The advantage of 3D printing-that is, additive manufacturing (AM) of structural materials-has been severely compromised by their disappointing fatigue properties1,2. Commonly, poor fatigue properties appear to result from the presence of microvoids induced by current printing process procedures3,4. Accordingly, the question that we pose is whether the elimination of such microvoids can provide a feasible solution for marked enhancement of the fatigue resistance of void-free AM (Net-AM) alloys. Here we successfully rebuild an approximate void-free AM microstructure in Ti-6Al-4V titanium alloy by development of a Net-AM processing technique through an understanding of the asynchronism of phase transformation and grain growth. We identify the fatigue resistance of such AM microstructures and show that they lead to a high fatigue limit of around 1 GPa, exceeding the fatigue resistance of all AM and forged titanium alloys as well as that of other metallic materials. We confirm the high fatigue resistance of Net-AM microstructures and the potential advantages of AM processing in the production of structural components with maximum fatigue strength, which is beneficial for further application of AM technologies in engineering fields.
RESUMO
The typical microstructure of the laser melting deposition (LMD) additive-manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy (TC11) contains the heat-affected bands (HABs), the narrow bands (NBs) and the melting pools (MPs) that formed due to the reheating and superheating effects during the layer-by-layer manufacturing process. Characterization results indicated that the coarse primary α lath (αp) and transformed ß (ßt) structures were located in the HABs, while the fine basketweave structure was formed inside the MPs. The rapid modifications of microstructure and tensile properties of the LMD-TC11 via electropulsing treatment (EPT) were investigated. The initial heterogeneous microstructure transformed into a complete basketweave structure and the HABs vanished after EPT. Thus, a more homogeneous microstructure was achieved in the EPT sample. The ultrafast microstructural changes were mainly attributed to the solid state phase transformation during electropulsing. The tensile properties of the sample were basically stable, except that the yield strength decreased as EPT voltage increased. This study suggests that EPT could be a promising method to modify the microstructure and mechanical properties of the additive-manufactured alloys in a very short time.