Poly(ethylene glycol) Diacrylate Iongel Membranes Reinforced with Nanoclays for CO2 Separation.

Despite the fact that iongels are very attractive materials for gas separation membranes, they often show mechanical stability issues mainly due to the high ionic liquid (IL) content (≥60 wt%) needed to achieve high gas separation performances. This work investigates a strategy to improve the mechanical properties of iongel membranes, which consists in the incorporation of montmorillonite (MMT) nanoclay, from 0.2 to 7.5 wt%, into a cross-linked poly(ethylene glycol) diacrylate (PEGDA) network containing 60 wt% of the IL 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ([C2mim][TFSI]). The iongels were prepared by a simple one-pot method using ultraviolet (UV) initiated polymerization of poly(ethylene glycol) diacrylate (PEGDA) and characterized by several techniques to assess their physico-chemical properties. The thermal stability of the iongels was influenced by the addition of higher MMT contents (>5 wt%). It was possible to improve both puncture strength and elongation at break with MMT contents up to 1 wt%. Furthermore, the highest ideal gas selectivities were achieved for iongels containing 0.5 wt% MMT, while the highest CO2 permeability was observed at 7.5 wt% MMT content, due to an increase in diffusivity. Remarkably, this strategy allowed for the preparation and gas permeation of self-standing iongel containing 80 wt% IL, which had not been possible up until now.

Impact on CO2/N2 and CO2/CH4 Separation Performance Using Cu-BTC with Supported Ionic Liquids-Based Mixed Matrix Membranes.

The efficient separation of gases has industrial, economic, and environmental importance. Here, we report the improvement in gas separation performance of a polyimide-based matrix (Matrimid®5218) filled with a Cu-based metal organic framework [MOF, Cu3(BTC)2] with two different ionic liquids (ILs) confined within the pores. The chosen ILs are commonly used in gas solubilization, 1-ethyl-3-methylimidazolium tetrafluoroborate ([EMIM][BF4]) and 1-Ethyl-3-methylimidazolium trifluoromethanesulfonate ([EMIM][OTf]), and the incorporation of the [EMIM][BF4]@Cu-BTC and [EMIM][OTf]@Cu-BTC composites in Matrimid®5218 proved to be an efficient strategy to improve the permeability and selectivity toward CO2/N2 and CO2/CH4 mixtures.