RESUMO
Soft ionic conductors exhibit immense potential for applications in soft ionotronics, including ionic skin, human-machine interface, and soft luminescent device. Nevertheless, the majority of ionogel-based soft ionic conductors are plagued by issues such as freezing, evaporation, liquid leakage, and inadequate self-healing capabilities, thereby constraining their usability in complex environments. In this study, we present a novel strategy for fabricating conductive ionogels through the proportionally mixing cationic guar gum (CGG), water, 1-butyl-3-methylimidazolium chloride (BmimCl)/glycerol eutectic-based ionic liquid, and poly(3,4-ethylenedioxythiophene)/lignosulfonate (PEDOT/LS). The resultant benefits from strong hydrogen bonding and electrostatic interactions among its constituents, endowing it with an ultrafast self-healing capability (merely 30 s) while sustaining high electrical conductivity (~16.5 mS cm-1). Moreover, it demonstrates exceptional water retention (62 % over 10 days), wide temperature tolerance (-20 to 60 °C), and injectability. A wearable sensor fabricated from this ionogel displayed remarkable sensitivity (gauge factor = 17.75) and a rapid response to variations in strain, pressure, and temperature, coupled with both long-term stability and wide working temperature range. These attributes underscore its potential for applications in healthcare devices and flexible electronics.
Assuntos
Compostos Bicíclicos Heterocíclicos com Pontes , Condutividade Elétrica , Galactanos , Géis , Lignina , Mananas , Gomas Vegetais , Polímeros , Gomas Vegetais/química , Galactanos/química , Mananas/química , Polímeros/química , Lignina/química , Lignina/análogos & derivados , Géis/química , Compostos Bicíclicos Heterocíclicos com Pontes/química , Dispositivos Eletrônicos Vestíveis , Cátions/química , Congelamento , HumanosRESUMO
This study aimed to prepare a new bio-based chromium-free tanning agent. The green epoxide monocase ethylene glycol diglycidyl ether (EGDE) was grafted with tannic acid (TA) derived from natural plant using the one-pot method to synthesize new plant polyphenol-derived tannic acid-based chromium-free tanning agents (TA-EGDE) with abundant terminal epoxides. FTIR, 1H NMR, XPS, GPC, SEM, and other analytical techniques were used to characterize tanning agents. These consequences manifested that EGDE was successfully grafted with the phenol hydroxyl group of TA. The epoxide value of TA-EGDE showed a tendency to increase and then decrease with increasing EGDE dosage, and the epoxide value of TA-EGDE-2 attained a maximum of 0.262 mol/100 g. GPC analysis showed that the formula weight of the prepared TA-EGDE was partially distributed above 5000 Da. The tanning experiment demonstrated that the shrinkage temperatures (Ts) of the TA-EGDE-tanned leathers were all higher than 81.5 °C. Compared with the traditional commercial chromium-free tanning agent (F-90, TWS), TA-EGDE-tanned leathers exhibited higher Ts and better mechanical properties. The TA-EGDE prepared in this study not only has ecological environmental protection but also provides finished leather with good moisture, heat resistance, and mechanical properties.
Assuntos
Polifenóis , Curtume , Taninos , Taninos/química , Polifenóis/química , Cromo/químicaRESUMO
The process of suspension polymerization was utilized to create acrylate resin microspheres with mesh numbers of 140-200 µm and particle sizes of 100 µm for implementation in mesh coating technology. The copolymer of methyl methacrylate (MMA) and methyl acrylate (MA) served as the primary polymer, with dibenzoyl peroxide (DBPO) functioning as the initiator, and a mixture of calcium carbonate and deionized water served as the dispersion medium. The surface morphology of the synthesized microspheres was analyzed through Fourier-transform infrared (FTIR) spectroscopy and scanning electron microscopy (SEM) to confirm successful synthesis. The optimal reaction conditions for the synthesis of these microspheres were determined to be a dispersant dosage of 30 g of calcium carbonate with a monomer ratio of 4:1, a reaction time of 1 h, an initiator dosage of 1.2 g of BPO, and a reaction temperature of approximately 75-80 C, resulting in microspheres with a regular spherical shape and smooth surface.