High temperature reverse-bias (HTRB), High temperature gate-bias (HTGB) tests and electrical DC characterization were performed on planar-SiC power MOSFETs which survived to accelerated neutron irradiation tests carried out at ChipIr-ISIS (Didcot, UK) facility, with terrestrial neutrons. The neutron test campaigns on the SiC power MOSFETs (manufactered by ST) were conducted on the same wafer lot devices by STMicroelectronics and Airbus, with different neutron tester systems. HTGB and HTRB tests, which characterise gate-oxide integrity and junction robustness, show no difference between the non irradiated devices and those which survived to the neutron irradiation tests, with neutron fluence up to 2× 1011 (n/cm2). Electrical characterization performed pre and post-irradiation on different part number of power devices (Si, SiC MOSFETs and IGBTs) which survived to neutron irradiation tests does not show alteration of the data-sheet electrical parameters due to neutron interaction with the device.
RESUMO
The photo-oxidative studies of ethylene vinyl acetate copolymer (EVA) matrix, filled with Layered Double Hydroxide (LDH) modified with methacrylic anion (MA), were herein reported, together with gas permeation tests. The formulation of nano-hybrid LDHs was characterized using X-ray diffractometry (XRD) and thermogravimetric analysis (TGA), demonstrating the partial intercalation of the 30% of MA anion between the LDH's galleries. The as-modified filler was introduced into an EVA matrix by mechanical milling, producing free-standing films subjected to accelerated aging. Fourier transform infrared spectroscopy (FT-IR) results suggested that the nanohybrid presence determined a stabilizing effect up to 45 days of UV irradiation, especially if compared to the EVA/LDH references for all formulated EVA hybrid nanocomposites. Conversely, the presence of nanohybrid in the matrix did not significantly change the thermal stability of EVA samples. The dispersion of modified MA-LDH in the EVA matrix produces defect-free samples in the whole range of investigated loadings. The samples show a slight decrease in gas permeability, coupled with a substantial stabilization of the original CO2/O2 selectivity, which also proves the integrity of the films after 30 days of UV irradiation.
RESUMO
The immobilization of inorganic nanomaterials on polymeric substrates has been drawing a lot of attention in recent years owing to the extraordinary properties of the as-obtained materials. The hybrid materials, indeed, combine the benefits of the plastic matter such as flexibility, low-cost, mechanical stability and high durability, with them deriving from their inorganic counterparts. In particular, if the inorganic fillers are nanostructured photocatalysts, the originated hybrid systems will be able to utilize the energy delivered by light, catalysing chemical reactions in a sustainable pathway. Most importantly, since the nanofillers can be ad-hoc anchored to the macromolecular structure, their release in the environment will be prevented, thus overcoming one of the main restrictions that impedes their applications on a large scale. In this review, several typologies of hybrid photocatalytic nanomaterials, obtained by using both organic and inorganic semiconductors and realized with different synthetic protocols, were reported and discussed. In the first part of the manuscript, nanocomposites realized by simply blending the TiO2 or ZnO nanomaterials in thermoplastic polymeric matrices are illustrated. Subsequently, the atomic layer deposition (ALD) technique is presented as an excellent method to formulate polymeric nanocomposites. Successively, some examples of polyporphyrins hybrid systems containing graphene, acting as photocatalysts under visible light irradiation, are discussed. Lastly, photocatalytic polymeric nanosponges, with extraordinary adsorption properties, are shown. All the described materials were deeply characterized and their photocatalytic abilities were evaluated by the degradation of several organic water pollutants such as dyes, phenol, pesticides, drugs, and personal care products. The antibacterial performance was also evaluated for selected systems. The relevance of the obtained results is widely overviewed, opening the route for the application of such multifunctional photocatalytic hybrid materials in wastewater remediation.
RESUMO
Photocatalysis has long been touted as one of the most promising technologies for environmental remediation. The ability of photocatalysts to degrade a host of different pollutants, especially recalcitrant molecules, is certainly appealing. Titanium dioxide (TiO2) has been used extensively for this purpose. Anodic oxidation allows for the synthesis of a highly ordered nanotubular structure with a high degree of tunability. In this study, a series of TiO2 arrays were synthesised using different electrolytes and different potentials. Mixed anatase-rutile photocatalysts with excellent wettability were achieved with all the experimental iterations. Under UVA light, all the materials showed significant photoactivity towards different organic pollutants. The nanotubes synthesised in the ethylene glycol-based electrolyte exhibited the best performance, with near complete degradation of all the pollutants. The antibacterial activity of this same material was similarly high, with extremely low bacterial survival rates. Increasing the voltage resulted in wider and longer nanotubes, characteristics which increase the level of photocatalytic activity. The ease of synthesis coupled with the excellent activity makes this a viable material that can be used in flat-plate reactors and that is suitable for photocatalytic water treatment.
RESUMO
This work attempts to produce photocatalytic surfaces for large-scale applications by depositing nanostructured coatings on polymeric substrates. ZnO/poly(methyl methacrylate) (PMMA) composites were prepared by low-temperature atomic layer deposition (ALD) of ZnO on PMMA substrates. In addition, to increase the photocatalytic and antibacterial activities of ZnO films, Ag nanoparticles were added on ZnO surfaces using plasma-enhanced ALD. The morphology, crystallinity, and chemical composition of the specimens were meticulously examined by scanning and transmission electron microscopies, energy-dispersive X-ray spectroscopy, and X-ray diffraction analyses. The noteworthy photocatalytic activity of the nanocomposites was proved by the degradation of the following organic pollutants in aqueous solution: methylene blue, paracetamol, and sodium lauryl sulfate. The antibacterial properties of the samples were tested using Escherichia coli as a model organism. Moreover, the possible toxic effects of the specimens were checked by biological tests. The present results unambiguously indicate the Ag/ZnO/PMMA nanocomposite as a powerful tool for an advanced wastewater treatment technology.
RESUMO
Two-dimensional (2D) nanomaterials have received much attention in recent years, because of their unusual properties associated with their ultra-thin thickness and 2D morphology. Besides graphene, a new 2D material, molybdenum disulfide (MoS2), has attracted immense interest in various applications. On the other hand, ball-milling process provides an original strategy to modify materials at the nanometer scale. This methodology represents a smart solution for the fabrication of MoS2 nanopowders extremely-efficient in adsorbing water contaminants in aqueous solution. This work reports a comprehensive morphological, structural, and physicochemical investigation of MoS2 nanopowders treated with dry ball-milling. The adsorption performances of the produced nanopowders were tested using methylene blue (MB) dye and phenol in aqueous solution. The adsorption capacity as a function of ball-milling time was deeply studied and explained. Importantly, the ball-milled MoS2 nanopowders can be easily and efficiently regenerated without compromising their adsorption capacity, so to be reusable for dye adsorption. The eventual toxic effects of the prepared materials on microcrustacean Artemia salina were also studied. The present results demonstrate that ball-milling of MoS2 offers a valid method for large-scale production of extremely efficient adsorbent for the decontamination of wastewaters from several pollutants.
RESUMO
HYPOTHESIS: If nanocrystals of such semiconductor as SnO2 and TiO2, which are not known as powerful adsorbents, have their surface modified by layer of V2O5, how will the adsorption properties be affected? Answering this question would provide a new set of surface properties to be designed by surface engineering of oxide nanocrystals. EXPERIMENTS: SnO2 and TiO2 colloidal nanocrystals were prepared by coupling sol-gel and solvothermal synthesis. By co-processing with V chloroalkoxide and subsequent heat-treatment at 400-500⯰C, surface deposition of V2O5 layers was obtained. The methylene blue adsorption onto the prepared materials was tested and compared with the pure oxide supports. Cycling of the materials and analysis of the adsorption process was also investigated. FINDINGS: The V-modified nanocrystals extracted â¼80% methylene blue from 1.5â¯×â¯10-5 M aqueous solution after 15â¯min only, contrarily to pure materials, which took up only 30% of the dye even after 120â¯min. Comparison with pure commercial V2O5 showed that the peculiar adsorption properties were imparted by the surface deposition of the V2O5-like layers. This report demonstrates that new classes of adsorbing materials can be conceived by suitably coupling different metal oxides.
RESUMO
The design of new hybrid nanocomposites based on poly(2-hydroxyethylmethacrylate) (pHEMA) graphene oxide (GO) cryosponges, wherein ZnO nanolayers have been deposited to induce photocatalytic properties, is reported here. Atomic layer deposition at low temperature is specifically selected as the deposition technique to stably anchor ZnO molecules to the pendant polymer OH groups. Furthermore, to boost the pHEMA cryogel adsorption capability versus organic dyes, GO is added during the synthetic procedure. The morphology, the crystallinity, and the chemical composition of the samples are deeply investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction analyses, Fourier transform infrared spectroscopy, and thermogravimetric analysis. Swelling properties, mechanical performance, and adsorption kinetics models of the hybrid materials are also evaluated. Finally, the adsorption and photocatalytic performance are tested and compared for all of the samples using methylene blue as a dye. Particularly, the adsorption efficiency of ZnO/pHEMA and ZnO/pHEMA-GO nanocomposites, as well as their in situ regeneration via photocatalysis, renders such devices very appealing for advanced wastewater treatment technology.
RESUMO
The incorporation of nanostructured photocatalysts in polymers is a strategic way to obtain novel water purification systems. This approach takes the advantages of: (1) the presence of nanostructured photocatalyst; (2) the flexibility of polymer; (3) the immobilization of photocatalyst, that avoids the recovery of the nanoparticles after the water treatment. Here we present ZnO-polymer nanocomposites with high photocatalytic performance and stability. Poly (methyl methacrylate) (PMMA) powders were coated with a thin layer of ZnO (80 nm thick) by atomic layer deposition at low temperature (80 °C). Then the method of sonication and solution casting was performed so to obtain the ZnO/PMMA nanocomposites. A complete morphological, structural, and chemical characterization was made by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) analyses. The remarkable photocatalytic efficiency of the nanocomposites was demonstrated by the degradation of methylene blue (MB) dye and phenol in aqueous solution under UV light irradiation. The composites also resulted reusable and stable, since they maintained an unmodified photo-activity after several MB discoloration runs. Thus, these results demonstrate that the proposed ZnO/PMMA nanocomposite is a promising candidate for photocatalytic applications and, in particular, for novel water treatment.
RESUMO
For this study, we originally realized ZnO nanofibers (â¼50 nm in mean radius) mixed with Pt nanoparticles (â¼30 nm in mean radius), prepared by pulsed laser ablation in liquid, and investigated their photocatalytic performance. The material was synthesized by the simple electrospinning method coupled with subsequent thermal treatments. Methylene blue was employed as a representative dye pollutant to evaluate the photocatalytic activity of the nanofibers. It was found that the Pt-ZnO fibers exhibit a photodegradation reaction rate that is â¼40 % higher than the one obtained for reference ZnO fibers. These encouraging results demonstrate that Pt-ZnO nanofibers can be fruitfully applied for environmental applications.
RESUMO
Cysteine is a sulfur-containing amino acid that easily coordinates to soft metal ions and grafts to noble metal surfaces. Recently, chiroptical activity of Ag(+)/cysteine coordination polymers has been widely studied, while, on the other hand, the appearance of a plasmon-enhanced circular dichroic signal (PECD) at the plasmonic spectral region (λ > 400 nm) has been observed for AgNPs capped with chiral sulfur-containing amino acids. These two events are both potentially exploited for sensing applications. However, the presence of Ag(+) ions in AgNP colloidal solution deals with the competition of cysteine grafting at the metal NP surface and/or metal ion coordination. Herein we demonstrate that the chiroptical activity observed by adding cysteine to AgNP colloids prepared by pulsed laser ablation in liquids (PLAL) is mainly related to the formation of CD-active Ag(+)/cysteine supramolecular polymers. The strict correlation between supramolecular chirality and hierarchical effects, driven by different chemical environments experienced by cysteine when different titration modalities are used, is pivotal to validate cysteine as a fast and reliable probe to characterize the surface oxidation of AgNPs prepared by pulsed laser ablation in liquids by varying the laser wavelengths.
Assuntos
Complexos de Coordenação/química , Cisteína/química , Polímeros/química , Prata/química , Nanopartículas Metálicas/química , Modelos Moleculares , Conformação Molecular , Nitrato de Prata/química , EstereoisomerismoRESUMO
Understanding the factors that governs spontaneous molecular transfer from solution to solid surface is fundamental to control noncovalent surface functionalization strategies, both in term of robustness and reproducibility. The comprehension of the nature of interaction involved in the mechanism of spontaneous adsorption will allow for a fine modulation of the deposition process. Herein, we provide experimental evidences to demonstrate that poly-lysine secondary structure represents a crucial factor profoundly influencing the outcome of its spontaneous deposition on quartz surfaces. In particular, random coil to α-helix transition is required to drive an effective transfer of the poly-l-lysine at the liquid-solid interface. ß-sheet deposition requires longer times to be accomplished, while random-coil deposition is highly unfavored. Accordingly, polylysine deposition on quartz and silicon is effective when α-helix is formed in solution (pH>10). This surface noncovalent functionalization represents a simple strategy to fabricate hybrid organic-inorganic or biocompatible materials. In fact, the proposed methodology is proven robust and repeatable and compatible for combination with solution or vapor phases (i.e. MOCVD) nanomaterial deposition approaches.