyelitis.

Preclinical evaluation of mucogingival defect treatment using piscine membranes: An in vivo assessment of wound healing.

Periodontitis is a bacteria-induced chronic inflammatory disease characterized by degradation of the supporting tissue and bone in the oral cavity. Treatment modalities seek to facilitate periodontal rehabilitation while simultaneously preventing further gingival tissue recession and potentially bone atrophy. The aim of this study was to compare two differently sourced membranes, a resorbable piscine collagen membrane and a porcine-derived collagen membrane, in the repair of soft tissue defects utilizing a preclinical canine model. This in vivo component consisted of 10 beagles which were subjected to bilateral maxillary canine mucogingival flap defects, as well as bilateral soft tissue defects (or pouches) with no periodontal ligament damage in the mandibular canines. Defects received either a piscine-derived dermal membrane, (Kerecis® Oral, Ísafjörður, Iceland) or porcine-derived dermal membrane (Geistlich Mucograft®, Wolhusen, Switzerland) in a randomized fashion (to avoid site bias) and were allowed to heal for 30, 60, or 90 days. Statistical evaluation of tissue thickness was performed using general linear mixed model analysis of variance and least significant difference (LSD) post hoc analyses with fixed factors of time and membrane. Semi-quantitative analysis employed for inflammation assessment was evaluated using a chi-squared test along with a heteroscedastic t-test and values were reported as mean and corresponding 95% confidence intervals. In both the mucogingival flap defects and soft tissue gingival pouches, no appreciable qualitative differences were observed in tissue healing between the membranes. Furthermore, no statistical differences were observed in the thickness measurements between piscine- and porcine-derived membranes in the mucogingival flap defects (1.05 mm [±0.17] and 1.29 mm [±0.17], respectively [p = .06]) or soft tissue pouches (1.36 mm [±0.14] and 1.47 mm [±0.14], respectively [p = .27]), collapsed over time. Independent of membrane source (i.e., piscine or porcine), similar inflammatory responses were observed in both the maxilla and mandible at the three time points (p = .88 and p = .79, respectively). Histologic and histomorphometric evaluation results indicated that both membranes yielded equivalent tissue responses, remodeling dynamics and healing patterns for the mucogingival flap as well as the soft tissue gingival pouch defect models.

Effects on dentin nanomechanical properties, cell viability and dentin wettability of a novel plant-derived biomodification monomer.

OBJECTIVES: To evaluate the effects of dentin biomodification agents (Proanthocyanidin (PAC), Cardol (CD) and Cardol-methacrylate (CDMA) on dentin hydrophilicity by contact angle measurement, viability of dental pulp stem cells (DPSCs) and nanomechanical properties of the hybrid layer (HL). METHODS: CDMA monomer was synthesized from cardol through methacrylic acid esterification. Human extracted third molars were used for all experiments. For nanomechanical tests, specimens were divided in four groups according to the primer solutions (CD, CDMA, PAC and control) were applied before adhesive and composite coating. Nanomechanical properties of the HL were analyzed by nanoindentation test using a Berkovich probe in a nanoindenter. Wettability test was performed on dentin surfaces after 1 min biomodification and measured by contact angle analysis. Cytotoxicity was assessed by a MTT assay with DPSCs after 48 and 72 h. Data were analyzed with Student's t test or Two-way ANOVA and Tukey HSD test (p < 0.05). RESULTS: CD and CDMA solutions achieved greater hydrophobicity and increased the water-surface contact angles when compared to PAC and control groups (p < 0.05). PAC group showed a greater reduction of elastic modulus in nanoindentation experiments when compared to CD and CDMA groups (p < 0.05) after 4 months of aging. CD inhibited cell proliferation compared to all further materials (p < 0.05), whilst CDMA and PAC indicated no cell cytotoxicity to human DPSCs. SIGNIFICANCE: Cardol-methacrylate provided significantly higher hydrophobicity to dentin and demonstrated remarkable potential as collagen crosslinking, attaining the lowest decrease of HL's mechanical properties. Furthermore, such monomer did not affect pulp cytotoxicity, thereby highlighting promising feasibility for clinical applications.

Evaluation of Porcine-Derived Collagen Membranes for Soft Tissue Augmentation in the Oral Cavity: An In Vivo Study.

The use of porcine-derived collagen membranes (PDCM) to improve intraoral soft tissue rehabilitation remains under investigation. Different degrees of crosslinking have yielded differences in resorption time and inflammation surrounding collagen membranes. The aim of this study was to evaluate the in vivo performance of bilayered PDCMs with varying degrees of crosslinking for the regeneration of oral soft tissue defects. Bilateral split-thickness oral mucosa defects were created in mandibles of beagles (n=17) and assigned to one of the following: bilayer PDCM (high crosslinking porcine dermis in sheet form-H-xlink) and (low crosslinking porcine dermis in sheet form-L-xlink), bilayer PDCM (non-crosslinked predicate collagen membrane in spongy form-Ctrl), or negative control (Sham) and compared with positive control (unoperated). Animals were euthanized after 4-, 8-, or 12-weeks of healing to evaluate soft tissue regeneration and remodeling through histomorphometric analyses. H-xlink membranes presented delayed healing with a poorly developed epithelial layer (analogous to the sham group) across time points. Relative to Ctrl at 8 and 12 weeks, defects treated with H-xlink presented no difference in semiquantitative scores ( P > 0.05), while L-xlink exhibited greater healing ( P = 0.042, P = 0.043, at 8 and 12 weeks, respectively). Relative to positive control, L-xlink exhibited similar healing at 8 weeks and greater healing at 12 weeks ( P = 0.037) with a well-developed epithelial layer. Overall, groups treated with L-xlink presented with greater healing relative to the positive control after 12 weeks of healing and may serve as an alternative to autologous grafts for intraoral soft tissue regeneration.

Odontogenic Cutaneous Fistula: A Zombie Diagnosis.

BACKGROUND: Odontogenic cutaneous fistula (OCF) is a pathologic communication between the cutaneous surface of the face and oral cavity. Majority of oral cutaneous fistulas are reported to arise from chronic dental infection. Delay in treatment may result in chronic tissue injury as well as cosmetic deformities. Lesions are often misdiagnosed, leading to delayed management. Misdiagnosis may be the result of the variability of clinical morphological presentation and location of lesions compounded by the lack of knowledge that these lesions can have dental etiology. It is estimated that half of patients with OCF undergo multiple dermatologic surgical operations, antibiotic regimens, and other excisions and biopsies before a correct diagnosis is made. Herein, we present a systematic review to detail cases of odontogenic cutaneous lesions that had been previously misdiagnosed or managed inappropriately. In addition, we include a case report from our own institution. The aims are to demonstrate various presentations of OCF, increase awareness of plastic surgeons and oral maxillofacial surgeons to this pathological condition, and reinforce the importance of prompt diagnosis and treatment. METHODS: The study was conducted following the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. A literature search was conducted in PubMed, Web of Science, and Cochrane databases from January 1, 2013 to July 24, 2023. The following search terms were utilized: "odontogenic cutaneous fistula" OR "odontogenic cutaneous sinus." RESULTS: Twenty-three articles published between 2013 and 2023 were included in this review. In addition, we report a case from our own institution. A total of 28 cases were included in the review. CONCLUSIONS: Diagnosis of OCF is challenging for numerous reasons. Misdiagnosis can lead to multiple trials of antibiotics and surgical procedures as well as reoccurrence of the lesion. Cases summarized highlight the importance of communication between oral maxillofacial surgery, plastic surgery, other medical subspecialists, and dentists in the evaluation of patients with head and neck lesions. Physicians should consider dental etiology in the differential diagnosis of orofacial skin lesions, even if teeth appear normal on oral examination.

Translational Experimental Basis of Indirect Adenosine Receptor Agonist Stimulation for Bone Regeneration: A Review.

Bone regeneration remains a significant clinical challenge, often necessitating surgical approaches when healing bone defects and fracture nonunions. Within this context, the modulation of adenosine signaling pathways has emerged as a promising therapeutic option, encouraging osteoblast activation and tempering osteoclast differentiation. A literature review of the PubMed database with relevant keywords was conducted. The search criteria involved in vitro or in vivo models, with clear methodological descriptions. Only studies that included the use of indirect adenosine agonists, looking at the effects of bone regeneration, were considered relevant according to the eligibility criteria. A total of 29 articles were identified which met the inclusion and exclusion criteria, and they were reviewed to highlight the preclinical translation of adenosine agonists. While preclinical studies demonstrate the therapeutic potential of adenosine signaling in bone regeneration, its clinical application remains unrealized, underscoring the need for further clinical trials. To date, only large, preclinical animal models using indirect adenosine agonists have been successful in stimulating bone regeneration. The adenosine receptors (A1, A2A, A2B, and A3) stimulate various pathways, inducing different cellular responses. Specifically, indirect adenosine agonists act to increase the extracellular concentration of adenosine, subsequently agonizing the respective adenosine receptors. The agonism of each receptor is dependent on its expression on the cell surface, the extracellular concentration of adenosine, and its affinity for adenosine. This comprehensive review analyzed the multitude of indirect agonists currently being studied preclinically for bone regeneration, discussing the mechanisms of each agonist, their cellular responses in vitro, and their effects on bone formation in vivo.

Characterization of a hydrothermally aged experimental alumina-toughened zirconia composite.

OBJECTIVES: To assess the effects of different aging protocols on chemical, physical, and mechanical properties of an experimental ATZ composite compared to a zirconia. METHODS: Disc-shaped specimens were obtained through uniaxial pressing of commercial powders (Tosoh), ATZ comprised of 80%ZrO2/20%Al2O3 (TZ-3YS20AB) and 3Y-TZP (3Y-SBE). The specimens of each material were divided into different groups according to the aging protocol: immediate, autoclave aging and hydrothermal reactor aging. The aging protocols were performed at 134 ºC for 20 h at 2.2 bar. Crystalline evaluations were performed using X-Ray Diffraction. The nanoindentation tests measured the elastic modulus (Em) and hardness (H). Biaxial flexural strength was performed, and Weibull statistics were used to determine the characteristic strength and Weibull modulus. The probability of survival was also determined. The Em and H data were analyzed by one-way ANOVA and Tukey test. RESULTS: Diffractograms revealed the presence of monoclinic phase in both materials after aging. The hydrothermal reactor decreased the Em for ATZ compared to its immediate condition; and the H for both ATZ and 3Y-TZP regarding their immediate and autoclave aging conditions, respectively. The aging protocols significantly increased the characteristic strength for ATZ, while decreased for 3Y-TZP. No difference regarding Weibull modulus was observed, except for 3Y-TZP aged in reactor. For missions of up to 500 MPa, both materials presented a high probability of survival (>99 %) irrespective of aging condition. SIGNIFICANCE: The synthesized ATZ composite exhibited greater physical and microstructural stability compared to 3Y-TZP, supporting potential application of the experimental material for long-span reconstructive applications.

Elucidating the Benefit of Perforated vs Non-Perforated Membranes in Guided Bone Regeneration: An in Vivo Histologic Evaluation and Histomorphometric Analysis.

BACKGROUND: Non-perforated Polytetrafluoroethylene (PTFE) membranes are effectively utilized in guided bone regeneration (GBR) but may hinder cell migration due to limited interaction with the periosteum. This study compared bone regeneration using occlusive or perforated membranes combined with acellular collagen sponge (ACS) and recombinant human bone morphogenic protein-2 (rhBMP-2) in a canine mandibular model. MATERIAL AND METHODS: Male beagle dogs (n=3) received two mandibular defects each to compare ACS/rhBMP-2 with experimental (perforated group) and control (non-perforated group) membranes (n=3 defects/group). Tissue healing was assessed histomorphologically, histomorphometrically and through volumetric reconstruction using microcomputed tomography. RESULTS: The perforated group showed increased bone formation and reduced soft tissue formation compared to the non-perforated group. For the primary outcome, histomorphometric analysis revealed significantly greater total regenerated bone in the perforated group (67.08 ± 6.86%) relative to the nonperforated group (25.18 ± 22.44%) (p = 0.036). Perforated membranes had less soft tissue infiltration (32.91 ± 6.86%) compared to non-perforated membranes (74.82 ± 22.44%) (p = 0.036). CONCLUSION: The increased permeability of membranes in the perforated group potentially enabled periosteal precursor cells greater accessibility to rhBMP-2. The availability may have accelerated their differentiation into mature bone-forming cells, contributing to the stimulation of new bone production, relative to the non-perforated group.

An Evaluation of Autologous Fat Injection as a Treatment for Velopharyngeal Insufficiency: A Review and Integrated Data Analysis.

BACKGROUND: Velopharyngeal insufficiency (VPI) is a condition characterized by incomplete separation of the oral and nasal cavities during speech production, thereby leading to speech abnormalities and audible nasal emissions. Subsequently, this adversely impacts communication and potentially interpersonal social interactions. Autologous fat grafting (AFG) to the velopharynx, a minimally invasive technique, aims to improve oronasal separation by providing bulk and advancing the posterior pharyngeal wall toward the soft palate. Despite its potential, the relative novelty of AFG in treating VPI has resulted in reporting of inconsistent indications, varied surgical techniques, and mixed outcomes across existing literature. METHODS: This systemic review examined the evidence of AFG for VPI treatment over the past decade (2013-2023). A thorough search across five electronic databases yielded 233 studies, with 20 meeting the inclusion criteria (e.g., utilized fat injection as their selected VPI treatment, conducted study in human subjects, did not perform additional surgical procedure at time of fat injection). Selected studies encompassed patient and surgical intervention characteristics, perceptual speech assessment (PSA) scores, gap sizes, nasalance measurements, and complications. RESULTS: The majority of patients had a prior cleft palate diagnosis (78.2%), in which nasoendoscopy was the prevalent method for visualizing the velopharyngeal port defect. Fat harvesting predominantly occurred from the abdomen (64.3%), with an average injection volume of 6.3 mL across studies. PSA and subjective gap size scores were consistently higher preoperatively than postoperatively. PSA score analysis from seven studies revealed significant and sustained improvements postoperatively. Gap size score analysis from four studies demonstrated similar preoperative and postoperative differences. Complications were reported in 17 studies, yielding a 2.7% summative complication rate among 594 cases. CONCLUSIONS: Autologous fat grafting has emerged as a minimally invasive, safe, and effective treatment for mild to moderate VPI. However, challenges remain because of variability in patient selection criteria, diagnostic modalities, and outcome measurements. This review underscores the need for randomized control trials to directly compare AFG with standard-of-care surgical interventions, providing more conclusive evidence of its clinical efficacy.

Application of 3D Printing in Cleft Lip and Palate Repair.

This manuscript reviews the transformative impact of 3-dimensional (3D) printing technologies in the treatment and management of cleft lip and palate (CLP), highlighting its application across presurgical planning, surgical training, implantable scaffolds, and postoperative care. By integrating patient-specific data through computer-aided design and manufacturing, 3D printing offers tailored solutions that improve surgical outcomes, reduce operation times, and enhance patient care. The review synthesizes current research findings, technical advancements, and clinical applications, illustrating the potential of 3D printing to revolutionize CLP treatment. Further, it discusses the future directions of combining 3D printing with other innovative technologies like artificial intelligence, 4D printing, and in situ bioprinting for more comprehensive care strategies. This paper underscores the necessity for multidisciplinary collaboration and further research to overcome existing challenges and fully utilize the capabilities of 3D printing in CLP repair.

Nasopharyngoscopic Evaluation of Velopharyngeal Closure During Speech.

Definitive oronasal separation through closure of the velopharyngeal (VP) sphincter is necessary for the development of normal speech and feeding. Individuals with velopharyngeal incompetence or insufficiency often exhibit hypernasal speech, poor speech intelligibility, and nasal regurgitation. Assessment of VP sphincter function using nasopharyngoscopy is a key element in identifying VP dysfunction. A foundational understanding of normal anatomy and physiology of the velopharyngeal mechanism is paramount to successful diagnosis. This includes recognition of 4 distinct VP sphincter closure patterns: coronal, sagittal, circular, and circular with Passavant's ridge. In this study, the authors showcase 2 patients with velopharyngeal competence who presented to an ear, nose, and throat clinic for nasopharyngoscopic evaluation. This study sought to demonstrate the use of nasopharyngoscopy to recognize velopharyngeal closure patterns and discuss how they may influence the surgical management of VP dysfunction.

What a Ratchet! A Gripping Case Report of an Entrapped Finger with an Unyielding Wrench.

Finger entrapment with rings or ring-like objects is an uncommon possible hand emergency. In cases in which noncutting removal is ineffective, ring cutters or dental drills with carbide or diamond burs have been successfully used. However, objects composed of hard metallic alloys, such as lug nuts or wrenches, are often resistant to such equipment. In these instances, larger diameter metal cutting burrs or rasps may be more advantageous. Due to their increased size and cutting power, these tools are better suited to handle the toughness of hard metals. In this case report, we present the effective and efficient removal of a stainless steel wrench from an entrapped digit using a helicoidal rasp. Availability of this instrument within orthopedic departments may prevent the delays often described in the treatment of finger entrapment when traditional cutting equipment fails.

3D printed ß-tricalcium phosphate versus synthetic bone mineral scaffolds: A comparative in vitro study of biocompatibility.

BACKGROUND: ß-tricalcium phosphate (ß-TCP) has been successfully utilized as a 3D printed ceramic scaffold in the repair of non-healing bone defects; however, it requires the addition of growth factors to augment its regenerative capacity. Synthetic bone mineral (SBM) is a novel and extrudable carbonate hydroxyapatite with ionic substitutions known to facilitate bone healing. However, its efficacy as a 3D printed scaffold for hard tissue defect repair has not been explored. OBJECTIVE: To evaluate the biocompatibility and cell viability of human osteoprecursor (hOP) cells seeded on 3D printed SBM scaffolds via in vitro analysis. METHODS: SBM and ß-TCP scaffolds were fabricated via 3D printing and sintered at various temperatures. Scaffolds were then subject to qualitative cytotoxicity testing and cell proliferation experiments utilizing (hOP) cells. RESULTS: SBM scaffolds sintered at lower temperatures (600 °C and 700 °C) induced greater levels of acute cellular stress. At higher sintering temperatures (1100 °C), SBM scaffolds showed inferior cellular viability relative to ß-TCP scaffolds sintered to the same temperature (1100 °C). However, qualitative analysis suggested that ß-TCP presented no evidence of morphological change, while SBM 1100 °C showed few instances of acute cellular stress. CONCLUSION: Results demonstrate SBM may be a promising alternative to ß-TCP for potential applications in bone tissue engineering.