RESUMO
This study evaluated the influence of hydrofluoric acid (HF) concentration and thermal cycling on the microshear bond strength (µSBS) of a resin luting agent to IPS e.max® CAD and Rosetta® SM. Ceramic specimens (12.0 x 14.0 x 1.5mm) were randomized into 8 groups (n=10) according to HF concentration, commercial brand, and aging. Immediately after polishing, and etching, all specimens were silanized and a layer of adhesive was applied. A PVS mold of 3 mm thickness and 10mm diameter with (four) 1.0mm holes was fabricated, placed on each specimen, and then filled with a resin luting agent. Half of the specimens were subjected to the µSBS test using an Instron at a speed of 1.0 mm/min, following a 24-hour storage in deionized water at 37ºC. The remaining specimens were subjected to thermal cycling (5ºC-55ºC, 30 seconds per bath) and µSBS. The data were evaluated utilizing a three-way ANOVA and Tukey's post-hoc test (α=0.05). Significant differences were found for HF concentration and aging (p<0.0001). No significant difference in µSBS was found for commercial brands (p=0.085). The interaction between brand and HF concentration (p=0.358), brand and aging (p=0.135), and HF concentration and aging (p=0.138) were not statistically significant. The triple interaction among these factors was not statistically significant (p=0.610). In conclusion, the bond strength is affected by the HF concentration. No statistical difference was observed between the two ceramics. Thermal cycling significantly reduced µSBS.
Assuntos
Cerâmica , Colagem Dentária , Ácido Fluorídrico , Cimentos de Resina , Ácido Fluorídrico/química , Cimentos de Resina/química , Cerâmica/química , Teste de Materiais , Análise do Estresse DentárioRESUMO
Many women seek treatment to improve menopausal vasomotor symptoms (VMS). The selection of women most likely to benefit from menopause hormone therapy (MHT) is crucial in clinical practice. There is general agreement that women younger than 60 years or who initiate MHT within the first 10 years of menopause, with no contraindications, have greater benefits considering symptomatic relief and additional advantages. This group may have the advantage of protection from osteoporosis and from other chronic diseases that affect postmenopausal women, namely cardiovascular disease (CVD). Cumulating evidence supports MHT for symptomatic women. However, inadequate use according to the needs of symptomatic women led to a burden of suffering worldwide. In recent years, the emergent use of non-regulated body-identical hormones (non-rBHT) can expose patients to potential harms. These hormone preparations are not regulated through the same tests of safety, efficacy or dosing consistency as regulated-BHT (r-BHT). The POESIT (Portugal + Spain + Italy) recommendations highlight the use of 17ß-estradiol (E2) and micronized progesterone (P4) as the real r-BHT. In addition, the group emphasizes as an example the data from the REPLENISH study with 1 mg E2/100 mg P4. The combination of the two hormones in one convenient pill showed a clear reduction or elimination of hot flashes and an improvement in sleep quality and, consequently, quality of life. At the same time, this combination has shown high rates of amenorrhea and no significant impact on lipid, glucose or coagulation parameters. Both the REPLENISH study and a real-life retrospective study pointed to the possibility of a lower risk of venous thromboembolism (VTE) with this formulation than with other combinations.
Assuntos
Estradiol , Terapia de Reposição de Estrogênios , Fogachos , Menopausa , Progesterona , Humanos , Feminino , Fogachos/tratamento farmacológico , Estradiol/administração & dosagem , Progesterona/administração & dosagem , Progesterona/uso terapêutico , Terapia de Reposição de Estrogênios/métodos , Pessoa de Meia-Idade , Qualidade de Vida , Espanha , ItáliaRESUMO
The objective of this study was to synthesize and characterize porous Cellulose Acetate (CA) scaffolds using the electrospinning technique and functionalize the surface of the scaffolds obtained through the dip-coating method with a Hydroxyapatite (HA) nanocomposite and varying concentrations of graphene oxide (GO) for application in tissue engineering regeneration techniques. The scaffolds were divided into four distinct groups based on their composition: 1) CA scaffolds; 2) CAHAC scaffolds; 3) CAHAGOC 1.0% scaffolds; 4) CAHAGOC 1.5% scaffolds. Scaffold analyses were conducted using X-ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Raman Spectroscopy, Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM/EDS), and in vitro cell viability assays (WST). For the biological test analysis, Variance (two-way) was used, followed by Tukey's post-test (α = 0.05). The XRD results revealed the predominant presence of CaP phases in the CAHAC, CAHAGOC 1.0%, and CAHAGOC 1.5% groups, emphasizing the presence of HA in the scaffolds. FTIR demonstrated characteristics of cellulose and PO4 bands in the groups containing HA, confirming the presence of CaP in the synthesized materials, as also indicated by XRD. Raman spectroscopy showed the presence of D and G bands, consistent with GO, confirming the successful incorporation of the HAGO nanocomposite into the scaffolds. The micrographs displayed overlapping electrospun fibers, forming the three-dimensional structure in the produced scaffolds. It was possible to observe hydroxyapatite crystals filling some of these pores, creating a suitable structure for cell adhesion, proliferation, and nutrition, as corroborated by the results of in vitro tests. All scaffolds exhibited high cell viability, with significant cell proliferation. Even after 48 h, there was a slight reduction in the number of cells, but a noteworthy increase in cell proliferation was evident in the CAHAGOC 1.5% group after 48 h (p < 0.05). In conclusion, it can be affirmed that the produced scaffolds demonstrated physical and biological characteristics and properties capable of promoting cell adhesion and proliferation. Therefore, they represent significant potential for application in tissue engineering, offering a new perspective regarding techniques and biomaterials applied in regenerative therapies.
Assuntos
Celulose , Durapatita , Grafite , Nanocompostos , Engenharia Tecidual , Alicerces Teciduais , Grafite/química , Durapatita/química , Celulose/química , Celulose/análogos & derivados , Nanocompostos/química , Alicerces Teciduais/química , Sobrevivência Celular/efeitos dos fármacos , AnimaisRESUMO
This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.
Assuntos
Colagem Dentária , Porcelana Dentária/química , Cerâmica/química , Cimentos de Resina/química , Teste de Materiais , Propriedades de SuperfícieRESUMO
PURPOSE: This study aimed to evaluate the influence of different manufacturing procedures (Eli annealed - hot work versus cold worked - cold work) of the raw material under mechanical properties and morphological characteristics of orthodontic miniscrews (MS). MATERIAL AND METHODS: Thirty MS were randomly separated into 3 types (n=10) according to manufacturer and manufacturing process of the raw material: type A - SIN® annealed (control group); type B - Dentfix® annealed; and, type C - Dentfix® cold worked. MI were inserted in artificial bone blocks, through the manufacturer's specific manual key attached to the digital torquemeter stabilized via custom device. Data of fracture's occurrence was performed using Fisher's exact test. Comparisons between the other two types regarding insertion torque and removal torque were performed using the Mann-Whitney test. Data of fracture torque, shear stress, normal stress and torque ratio was submitted to Kruskal Wallis and Dunn tests (α=0.05). Representative images of surface morphology and fractures were selected. RESULTS: Type C showed statistically the lowest fracture torque (N.cm) (26.11±0.41) (P=0.0012) and highest torque ratio (%) (98.74±0.85) (P=0.0007). Type C showed statistically higher calculated shear (MPa) (2,432.73±508.41) and normal stress (MPa) (1,403.86±293.39) than type B and type A, showing that they differed in relation to the mechanical strength of the material with which they were made (P=0.0007). CONCLUSION: Type A fractured completely inside the most apical bone. Type B and type C fractured closer to the transmucosal profile. Cold worked process should be more prone to fractures than those annealed raw manufactured.
Assuntos
Procedimentos de Ancoragem Ortodôntica , Titânio , Humanos , Parafusos Ósseos , Desenho de Aparelho Ortodôntico , Ligas , Estresse Mecânico , Propriedades de SuperfícieRESUMO
Abstract This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.
Resumo: Este estudo investigou a resistência de união ao microcisalhamento (RUµC) de dois (2) agentes de cimentação de resina dual (RelyX™ Ultimate e RelyX™ U200) quando fotoativados através de diferentes espessuras de dissilicato de lítio, com ou sem ciclagem térmica. Discos do IPS e.max Press de 0,5, 1,5 e 2 mm de espessura foram obtidos. Moldes de elastômero (3,0 mm de espessura) com quatro orifícios cilíndricos de 1,0 mm de diâmetro foram colocados sobre as superfícies cerâmicas e preenchidos com agentes de cimentação de resina. Uma tira Mylar, placa de vidro e carga de 250 gramas foram colocadas sobre o molde preenchido. A carga foi removida e os agentes de cimentação resinosos foram fotoativados através da cerâmica usando um LED de pico-único (Radii Plus). Todas as amostras foram armazenadas em água deionizada a 37oC por 24 h. Metade das amostras foi submetida a ciclagem térmica (3.000 ciclos; 5ºC e 55ºC). Todas as amostras foram então submetidas ao teste de RUµC usando uma máquina de teste universal (Instron 4411) com velocidade de 0,5 mm/min. Os dados foram submetidos à Análise de Variância três fatores e ao teste post-hoc de Tukey (α = 0,05). A média de RUµC em 24 h foi significativamente maior do que após a ciclagem térmica (p < 0,05). Não houve diferença estatística entre os cimentos resinosos (p > 0,05). As médias de RUµC para grupos fotoativados através de cerâmica de 0,5 mm foram significativamente maiores do que 1,5 mm e 2,0 mm (p < 0,05). Em conclusão, o aumento da espessura da cerâmica reduziu a resistência de união dos agentes de cimentação resinosos ao dissilicato de lítio. Não foram encontradas diferenças entre os agentes de cimentação resinosos. A ciclagem térmica reduziu a resistência de união de ambos os agentes de cimentação resinosos.
RESUMO
Abstract This study evaluated the influence of hydrofluoric acid (HF) concentration and thermal cycling on the microshear bond strength (µSBS) of a resin luting agent to IPS e.max® CAD and Rosetta® SM. Ceramic specimens (12.0 x 14.0 x 1.5mm) were randomized into 8 groups (n=10) according to HF concentration, commercial brand, and aging. Immediately after polishing, and etching, all specimens were silanized and a layer of adhesive was applied. A PVS mold of 3 mm thickness and 10mm diameter with (four) 1.0mm holes was fabricated, placed on each specimen, and then filled with a resin luting agent. Half of the specimens were subjected to the µSBS test using an Instron at a speed of 1.0 mm/min, following a 24-hour storage in deionized water at 37ºC. The remaining specimens were subjected to thermal cycling (5ºC-55ºC, 30 seconds per bath) and µSBS. The data were evaluated utilizing a three-way ANOVA and Tukey's post-hoc test (α=0.05). Significant differences were found for HF concentration and aging (p<0.0001). No significant difference in µSBS was found for commercial brands (p=0.085). The interaction between brand and HF concentration (p=0.358), brand and aging (p=0.135), and HF concentration and aging (p=0.138) were not statistically significant. The triple interaction among these factors was not statistically significant (p=0.610). In conclusion, the bond strength is affected by the HF concentration. No statistical difference was observed between the two ceramics. Thermal cycling significantly reduced µSBS.
Resumo Este estudo avaliou a influência da concentração do ácido fluorídrico (AF) e da ciclagem térmica na resistência de união ao microcisalhamento (RUµC) de um cimento resinoso para IPS e.max® CAD e Rosetta® SM. Espécimes cerâmicos (12,0 x 14,0 x 1,5mm) foram divididos em 8 grupos (n=10) de acordo com concentração do HF, marca comercial e envelhecimento. Imediatamente após o polimento e condicionamento ácido, todos os espécimes foram silanizados e uma camada de adesivo foi aplicada. Um molde PVS de 3 mm de espessura e 10 mm de diâmetro com (quatro) orifícios de 1,0 mm foi confeccionado, colocado em cada espécime e preenchido com o cimento resinoso. Metade dos espécimes foi submetida ao teste RUµC na Instron a velocidade de 1,0 mm/min, após 24 horas de armazenamento em água deionizada a 37ºC. Os espécimes restantes foram submetidos a ciclagem térmica (5ºC-55ºC, 30 segundos por banho) e a RUµC. Os dados foram avaliados por ANOVA de três fatores e ao teste post-hoc de Tukey (α=0,05). Diferenças significativas foram encontradas para concentração de HF e envelhecimento (p<0,0001). Nenhuma diferença significativa na RUµC foi encontrada para cada marca comercial (p=0,085). A interação entre marca comercial e a concentração do HF (p=0,358), marca comercial e envelhecimento (p=0,135) e concentração do HF e envelhecimento (p=0,138) não foram estatisticamente significativas. A tripla interação entre esses fatores não foi estatisticamente significativa (p=0,610). Concluindo, a resistência de união é afetada pela concentração de HF. Não foi observada diferença estatística entre as duas cerâmicas. A ciclagem térmica reduziu significativamente a resistência de união ao microcisalhamento.
RESUMO
ABSTRACT Introduction: Brazil has many inequities in the healthcare provided nationwide. Therefore, in order to access challenges in treatment, available resources and current practices, to identify barriers in delivering a good quality of care among Brazilian centers treating children and adolescents with Non-Hodgkin Lymphoma (NHL) and to generate a future prospective guideline, a customized online survey was distributed to pediatric hematologists and oncologists across the country. Results: A total of 97 surveys were completed (35% response rate), from 47 cities in all Brazilian regions and 79 units of care, with a median of 1 answer by the center (range 1 - 5). Most respondents work at an institution supported exclusively by public/philanthropic resources (58%), with an average of 5 to 9 new cases/year (49%), and 41% have 4 to 6 oncologists/centers. Additionally, 22% have no easy access to the intensive care unit, 26% have no access to Rasburicase, 28% have no access to Rituximabe as front-line therapy and 41% have unreliable methotrexate monitoring levels. Those differences cannot be explained thoroughly by regional wealth variances, nor by the financing model. Regarding the pathology service, 70% consider having reasonable quality assistance, but the timeframe to deliver diagnosis is satisfactory to 46%. There is no uniform management of care, with the current guideline from the Sociedade Brasileira de Oncologia Pediátrica being adopted by 54 to 59%, depending on the NHL subtype. Conclusion: This study provides insights into the heterogeneity of care among Brazilian centers. Recognizing those diversities will support the design of effective strategies and collaboration nationwide.
Assuntos
Linfoma não HodgkinRESUMO
The aim of this study was to quantify the force exerted by tandem archwires in a specific system of passive self-ligating bracket. Forty-eight thermo-activated nickel-titanium orthodontic archwires were separated into four groups (n = 12): G1 - two .014" + .014" round archwires; G2 - two .014" + .016" round archwires; G3 - .014" x .025" rectangular archwire; and. G4 - .016" x .022" rectangular archwire. Brackets were fixed onto teeth 1.5 to 2.5 using a device that represented the upper teeth, maintaining an interbracket distance of 6.0 mm. The deflection tests were performed using the structure representative of tooth 1.1 as support on the Instron testing machine at a speed of 2.0 mm/min. The archwires were evaluated at deflections of 0.5 mm, 1.0 mm, and 1.5 mm. The data were analyzed by a generalized linear model, considering values at different deflections as repeated measurements in the same experimental unit (α = 0.5%). At 0.5 mm, higher forces were observed in G2 and G3, which did not differ significantly (p > 0.05). The lowest force was observed in G4 (p < 0.05). At 1.0 mm and 1.5 mm, the highest force was observed in G3, followed by G4 and G2 (p < 0.05). The lowest force was observed in G1 (p < 0.05). In general, tandem archwires (same or different calibers) in a specific passive self-ligating bracket exerted lower force when compared with rectangular archwires.
Assuntos
Aparelhos Ortodônticos , Projetos de Pesquisa , Modelos LinearesRESUMO
PURPOSE: This study aimed to assess the experience and satisfaction with contraceptives and use of Combined Oral Contraceptives (COC) by women and compare their perceptions with those of gynaecologists. METHODS: This was a multicentre survey study conducted in Portugal, during April and May, 2021 with women using contraceptives and gynaecologists. Online quantitative questionnaires were carried out. RESULTS: A total of 1508 women and 100 gynaecologists were included. Cycle control was the pill non-contraceptive benefit most valued by gynaecologists and women. For gynaecologists, the main pill concern was the risk of thromboembolic events, but they believed that weight gain was the main concern for their patients. The pill was the most used contraceptive (70%) and women were largely (92%) satisfied. The pill was associated with health risks for 85% of users, mainly thrombosis (83%), weight gain (47%), and cancer (37%). The attributes of the pill most valued by women are contraceptive efficacy (82%), followed by low risk of thromboembolic events (68%), good cycle control (60%), non-interference with libido and mood (59%) and weight (53%). CONCLUSION: Most women use contraceptive pills and are generally satisfied with their contraceptive. Cycle control was the most valued non-contraceptive benefit for gynaecologists and women, agreeing with physicians' beliefs about women. On the other hand, contrary to physicians' beliefs, that women's main concern is weight gain, women are mainly concerned with risks associated with contraceptives. Thromboembolic events are women's and gynaecologists most valued risk. Finally, this study indicates the need for physicians to better understand what COC users really fear.
Comparing women's perceptions with those of gynaecologists regarding Combined Oral Contraceptives, this study showed that contrary to physicians' beliefs, that women's main concern is weight gain, their main concern are risks associated with contraceptives. So, physicians need to better understand what women really fear.
Assuntos
Anticoncepção , Anticoncepcionais Orais Combinados , Humanos , Feminino , Masculino , Dispositivos Anticoncepcionais , Aumento de Peso , PercepçãoRESUMO
INTRODUCTION: Brazil has many inequities in the healthcare provided nationwide. Therefore, in order to access challenges in treatment, available resources and current practices, to identify barriers in delivering a good quality of care among Brazilian centers treating children and adolescents with Non-Hodgkin Lymphoma (NHL) and to generate a future prospective guideline, a customized online survey was distributed to pediatric hematologists and oncologists across the country. RESULTS: A total of 97 surveys were completed (35% response rate), from 47 cities in all Brazilian regions and 79 units of care, with a median of 1 answer by the center (range 1 - 5). Most respondents work at an institution supported exclusively by public/philanthropic resources (58%), with an average of 5 to 9 new cases/year (49%), and 41% have 4 to 6 oncologists/centers. Additionally, 22% have no easy access to the intensive care unit, 26% have no access to Rasburicase, 28% have no access to Rituximabe as front-line therapy and 41% have unreliable methotrexate monitoring levels. Those differences cannot be explained thoroughly by regional wealth variances, nor by the financing model. Regarding the pathology service, 70% consider having reasonable quality assistance, but the timeframe to deliver diagnosis is satisfactory to 46%. There is no uniform management of care, with the current guideline from the Sociedade Brasileira de Oncologia Pediátrica being adopted by 54 to 59%, depending on the NHL subtype. CONCLUSION: This study provides insights into the heterogeneity of care among Brazilian centers. Recognizing those diversities will support the design of effective strategies and collaboration nationwide.
RESUMO
Abstract The aim of this study was to quantify the force exerted by tandem archwires in a specific system of passive self-ligating bracket. Forty-eight thermo-activated nickel-titanium orthodontic archwires were separated into four groups (n = 12): G1 - two .014" + .014" round archwires; G2 - two .014" + .016" round archwires; G3 - .014" x .025" rectangular archwire; and. G4 - .016" x .022" rectangular archwire. Brackets were fixed onto teeth 1.5 to 2.5 using a device that represented the upper teeth, maintaining an interbracket distance of 6.0 mm. The deflection tests were performed using the structure representative of tooth 1.1 as support on the Instron testing machine at a speed of 2.0 mm/min. The archwires were evaluated at deflections of 0.5 mm, 1.0 mm, and 1.5 mm. The data were analyzed by a generalized linear model, considering values at different deflections as repeated measurements in the same experimental unit (α = 0.5%). At 0.5 mm, higher forces were observed in G2 and G3, which did not differ significantly (p > 0.05). The lowest force was observed in G4 (p < 0.05). At 1.0 mm and 1.5 mm, the highest force was observed in G3, followed by G4 and G2 (p < 0.05). The lowest force was observed in G1 (p < 0.05). In general, tandem archwires (same or different calibers) in a specific passive self-ligating bracket exerted lower force when compared with rectangular archwires.
RESUMO
A new device was developed to enable the visualization and measurement of canine angulation while at the same time visualizing and measuring the force transmitted to adjacent teeth. This study aimed to evaluate the mesiodistal tilt angle of the upper canine brackets, the wire deflection, and its effects on adjacent teeth with five different slot designs of upper canines. Wires (0.020" and 0.019" x 0.025") were tested on different five bracket types at five different distal angles. The force applied to adjacent teeth was measured as the angle was increased, and its consequences were observed in the posterior and anterior regions as well. The force tension (gf) was measured in a universal testing machine. Data were submitted to a 3-way ANOVA and Tukey's test (α=0.05). For both arches, regardless of the type of tooth and bracket type, the highest means tension mean values were shown by the 20° angle, followed by the 15°,10°, and 5° angles, which differed statistically among themselves. Overall, for 5°, 10°, and 15° angles, conventional and versatile brackets showed significantly higher force values in all teeth, tip-edge and control brackets showed the lowest. The highest force values were observed in central and lateral incisors with conventional and versatile brackets and on first and second premolar teeth with self-ligating passive and control brackets. Conventional brackets presented the highest forces, tip-edge and control brackets showed the lowest. The teeth that suffered the greatest forces were lateral incisors, and those that suffered the least were second premolars.
Assuntos
Braquetes Ortodônticos , Fios Ortodônticos , Desenho de Aparelho Ortodôntico , Aço Inoxidável , Fricção , Análise do Estresse Dentário , Teste de MateriaisRESUMO
Abstract A new device was developed to enable the visualization and measurement of canine angulation while at the same time visualizing and measuring the force transmitted to adjacent teeth. This study aimed to evaluate the mesiodistal tilt angle of the upper canine brackets, the wire deflection, and its effects on adjacent teeth with five different slot designs of upper canines. Wires (0.020" and 0.019" x 0.025") were tested on different five bracket types at five different distal angles. The force applied to adjacent teeth was measured as the angle was increased, and its consequences were observed in the posterior and anterior regions as well. The force tension (gf) was measured in a universal testing machine. Data were submitted to a 3-way ANOVA and Tukey's test (α=0.05). For both arches, regardless of the type of tooth and bracket type, the highest means tension mean values were shown by the 20° angle, followed by the 15°,10°, and 5° angles, which differed statistically among themselves. Overall, for 5°, 10°, and 15° angles, conventional and versatile brackets showed significantly higher force values in all teeth, tip-edge and control brackets showed the lowest. The highest force values were observed in central and lateral incisors with conventional and versatile brackets and on first and second premolar teeth with self-ligating passive and control brackets. Conventional brackets presented the highest forces, tip-edge and control brackets showed the lowest. The teeth that suffered the greatest forces were lateral incisors, and those that suffered the least were second premolars.
Resumo Foi desenvolvido um novo dispositivo para permitir a visualização e medição da angulação canina ao mesmo tempo que se visualiza e mede a força transmitida aos dentes adjacentes. Este estudo avaliou o ângulo de inclinação mesiodistal dos braquetes caninos superiores, a deflexão do fio, e os seus efeitos nos dentes adjacentes com cinco diferentes desenhos de ranhuras dos caninos superiores. Os fios (0,020" e 0,019" x 0,025") foram testados em cinco diferentes tipos de braquetes e ângulos distais. A força aplicada aos dentes adjacentes foi medida a medida que o ângulo era aumentado, e as suas consequências foram observadas também nas regiões posterior e anterior. A tensão da força (gf) foi medida em uma máquina de ensaio universal (Instron). Os dados foram submetidos ao teste ANOVA 3 fatores e Tukey (α=0,05). Para ambos os arcos, independentemente do tipo de dente e tipo de braquete, os valores médios de tensão mais elevados foram mostrados pelo ângulo de 20°, seguido pelos ângulos de 15°, 10°, e 5°, que diferiram estatisticamente entre si. Em geral, para ângulos de 5°, 10° e 15°, os braquetes convencionais e versáteis apresentaram valores de força significativamente mais elevados em todos os dentes, braquetes tip-edge e controle apresentaram os mais baixos. Os maiores valores de força foram observados nos incisivos centrais e laterais com braquetes convencionais e versáteis e no primeiro e segundo pré-molares com braquetes auto-ligantes passivo e controle. Os braquetes convencionais apresentaram as forças mais elevadas, os braquetes controle e tip-edge apresentaram os valores mais baixos. Os dentes que sofreram as maiores forças foram os incisivos laterais, e os que sofreram menos foram os segundos pré-molares.
RESUMO
PURPOSE: To evaluate in vitro the effect of gastroesophageal reflux, before and after bonding of metal brackets on composite resin surface. MATERIALS AND METHODS: Two hundred and ten resin discs were divided into 5 groups (n=42), according to the time and medium of storage: 24h, 7- and -30 days in artificial saliva (AS) and hydrochloric acid (HCL). Twelve samples from each group were submitted to surface roughness analysis (n=60). The other one hundred and fifty samples were divided into 3 groups (n=50) according to the bonding material: Transbond™ XT (TXT), 3M™ Filtek™ Z250 (Z250) and 3M™ Filtek™ Z350 XT (Z350). After bonding, the samples were subdivided, one more time, into 5 groups (n=10) according to the time (24h, 7, and 30 days) and medium storage (AS, HCL). Following, the shear bond strength (SBS) analysis was accomplished. Erosive challenge was performed for 7 or 30 days, before and after bonding of orthodontic brackets, for 1min, 4 times a day. SBS was performed in a universal testing machine (Instron) at 0.5mm/min. SBS data were subjected to two-way ANOVA and Tukey's test (α=0.05). RESULTS: TXT showed higher SBS values in all conditions (AS - 10.9±2.0 (24h); 10.5±4.9 (7 days); 9.4±2.2 (30 days); HCL - 11.5±3.7 (7 days); 8.0±2.1 (30 days)) - (P<0.0001). No statistical difference was detected in SBS between Z250 and Z350 composite resins (Z250 SBS: AS - 7.1±1.9 (24h), 5.2±1.8 (7 days), 4.5±1.5 (30 days); HCL - 5.2±2.3 (7 days), 5.0±2.5 (30 days)) - (P<=0.063)/Z350 SBS: AS - 7.4±1.0 (24h); 3.7±1.7 (7 days); 3.4±1.7 (30 days); HCL - 3.5±3.3 (7 days); 4.4±1.2 (30 days)) - (P<=0.167), respectively). Storage times and media did not statistically influence the SBS of TXT and Z250 composite resins (P>0.05), but did influence the Z350 SBS (P<0.05). CONCLUSION: Regardless of time and storage medium, TXT was the best composite resin for bonding brackets. Furthermore, the erosive challenge did not lead to surface changes in the Z250 resin at 7 and 30 days, unlike the Z350 resin.
Assuntos
Colagem Dentária , Refluxo Gastroesofágico , Braquetes Ortodônticos , Resinas Compostas/química , Análise do Estresse Dentário , Humanos , Teste de Materiais , Cimentos de Resina/química , Saliva Artificial , Resistência ao Cisalhamento , Propriedades de SuperfícieRESUMO
OBJECTIVES: The aim of this study was to measure the frictional resistance of different types of ligatures used on conventional and self-ligating brackets. MATERIALS AND METHODS: Monoblock (conventional) and Portia (self-ligating) brackets were used and the archwire used was nickel-titanium. On conventional brackets the ligatures tested were the Elastomeric type and steel 0.30 tie-wire. The groups were divided according to the ligature types (n=8): (1) conventional elastomeric ligature; (2) relaxed conventional elastomeric ligature; (3) elastomeric ligature in shape-8; (4) double vertical elastomeric ligatures; (5) double-crossed elastomeric ligatures; (6) crossed ligature; (7) steel wire ligature; and (8) self-ligating ligature (self-ligating bracket). A segment of five brackets, each ligature types, was mounted. The archwire, between the bracket and the ligature, was connected on Instron® Universal test machine to simulate the frictional resistance. The maximum frictional resistance was obtained, and the mean values were submitted to the analysis of variance (ANOVA) and the Tukey's post-hoc test (α=0.05). RESULTS: The elastomeric ligature in shape-8 showed the highest value compared with other groups (P<0.05). Although the crossed elastomeric ligature presented the lowest mean value and it was not statistically different regarding relaxed conventional elastomeric ligature, steel wire ligature and self-ligating (P≥0.05). CONCLUSIONS: The frictional resistance was influenced by ligature types. Elastomeric Ligature in shape-8 showed the highest frictional force. Crossed Elastomeric Ligature had the lowest frictional force value.
Assuntos
Braquetes Ortodônticos , Fios Ortodônticos , Ligas Dentárias , Análise do Estresse Dentário , Fricção , Humanos , Teste de Materiais , Níquel , Desenho de Aparelho Ortodôntico , Aço Inoxidável , TitânioRESUMO
OBJECTIVE: The aim of this study was to evaluate the physical-chemical changes in orthodontic devices made with laser and silver solder after immersion in different antiseptic solutions. METHODS: Wire/band assemblies were fabricated using different types of solders (silver and laser). The devices were immersed in different antimicrobial solutions (chlorhexidine - CHX 0.12% and Silver nanoparticles - NAg 0.12% and 0.18%). Non-immersion in solution and immersion in artificial saliva were used as initial and negative control, respectively (n=12). Surface morphological analysis was performed using Scanning Electron Microscopy (SEM). The quantitative analysis of the chemical elements present after the immersions in the solutions was analysed by Energy Dispersive X-ray Spectroscopy (EDS). The data were subjected to the Kruskal-Wallis test followed by Bonferroni, with a significance level of 5%. RESULTS: Greater amounts of copper, silver and zinc were released from silver soldering, on the other hand, iron, nickel, and chromium ions were the most prevalent metal ions in laser soldering. Regarding mouthwashes, the lowest amounts of metal ions were released in CHX, and the highest amounts of ions were released in the 0.12% NAg and 0.18% NAg solutions. CONCLUSIONS: Laser welding seems to be less susceptible to corrosion. The different antiseptic solutions did not contribute to an increase in ion release.
Assuntos
Anti-Infecciosos Locais , Soldagem em Odontologia , Nanopartículas Metálicas , Clorexidina , Corrosão , Soldagem em Odontologia/métodos , Humanos , Íons , Lasers , Teste de Materiais , Aparelhos Ortodônticos , Prata/químicaRESUMO
The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on microtensile bond strength (µTBS) between an adhesive system and under 3 dentin conditions. For that, this study evaluated the adhesive interface at initial, after 6 months and 1 year of storage. Forty-eight human third molars were prepared and randomly divided into 3 groups, according to dentin substrates: sound dentin (Sd), caries-infected dentin (Ci) and caries-affected dentin (Ca). The groups were subdivided into two according to the dentin pre-treatment: application of 2% CHX or without pre-treatment (control). The dentin surfaces were etched with 35% phosphoric acid gel and bonded with Adper Single Bond 2 (3M ESPE) adhesive system according to manufacturer's instructions. Subsequently, the specimens were stored in deionized water at 37°C for 24h, 6 months and 1 year. Two additional teeth were used to analyze the bonding interfaces by SEM. Data was submitted to three-way ANOVA in a split plot design and Tukey's test (α = 0.05). The results showed that Ci decreased µTBS values when compared to Ca and Sd, regardless storages time or treatment. Stored samples for 6 months and 1 year decreased the µTBS for the control group, but no difference was found between storages time for the CHX group. As a conclusion, the 2% CHX application after etching showed improved dentin bond strength in the storage time, regardless of the substrates evaluated.
Assuntos
Colagem Dentária , Adesivos Dentinários , Resinas Compostas , Dentina , Humanos , Teste de Materiais , Cimentos de Resina , Resistência à TraçãoRESUMO
The purpose of this in vitro study was to evaluate the force decrease of different elastomeric chains after different times: initial, 10 minutes, 1 day, 28 days and after mechanical brushing. Twenty orthodontic elastomeric chains segments were utilized for each commercial brand. Initially, the elastomeric chain of 15mm long were immediate stretched up to 20 mm in an Instron and the force was measured in gf. After all specimens were placed stretched on rectangular acrylic jigs with distance of 20 mm, immersed in deionized water at 37oC for 10 minutes and the force (gf) was measured again. Five test measurements of remaining force were made at the following time intervals: initial, 10 minutes, 1 day, 28 days and mechanical brushing. After 28 days, the acrylic plates with the specimens were adapted in the mechanical brushing machines (MSCT 3) and the elastomeric chains were submitted to mechanical brushing and the force (gf) measure again. The force (gf) was submitted to mixed-model ANOVA and Sidak post-hoc test (α=0.05). A statistically significant reduction in the force was found for all orthodontic elastomeric chain types after 1 day, 28 days and mechanical brushing (p<0.05). Morelli and 3M Unitek elastomeric chains showed significantly higher force than Abzil and GAC (p<0.05) after 1 day, 28 days and mechanical brushing. In conclusion, the force delivered by all elastomeric chains decayed rapidly over time. Morelli and 3M Unitek elastomeric chains consistently had a significantly greater force after mechanic brushing, while GAC the lowest.