RESUMO
The oxidation of Carbon monoxide (CO) to Carbon dioxide (CO2) is one of the most extensively investigated reactions in the field of heterogeneous catalysis, and it occurs via molecular rearrangements induced by catalytic metal atoms with oxygen intermediates. CO oxidation and CO2 capture are instrumental processes in the reduction of green-house gas emissions, both of which are used in low-temperature CO oxidation in the catalytic converters of vehicles. CO oxidation and CO2 adsorption at different temperatures are evaluated for palladium-supported silica aerogel (Pd/SiO2). The synthesized catalyst was active and stable for low-temperature CO oxidation. The catalytic activity was enhanced after the first cycle due to the reconditioning of the catalyst's pores. It was found that the presence of oxide forms of palladium in the SiO2 microstructure, influences the performance of the catalysts due to oxygen vacancies that increases the frequency of active sites. CO2 gas adsorption onto Pd/SiO2 was investigated at a wide-ranging temperature from 16 to 120 °C and pressures â¼1 MPa as determined from the isotherms that were evaluated, where CO2 showed the highest equilibrium adsorption capacity at 16 °C. The Langmuir model was employed to study the equilibrium adsorption behavior. Finally, the effect of moisture on CO oxidation and CO2 adsorption was considered to account for usage in real-world applications. Overall, mesoporous Pd/SiO2 aerogel shows potential as a material capable of removing CO from the environment and capturing CO2 at low temperatures.