RESUMO
The demand for macroporous hydrogel scaffolds with interconnected porous and open-pore structures is crucial for advancing research and development in cell culture and tissue regeneration. Existing techniques for creating 3D porous materials and controlling their porosity are currently constrained. This study introduces a novel approach for producing highly interconnected aspartic acid-gelatin macroporous hydrogels (MHs) with precisely defined open pore structures using a one-step emulsification polymerization method with surface-modified silica nanoparticles as Pickering stabilizers. Macroporous hydrogels offer adjustable pore size and pore throat size within the ranges of 50 to 130 µm and 15 to 27 µm, respectively, achieved through variations in oil-in-water ratio and solid content. The pore wall thickness of the macroporous hydrogel can be as thin as 3.37 µm and as thick as 6.7 µm. In addition, the storage modulus of the macroporous hydrogels can be as high as 7250 Pa, and it maintains an intact rate of more than 92% after being soaked in PBS for 60 days, which is also good performance for use as a biomedical scaffold material. These hydrogels supported the proliferation of human dental pulp stem cells (hDPSCs) over a 30 day incubation period, stretching the cell morphology and demonstrating excellent biocompatibility and cell adhesion. The combination of these desirable attributes makes them highly promising for applications in stem cell culture and tissue regeneration, underscoring their potential significance in advancing these fields.