RESUMO
Low-temperature plasma nitriding of austenitic stainless steel can ensure that its corrosion resistance does not deteriorate, improving surface hardness and wear performance. Nevertheless, it requires a longer processing time. The hollow cathode discharge effect helps increase the plasma density quickly while radiatively heating the workpiece. This work is based on the hollow cathode discharge effect to perform a rapid nitriding strengthening treatment on AISI 304 stainless steels. The experiments were conducted at three different temperatures (450, 475, and 500 °C) for 1 h in an ammonia atmosphere. The samples were characterized using various techniques, including SEM, AFM, XPS, XRD, and micro-hardness measurement. Potentiodynamic polarization and electrochemical impedance spectroscopy methods were employed to assess the electrochemical behavior of the different samples in a 3.5% NaCl solution. The finding suggests that rapid hollow cathode plasma nitriding can enhance the hardness, wear resistance, and corrosion properties of AISI 304 stainless steel.
RESUMO
Ti6Al4V titanium alloys, with high specific strength and good biological compatibility with the human body, are ideal materials for medical surgical implants. However, Ti6Al4V titanium alloys are prone to corrosion in the human environment, which affects the service life of implants and harms human health. In this work, hollow cathode plasm source nitriding (HCPSN) was used to generate nitrided layers on the surfaces of Ti6Al4V titanium alloys to improve their corrosion resistance. Ti6Al4V titanium alloys were nitrided in NH3 at 510 °C for 0, 1, 2, and 4 h. The microstructure and phase composition of the Ti-N nitriding layer was characterized by high-resolution transmission electron microscopy, atomic force microscopy, scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. This modified layer was identified to be composed of TiN, Ti2N, and α-Ti (N) phase. To study the corrosion properties of different phases, the nitriding 4 h samples were mechanically ground and polished to obtain the various surfaces of Ti2N and α-Ti (N) phases. The potentiodynamic polarization and electrochemical impedance measurements were conducted in Hank's solution to characterize the corrosion resistance of Ti-N nitriding layers in the human environment. The relationship between corrosion resistance and the microstructure of the Ti-N nitriding layer was discussed. The new Ti-N nitriding layer that can improve corrosion resistance provides a broader prospect for applying Ti6Al4V titanium alloy in the medical field.