The eCO2RR activity is correlated to the internal structural character of the catalyst. We employed two types of structural models of porphyrin-based MOFs of PCN-222(Cu) and PCN-224(Cu) into heterogeneous catalysis to illustrate the effect of structural factors on the eCO2RR performance. The composite catalyst PCN-222(Cu)/C displays better activity and selectivity (η = 450 mV, FEHCOOH = 44.3%, j = 3.2 mA cm-2) than PCN-224(Cu)/C (η = 450 mV, FEHCOOH = 34.1%, j = 2.4 mA cm-2) for the CO2 reduction to HCOOH in the range of -0.7--0.9 V (vs. RHE) due to its higher BET surface area, CO2 uptake, and a larger pore diameter. It is interesting that PCN-224(Cu)/C displays better performance in the range of -0.4--0.6 V (vs. RHE) due to its greater heat of adsorption, Qst and a higher affinity for CO2 molecule, which could promote the capture of CO2 onto the exposed active sites. As a result, PCN-224(Cu)/C exhibits better stability for the long-term electrolysis.
RESUMO
CO2 capture, utilization, and storage are promising strategies to solving the problems of superfluous CO2 or energy shortage. Here, mechanochemical reduction of CO2 by a MgH2/CaH2 mixture was first performed, by which we achieve selective methanation of CO2 and acquire an effective CaO-based CO2 sorbent, simultaneously. The selectivity of methanation is near 100% and the yield of CH4 reaches 30%. Four MgO and carbon-doped CaO-based CO2 sorbents (MgO/CaO/C, MgO/2CaO/C, MgO/4CaO/C, and MgO/8CaO/C) were formed as solid products in these reactions. Among them, the MgO/4CaO/C sorbent shows high initial adsorption amount of 59.3 wt% and low average activity loss of 1.6% after 30 cycles. This work provides a novel, well-scalable, and sustainable approach to prepare an efficient inert additive-including CaO-based CO2 sorbent and selectively convert CO2 to CH4 at the same time.