The use of ionic liquids (ILs) as corrosion inhibitors gained attention due to their attractive properties such as high inhibition efficiency and ability to absorb onto metal surfaces. In this work, six ILs, based on the coumarate anion combined with different nitrogen cations (triethylammonium, pyrrolidinium and imidazolium with short and long alkyl chain attached to the nitrogen atom) have been synthesized and evaluated as inhibitors for steel. The anticorrosion properties of these ILs in solution were investigated electrochemically and the metal surface was analyzed by SEM. Moreover, the IL prepared from the coumarate anion and N-dimethyl-N-tetradecyl ammonium ([DTA]Cou) was incorporated into an UV-coating formulation as an additive and by designing a similar ionic monomer which covalently links to the formulation. Impedance spectroscopy during 11 days of exposure to a solution of NaCl 0,01M, confirmed the high performance of the inhibitor in both solution and when incorporated into a coating. The synthesized ILs present efficiencies in solution exceeding 70%, in particular the ILs [DTA]Cou and tetradecyl imidazolium coumarate ([C14Im]Cou) showed efficiencies of 88% and 91% respectively. The obtained inhibitors showed interesting anticorrosion behaviors and demonstrated how different cations and an increase in the chain length affect the inhibition properties.
RESUMO
A set of ionic quasi-block copolymers were investigated to determine the effects of their composition and structure on their performance in their application as solid-state battery electrolytes. Diffusion and electrochemical tests have shown that these new quasi-block electrolytes have comparable performance to traditional block copolymers reaching ionic conductivities of 3.8 × 10-4 S cm-1 and lithium-ion diffusion of 4.6 × 10-12 m2 s-1 at 80 °C. It was illustrated that the mechanical properties of each quasi-block electrolyte are highly dependent on the order of monomer addition in polymer synthesis while the phase morphology hints at each of the quasi-blocks' unique compositional make up.
RESUMO
This Perspective aims to present the current status and future opportunities for polymer science in battery technologies. Polymers play a crucial role in improving the performance of the ubiquitous lithium ion battery. But they will be even more important for the development of sustainable and versatile post-lithium battery technologies, in particular solid-state batteries. In this article, we identify the trends in the design and development of polymers for battery applications including binders for electrodes, porous separators, solid electrolytes, or redox-active electrode materials. These trends will be illustrated using a selection of recent polymer developments including new ionic polymers, biobased polymers, self-healing polymers, mixed-ionic electronic conducting polymers, inorganic-polymer composites, or redox polymers to give some examples. Finally, the future needs, opportunities, and directions of the field will be highlighted.
RESUMO
Metal-air batteries are an emerging technology with great potential to satisfy the demand for energy in high-consumption applications. However, this technology is still in an early stage, facing significant challenges such as a low cycle life that currently limits its practical use. Poly(3,4-ethylenedioxythiophene) (PEDOT) conducting polymer has already demonstrated its efficiency as catalyst for oxygen reduction reaction (ORR) discharge as an alternative to traditional expensive and nonsustainable metal catalysts. Apart from that, in most electrochemical processes, three phenomena are needed: redox activity and electronic and ionic conduction. Material morphology is important to maximize the contact area and optimize the 3 mechanisms to obtain high-performance devices. In this work, porous scaffolds of PEDOT-organic ionic plastic crystal (OIPC) are prepared through vapor phase polymerization to be used as porous self-standing cathodes. The scaffolds, based on abundant elements, showed good thermal stability (200 °C), with potential ORR reversible electrocatalytic activity: 60% of Coulombic efficiency in aqueous medium after 200 cycles.
RESUMO
Solid polymer electrolytes that combine both a high lithium-ion transference number and mechanical properties at high temperatures are searched for improving the performance of batteries. Here, we show a salt-free all-polymer nanocomposite solid electrolyte for lithium metal batteries that improves the mechanical properties and shows a high lithium-ion transference number. For this purpose, lithium sulfonamide-functionalized poly(methyl methacrylate) nanoparticles (LiNPs) of very small size (20-30 nm) were mixed with poly(ethylene oxide) (PEO). The morphology of all-polymer nanocomposites was first investigated by transmission electron microscopy (TEM), showing a good distribution of nanoparticles (NPs) even at high contents (50 LiNP wt %). The crystallinity of PEO was investigated in detail and decreased with the increasing concentration of LiNPs. The highest ionic conductivity value for the PEO 50 wt % LiNP nanocomposite at 80 °C is 1.1 × 10-5 S cm-1, showing a lithium-ion transference number of 0.68. Using dynamic mechanic thermal analysis (DMTA), it was shown that LiNPs strengthen PEO, and a modulus of ≈108 Pa was obtained at 80 °C for the polymer nanocomposite. The nanocomposite solid electrolyte was stable with respect to lithium in a Li||Li symmetrical cell for 1000 h. In addition, in a full solid-state battery using LiFePO4 as the cathode and lithium metal as the anode, a specific capacity of 150 mAhg-1 with a current density of 0.05 mA cm-2 was achieved.
RESUMO
The increasing demands for sustainable energy storage technologies have prompted extensive research in the development of eco-friendly materials for lithium-ion batteries (LIBs). This research article presents the design of biobased latexes, which are fluorine-free and rely on renewable resources, based on isobornyl methacrylate (IBOMA) and 2-octyl acrylate (2OA) to be used as binders in batteries. Three different compositions of latexes were investigated, varying the ratio of IBOMA and 2OA: (1) Poly2OA homopolymer, (2) Poly(2OA0,6-co-IBOMA0,4) random copolymer, and (3) PolyIBOMA homopolymer. The combination of the two monomers provided a balance between rigidity from the hard monomer (IBOMA) and flexibility from the soft one (2OA). The study evaluated the performance of the biobased latexes using sodium carboxymethyl cellulose (CMC) as a thickener and cobinder by fabricating LiNi0.8Mn0.1Co0.1O2 (NMC 811) cathodes. Also, to compare with the state of the art, organic processed PVDF electrodes were prepared. Among aqueous slurries, rheological analysis showed that the CMC + Poly(2OA0,6-co-IBOMA0,4) binder system resulted in the most stable and well-dispersed slurries. Also, the electrodes prepared with this latex demonstrated enhanced adhesion (210 ± 9 N m-1) and reduced cracks compared to other aqueous compositions. Electrochemical characterization revealed that the aqueous processed cathodes using the CMC + Poly(2OA0,6-co-IBOMA0,4) biobased latex displayed higher specific capacities than the control with no latex at high C-rates (100.3 ± 2.1 vs 64.5 ± 0.8 mAh g-1 at 5C) and increased capacity retention after 90 cycles at 0.5C (84% vs 81% for CMC with no latex). Overall, the findings of this study suggest that biobased latexes, specifically the CMC + Poly(2OA0,6-co-IBOMA0,4) composition, are promising as environmentally friendly binders for NMC 811 cathodes, contributing to the broader goal of achieving sustainable energy storage systems.
RESUMO
Metallic lithium (Li) is the most attractive anode for Li batteries because it holds the highest theoretical specific capacity (3860 mA h g-1) and the lowest redox potential (-3.040 V vs SHE). However, the poor interface stability of the Li anode, which is caused by the high reactivity and dendrite formation of metallic Li upon cycling, leads to undesired electrochemical performance and safety issues. While two-dimensional boron nitride (BN) nanosheets have been utilized as an interfacial layer, the mechanism on how they stabilize the Li-electrolyte interface remains elusive. Here, we show how BN nanosheet interlayers suppress Li dendrite formation, enhance Li ion transport kinetics, facilitate Li deposition, and reduce electrolyte decomposition. We show through both simulation and experimental data that the desolvation process of a solvated Li ion within the interlayer nanochannels kinetically favors Li deposition. This process enables long cycling stability, reduced voltage polarization, improved interface stability, and negligible volume expansion. Their application as an interfacial layer in symmetric cells and full cells that display significantly improved electrochemical properties is also demonstrated. The knowledge gained in this study provides both critical insights and practical guidelines for designing a Li metal anode with significantly improved performance.
RESUMO
Solid polymer electrolytes (SPEs) have emerged as promising candidates for sodium-based batteries due to their cost-effectiveness and excellent flexibility. However, achieving high ionic conductivity and desirable mechanical properties in SPEs remains a challenge. In this study, we investigated an AB diblock copolymer, PS-PEA(BuImTFSI), as a potential SPE for sodium batteries. We explored binary and ternary electrolyte systems by combining the polymer with salt and [C3mpyr][FSI] ionic liquid (IL) and analyzed their thermal and electrochemical properties. Differential scanning calorimetry revealed phase separation in the polymer systems. The addition of salt exhibited a plasticizing effect localized to the polyionic liquid (PIL) phase, resulting in an increased ionic conductivity in the binary electrolytes. Introducing the IL further enhanced the plasticizing effect, elevating the ionic conductivity in the ternary system. Spectroscopic analysis, for the first time, revealed that the incorporation of NaFSI and IL influences the conformation of TFSI- and weakens the interaction between TFSI- and the polymer. This establishes correlations between anions and Na+, ultimately enhancing the diffusivity of Na ions. The electrochemical properties of an optimized SPE in Na/Na symmetrical cells were investigated, showcasing stable Na plating/stripping at high current densities up to 0.7 mA cm-2, maintaining its integrity at 70 °C. Furthermore, we evaluated the performance of a Na|NaFePO4 cell cycled at different rates (C/10 and C/5) and temperatures (50 and 70 °C), revealing remarkable high-capacity retention and Coulombic efficiency. This study highlights the potential of solvent-free diblock copolymer electrolytes for high-performance sodium-based energy storage systems, contributing to advanced electrolyte materials.
RESUMO
Hybrid solid electrolytes (HSEs), namely mixtures of polymer and inorganic electrolytes, have supposedly improved properties with respect to inorganic and polymer electrolytes. In practice, HSEs often show ionic conductivity below expectations, as the high interface resistance limits the contribution of inorganic electrolyte particles to the charge transport process. In this study, the transport properties of a series of HSEs containing Li(1+ x ) Alx Ti(2- x ) (PO4 )3 (LATP) as Li+ -conducting filler are analyzed. The occurrence of Li+ exchange across the two phases is proved by isotope exchange experiment, coupled with 6 Li/7 Li nuclear magnetic resonance (NMR), and by 2D 6 Li exchange spectroscopy (EXSY), which gives a time constant for Li+ exchange of about 50 ms at 60 °C. Electrochemical impedance spectroscopy (EIS) distinguishes a short-range and a long-range conductivity, the latter decreasing with LATP concentration. LATP particles contribute to the overall conductivity only at high temperatures and at high LATP concentrations. Pulsed field gradient (PFG)-NMR suggests a selective decrease of the anions' diffusivity at high temperatures, translating into a marginal increase of the Li+ transference number. Although the transport properties are only marginally affected, addition of moderate amounts of LATP to polymer electrolytes enhances their mechanical properties, thus improving the plating/stripping performance and processability.
RESUMO
Sodium-air batteries (SABs) are receiving considerable attention for the development of next generation battery alternatives due to their high theoretical energy density (up to 1105 W h kg-1). However, most of the studies on this technology are still based on organic solvents; in particular, diglyme, which is highly flammable and toxic for the unborn child. To overcome these safety issues, this research investigates the first use of a branched ether solvent 1,2,3-trimethoxypropane (TMP) as an alternative electrolyte to diglyme for SABs. Through this work, the reactivity of the central tertiary carbon in TMP towards bare sodium metal was identified, while the addition of N-butyl-N-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide ([C4mpyr][TFSI]) as a co-solvent proved to be an effective strategy to limit the reactivity. Moreover, a Na-ß-alumina disk was employed for anode protection, to separate the TMP-based electrolyte from the sodium metal. The new cell design resulted in improved cell performance: discharge capacities of up to 1.92 and 2.31 mA h cm-2 were achieved for the 16.6 mol% NaTFSI in TMP and 16.6 mol% NaTFSI in TMP/[C4mpyr][TFSI] compositions, respectively. By means of SEM, Raman and 23Na NMR techniques, NaO2 cubes were identified to be the major discharge product for both electrolyte compositions. Moreover, the hybrid electrolyte was shown to hinder the formation of side-products during discharge - the ratio of NaO2 to side-products in the hybrid electrolyte was 2.4 compared with 0.8 for the TMP-based electrolyte - and a different charge mechanism for the dissolution of NaO2 cubes for each electrolyte was observed. The findings of this work demonstrate the high potential of TMP as a base solvent for SABs, and the importance of careful electrolyte composition design in order to step towards greener and less toxic batteries.
RESUMO
Membrane-based gas separation technologies are one solution towards mitigating global emissions of CO2. New membrane materials with improved separation performance are still highly sought after. Composite membranes based on organic ionic plastic crystals (OIPCs) have shown preferential interaction for CO2 over N2, leading in some cases to competitive CO2/N2 selectivities. However, these ionic materials have been scarcely studied in the field of gas separation. Here, OIPCs based on the bis(trifluoromethylsulfonyl)imide ([TFSI]-) anion were investigated for use as gas separation membranes for the first time. The effect of the polymer type was also investigated, through the comparison of poly(vinylidene fluoride) (PVDF) and poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP) OIPC membranes. A strong temperature dependence of the gas separation performance was found, particularly in the N-methyl-N-ethylpyrrolidinium-based composites where the material undergoes a solid-solid phase transition within the testing temperature range. The polymer type was noted to induce a strong effect on the structure of the composites, as well as affecting the gas and ionic transport. Thus, this research provides insights on the influence of the [TFSI]- anion on the structure and separation properties of OIPC-based composites, and new information towards the development of novel OIPC-based membranes with enhanced gas separation performance.
RESUMO
Fabricating highly efficient and long-life redox bifunctional electrocatalysts is vital for oxygen-related renewable energy devices. To boost the bifunctional catalytic activity of Fe-N-C single-atom catalysts, it is imperative to fine-tune the coordination microenvironment of the Fe sites to optimize the adsorption/desorption energies of intermediates during oxygen reduction/evolution reactions (ORR/OER) and simultaneously avoid the aggregation of atomically dispersed metal sites. Herein, a strategy is developed for fabricating a free-standing electrocatalyst with atomically dispersed Fe sites (≈0.89 wt.%) supported on N, F, and S ternary-doped hollow carbon nanofibers (FeN4 -NFS-CNF). Both experimental and theoretical findings suggest that the incorporation of ternary heteroatoms modifies the charge distribution of Fe active centers and enhances defect density, thereby optimizing the bifunctional catalytic activities. The efficient regulation isolated Fe centers come from the dual confinement of zeolitic imidazole framework-8 (ZIF-8) and polymerized ionic liquid (PIL), while the precise formation of distinct hierarchical three-dimensional porous structure maximizes the exposure of low-doping Fe active sites and enriched heteroatoms. FeN4 -NFS-CNF achieves remarkable electrocatalytic activity with a high ORR half-wave potential (0.90 V) and a low OER overpotential (270 mV) in alkaline electrolyte, revealing the benefit of optimizing the microenvironment of low-doping iron single atoms in directing bifunctional catalytic activity.
RESUMO
Organic ionic plastic crystals (OIPCs) are attractive solid electrolyte materials for advanced energy storage systems owing to their inherent advantages (e.g., high plasticity, thermal stability, and moderate ionic conductivity), which can be further improved/deteriorated by the addition of polymer or metal oxide nanoparticles. The role of the nanoparticle/OIPC combinations on the resultant interphase structure and transport properties, however, is still unclear due to the complexity within the composite structures. Herein, we demonstrate a systematic approach to specifically interrogating the interphase region by fabricating layered OIPC/polymer thin films via spin coating and correlating variation in the ionic conductivity of the OIPC with their microscopic structures. In-plane interdigitated electrodes have been employed to obtain electrochemical impedance spectroscopy (EIS) spectra on both OIPC and layered OIPC/polymer thin films. The thin-film EIS measurements were evaluated with conventional bulk EIS measurements on the OIPC pressed pellets and compared with EIS obtained from the OIPC-polymer composites. Interactions between the OIPC and polymer films as well as the morphology of the film surfaces have been characterized through multiple microscopic analysis tools, including scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, and optical profilometry. The combination of EIS analysis with the microscopic visualization of these unique layered OIPC/polymer thin films has confirmed the impact of the OIPC-polymer interphase region on the overall ionic conductivity of bulk OIPC-polymer composites. By changing the chemistry of the polymer substrate (i.e., PMMA, PVDF, and PVDF-HFP), the importance of compatibility between the components in the interphase region is clearly observed. The methods developed here can be used to screen and further understand the interactions among composite components for enhanced compatibility and conductivity.
RESUMO
The physical properties of ionic liquids (ILs) have led to intense research interest, but for many applications, high viscosity is problematic. Mixing the IL with a diluent that lowers viscosity offers a solution if the favorable IL physical properties are not compromised. Here we show that mixing an IL or IL electrolyte (ILE, an IL with dissolved metal ions) with a nonsolvating fluorous diluent produces a low viscosity mixture in which the local ion arrangements, and therefore key physical properties, are retained or enhanced. The locally concentrated ionic liquids (LCILs) examined are 1-hexyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (HMIM TFSI), 1-hexyl-3-methylimidazolium tris(pentafluoroethyl)trifluorophosphate (HMIM FAP), or 1-butyl-3-methylimidazolium tris(pentafluoroethyl)trifluorophosphate (BMIM FAP) mixed with 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether (TFTFE) at 2:1, 1:1, and 1:2 (w/w) IL:TFTFE, as well as the locally concentrated ILEs (LCILEs) formed from 2:1 (w/w) HMIM TFSI-TFTFE with 0.25, 0.5, and 0.75 m lithium bis(trifluoromethylsulfonyl)imide (LiTFSI). Rheology and conductivity measurements reveal that the added TFTFE significantly reduces viscosity and increases ionic conductivity, and cyclic voltammetry (CV) reveals minimal reductions in electrochemical windows on gold and carbon electrodes. This is explained by the small- and wide-angle X-ray scattering (S/WAXS) and atomic force microscopy (AFM) data, which show that the local ion nanostructures are largely retained in LCILs and LCILEs in bulk and at gold and graphite electrodes for all potentials investigated.
RESUMO
High-voltage sodium batteries are an appealing solution for economical energy storage applications. Currently available electrolyte materials have seen limited success in such applications therefore the identification of high-performing and safer alternatives is urgently required. Herein we synthesise six novel ionic liquids derived from two fluoroborate anions which have shown great promise in recent battery literature. This study reports for the first time the electrochemically applicable room-temperature ionic liquid (RTIL) N-ethyl-N,N,N-tris(2-(2-methoxyethoxy)ethyl)ammonium (tetrakis)hexafluoroisopropoxy borate ([N2(2O2O1)3][B(hfip)4]). The RTIL shows promising physical properties with a very low glass-transition at -73 °C and low viscosity. The RTIL exhibits an electrochemical window of 5.3 V on a glassy carbon substrate which enables high stability electrochemical cycling of sodium in a 3-electrode system. Of particular note is the strong passivation behaviour of [N2(2O2O1)3][B(hfip)4] on aluminium current-collector foil at potentials as high as 7 V (vs. Na+/Na) which is further improved with the addition of 50 mol% Na[FSI]. This study shows [B(hfip)4]- ionic liquids have the desired physical and electrochemical properties for high-voltage sodium electrolytes.
RESUMO
Poly(vinylidene fluoride) (PVDF) is the most common binder for cathode electrodes in lithium-ion batteries. However, PVDF is a fluorinated compound and requires toxic N-methyl-2-pyrrolidone (NMP) as a solvent during the slurry preparation, making the electrode fabrication process environmentally unfriendly. In this study, we propose the use of carrageenan biopolymers as a sustainable source of water-processable binders for high-voltage NMC811 cathodes. Three types of carrageenan (Carr) biopolymers were investigated, with one, two, or three sulfonate groups (SO3-), namely, kappa, iota, and lambda carrageenans, respectively. In addition to the nature of carrageenans, this article also reports the optimization of the cathode formulations, which were prepared by using between 5 wt % of the binder to a lower amount of 2 wt %. Processing of the aqueous slurries and the nature of the binder, in terms of the morphology and electrochemical performance of the electrodes, were also investigated. The Carr binder with 3SO3- groups (3SO3-Carr) exhibited the highest discharge capacities, delivering 133.1 mAh g-1 at 3C and 105.0 mAh g-1 at 5C, which was similar to the organic-based PVDF electrode (136.1 and 108.7 mAh g-1, respectively). Furthermore, 3SO3-Carr reached an outstanding capacity retention of 91% after 90 cycles at 0.5C, which was attributed to a homogeneous NMC811 and a conductive carbon particle dispersion, superior adhesion strength to the current collector (17.3 ± 0.7 N m-1 vs 0.3 ± 0.1 N m-1 for PVDF), and reduced charge-transfer resistance. Postmortem analysis unveiled good preservation of the NMC811 particles, while the 1SO3-Carr and 2SO3-Carr electrodes showed damaged morphologies.
RESUMO
Before the debut of lithium-ion batteries (LIBs) in the commodity market, solid-state lithium metal batteries (SSLMBs) were considered promising high-energy electrochemical energy storage systems before being almost abandoned in the late 1980s because of safety concerns. However, after three decades of development, LIB technologies are now approaching their energy content and safety limits imposed by the rocking chair chemistry. These aspects are prompting the revival of research activities in SSLMB technologies at both academic and industrial levels. In this perspective article, we present a personal reflection on solid polymer electrolytes (SPEs), spanning from early development to their implementation in SSLMBs, highlighting key milestones. In particular, we discuss the SPEs' characteristics taking into account the concept of coupled and decoupled SPEs proposed by C. Austen Angell in the early 1990s. Possible remedies to improve the physicochemical and electrochemical properties of SPEs are also examined. With this article, we also aim to highlight the missing blocks in building ideal SSLMBs and stimulate research towards innovative electrolyte materials for future rechargeable high-energy batteries.
RESUMO
Corrosion is a significant problem that negatively affects a wide range of structures and buildings, resulting in their premature failure, which causes safety hazards and significant economic loss. For this reason, various approaches have been developed to prevent or minimize the effects of corrosion, including corrosion inhibitors. Recently, biobased inhibitors have gained a certain interest thanks to their unique properties, eco-friendliness, and availability. Among all the green precursors, lignin is of particular interest, being a natural polymer that can be obtained from different sources including agricultural residues. Corrosion inhibitors based on ionic liquids (ILs) also present interesting advantages, such as low volatility and high tunability. If combined, it may be possible to obtain new lignin-based ILs that present interesting corrosion inhibitor properties. In this work, the inhibition properties of new biobased lignin ILs and the influence of anions and cations on the corrosion of mild steel in an aqueous solution of 0.01 M NaCl were investigated by Potentiostatic Electrochemical Impedance Spectroscopy (PEIS) and Cyclic Potentiodynamic Polarization (CPP). Moreover, the surface was characterized using SEM, EDS, and optical profilometry. The IL choline syringate showed promising performance, reducing the corrosion current after 24 h immersion in 0.01 M sodium chloride, from 1.66 µA/cm2 for the control to 0.066 µA/cm2 with 10 mM of the IL present. In addition to its performance as a corrosion inhibitor, both components of this IL also meet or exceed the current additional desired properties of such compounds, being readily available, and well tolerated in organisms and the environment.
RESUMO
Ion adsorption within nanopores is involved in numerous applications. However, a comprehensive understanding of the fundamental relationship between in-pore ion concentration and pore size, particularly in the sub-2 nm range, is scarce. This study investigates the ion-species-dependent concentration in multilayered graphene membranes (MGMs) with tunable nanoslit sizes (0.5-1.6 nm) using nuclear magnetic resonance and computational simulations. For Na+-based electrolytes in MGMs, the concentration of anions in graphene nanoslits increases in correlation with their chaotropic properties. As the nanoslit size decreases, the concentration of chaotropic ion (BF4-) increases, whereas the concentration of kosmotropic ions (Cit3-, PO43-) and other ions (Ac-, F-) decreases or changes slightly. Notably, anions remain more concentrated than counter Na+ ions, leading to electroneutrality breakdown and unipolar anion packing in MGMs. A continuum modeling approach, integrating molecular dynamic simulation with the Poisson-Boltzmann model, elucidates these observations by considering water-mediated ion-graphene non-electrostatic interactions and charge screening from graphene walls.
RESUMO
Microorganisms do not live as dispersed single cells but rather they form aggregates with extracellular polymeric substances at interfaces. Biofilms are considered efficient life forms because they shield bacteria from biocides and collect dilute nutrients. This is a big concern in industry since the microorganisms can colonize a wide range of surfaces, accelerating material deterioration, colonizing medical devices, contaminating ultrapure drinking water, increasing energy costs and creating focus of infection. Conventional biocides that target a specific component of the bacteria are not effective in the presence of biofilms. Efficient biofilm inhibitors are based on a multitarget approach interacting with the bacteria and the biofilm matrix. Their rationale design requires a thorough understanding of inhibitory mechanisms that are still largely lacking today. Herein we uncover via molecular modelling the inhibition mechanism of cetrimonium 4-OH cinnamate (CTA-4OHcinn). Simulations show that CTA-4OH micelles can disrupt symmetric and asymmetric bilayers, representative of inner and outer bacterial membranes, following three stages: adsorption, assimilation, and defect formation. The main driving force for micellar attack is electrostatic interactions. In addition to disrupting the bilayers, the micelles work as carriers facilitating the trapping of 4OH cinnamate anions within the bilayer upper leaflet and overcoming electrostatic repulsion. The micelles also interact with extracellular DNA (e-DNA), which is one of the main components of biofilms. It is observed that CTA-4OHcinn forms spherical micelles on the DNA backbone; which hinders their ability to pack. This is demonstrated by modelling the DNA along the hbb histone-like protein, showing that in the presence of CTA-4OHcinn, DNA does not pack properly around hbb. The abilities of CTA-4OHcinn to cause cell death through membrane disruption and to disperse a mature, multi-species biofilm are also confirmed experimentally.