A traditional phase transformation method is commonly used to prepare molecular imprinting membranes for selective separation. However, traditional molecularly imprinted polymers are mostly micron-sized particles, and the imprinting sites in their membrane are easily embedded, leading to a reduced adsorption capacity and decreased selectivity. In this study, an ultra-long nanowire with a diameter of about 15 nm was synthesized for the separation of artemisinin (ART), and its adsorption capacity was as high as 198.29 mg g-1 after imprinting polymerization. Molecular imprinting membranes were prepared, using polyvinylidene fluoride (PVDF), polyethersulfone (PES), and polysulfone (PSF) as the membrane matrix, for comparison. The average membrane pore size of PVDF-MIM was about 480 nm, and PVDF-MIM had the highest adsorption capacity (69 mg g-1) for ART. The optimal flow rate for PVDF-MIM's dynamic adsorption of ART was 7 mL min-1. Under this optimal flow rate, selectivity experiments were carried out to obtain the separation factor of PVDF-MIM (α = 8.37), which was much higher than the corresponding values of PES-MIM and PSF-MIM. In addition, the hydrophobicity and low flux of PES-MIM and PSF-MIM lead to higher non-specific adsorption. The hydrophobicity of PVDF-MIM is lower than that of PES-MIM and PSF-MIM, which greatly reduces the non-specific adsorption of the membrane, thus increasing the selectivity of the membranes. Therefore, the effective density of the imprinting sites in the pores and the membrane structure are the main factors determining the efficient separation of molecularly imprinted membranes.
RESUMO
The selective separation and purification of artesunate (ARU) and artemisinin (ART) using zirconium-based metal-organic frameworks (MOF), especially UiO-66 MOF, are receiving increasing attention. In this study, tunable "hydrophobic" sites of thiol (-SH) were introduced to amino-functionalized MOFs (UiO-66-NH2) to fabricate a thiol-amino bifunctional UiO-66/polyvinylidene fluoride (PVDF)-blended membrane (S1-UiO/PVDF-DPIM) via the delayed-phase-inversion method for selective separation of ARU/ART. The adsorption results indicated that the modification of UiO-66-NH2 with thiol can indeed increase the ARU adsorption. The thiol-functional MOF (S1-UiO-66-NH2) was chosen as the optimal thiol-amino bifunctional MOF, as it possessed the maximum ARU adsorption capacity (111.14 mg g-1) and the highest selective-separation factor (α = 51.84). The ATR FT-IR dynamic spectrum disclosed the recognition mechanism, indicating that incorporating thiol groups into a hydrophilic MOF as hydrophobic sites can boost adsorption efficiency. Moreover, the static-selective permeation results showed that the S1-UiO/PVDF-DPIM preferentially transfers ARU when mixed with ART, even achieving complete ARU/ART separation. The most crucial aspect was the introduction of a hydrophobic core of -SH and new spontaneously formed disulfide bonds to S1-UiO/PVDF-DPIM, creating alternated hydrogen bonds and hydrophobic interactions. This work provides an alternative strategy to prepare hydrophobic-hydrophilic MOF-based membranes for the highly efficient and selective separation of complex analogue systems.