Bioactive polymer grafting onto titanium alloy surfaces.

Bioactive polymers bearing sulfonate (styrene sodium sulfonate, NaSS) and carboxylate (methylacrylic acid, MA) groups were grafted onto Ti6Al4V alloy surfaces by a two-step procedure. The Ti alloy surfaces were first chemically oxidized in a piranha solution and then directly subjected to radical polymerization at 70 degrees C in the absence of oxygen. The grafted surfaces were characterized by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS) and the toluidine blue colorimetric method. Toluidine blue results showed 1-5microgcm(-2) of polymer was grafted onto the oxidized Ti surfaces. Grafting resulted in a decrease in the XPS Ti and O signals from the underlying Ti substrate and a corresponding increase in the XPS C and S signals from the polymer layer. The ToF-SIMS intensities of the S(-) and SO(-) ions correlated linearly with the XPS atomic percent S concentrations and the ToF-SIMS intensity of the TiO(3)H(2)(-) ion correlated linearly with the XPS atomic per cent Ti concentration. Thus, the ToF-SIMS S(-), SO(-) and TiO(3)H(2)(-) intensities can be used to quantify the composition and amount of grafted polymer. ToF-SIMS also detected ions that were more characteristic of the polymer molecular structure (C(6)H(4)SO(3)(-) and C(8)H(7)SO(3)(-) from NaSS, C(4)H(5)O(2)(-) from MA), but the intensity of these peaks depended on the polymer thickness and composition. An in vitro cell culture test was carried out with human osteoblast-like cells to assess the influence of the grafted polymers on cell response. Cell adhesion after 30min of incubation showed significant differences between the grafted and ungrafted surfaces. The NaSS grafted surfaces showed the highest degree of cell adhesion while the MA-NaSS grafted surfaces showed the lowest degree of cell adhesion. After 4 weeks in vivo in rabbit femoral bones, bone was observed to be in direct contact with all implants. The percentage of mineralized tissue around the implants was similar for NaSS grafted and non-grafted implants (59% and 57%). The MA-NaSS grafted implant exhibited a lower amount of mineralized tissue (47%).

Modulus-dependent macrophage adhesion and behavior.

Macrophage attachment and activation to implanted materials is crucial in determining the extent of acute and chronic inflammation, and biomaterials degradation. In an effort to improve implant performance, considerable attention has centered on altering material surface chemistry to modulate macrophage behavior. In this work, the influence of the modulus of a material on the behavior of model macrophages (i.e., human promonocytic THP-1 cells) was investigated. We synthesized interpenetrating polymer network (IPN) coatings with varying moduli to test the hypothesis that lower moduli surfaces attenuate THP-1 cell attachment and activation. The surface chemistry and moduli of the IPN coatings were characterized using X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM), respectively. THP-1 cells preferentially attached to stiffer coatings of identical surface chemistry, confirming that fewer macrophages attach to lower moduli surfaces. The secretion of human TNF-alpha, IL-10, IL-8 and IL-1beta from THP-1 cells attached to the IPNs was measured to assess the concentration of both pro- and anti-inflammatory cytokines. The global amount of TNF-alpha released did not vary for IPN surfaces of different moduli; however, the amount of the pro-inflammatory cytokine IL-8 released demonstrated a biphasic response, where lower (approx. 1.4 kPa) and very high (approx. 348 kPa) moduli IPN surfaces attenuated IL-8 secretion. The different trends for TNF-alpha and IL-8 secretion highlight the complexity of the wound healing response, suggesting that there may not be a unique surface chemistry and substratum modulus combination that minimizes the pro-inflammatory cytokines produced by activated macrophages.

Bioactive poly(ethylene terephthalate) fibers and fabrics: grafting, chemical characterization, and biological assessment.

The grafting of poly(sodium styrene sulfonate) (pNaSS) onto ozone-treated poly(ethylene terephthalate) (PET) fabric surfaces was characterized by X-ray photoelectron spectroscopy and toluidine blue colorimetry. Significant amounts of pNaSS were grafted over the range of experimental conditions examined in this study (30-120 min of ozonation, reaction at 65 or 70 degrees C, and reaction times up to 240 min). Within these ranges the amount of grafted pNaSS increased with both ozonation time and reaction temperature. The amount of grafted pNaSS increased over the first 60 min of reaction, then remained relatively constant from 60 to 240 min. For the biological experiments pNaSS-grafted samples were prepared with 30 min of ozonation and 60 min of reaction at a grafting temperature of 70 degrees C. The ozonation time was limited to 30 min to minimize any possible degradation of the PET fabrics by the ozonation treatment. The pNaSS-grafted PET surface adsorbed a factor of 4 more compared to the nongrafted surfaces. The strength of fibroblast adhesion was an order of magnitude higher on pNaSS-grafted PET fabrics compared to that on nongrafted PET fabrics. This difference in the cell attachment was correlated to the cell spreading, which was better and more homogeneous on the grafted fibers compared to the nongrafted fibers. Fibroblasts adhered more strongly on surfaces precoated with normal human plasma compared to surfaces precoated with 10% fetal calf serum in Dulbecco's modified Eagle's medium.

Radical graft polymerization of styrene sulfonate on poly(ethylene terephthalate) films for ACL applications: "grafting from" and chemical characterization.

The purpose of this study is to develop a reliable method of functionalizing poly(ethylene terephthalate) with bioactive polymers to produce a "biointegrable" artificial anterior cruciate ligament. Radical graft polymerization of the sodium salt of styrene sulfonate (NaSS) onto poly(ethylene terephthalate) (PET) films was performed using the "grafting from" technique. Prior to the grafting, the surfaces of poly(ethylene terephthalate) films were activated by ozonation to generate peroxide and hydroperoxide reactive species on the PET film surfaces. The radical polymerization of NaSS was initiated by thermal decomposition of the hydroperoxides. The grafted PET surfaces were characterized by a toluidin blue colorimetric method, X-ray photoelectron spectroscopy, contact angle measurements, and atomic force microscopy. The influence of ozonation time, monomer concentration, and temperature on NaSS grafting ratios was examined. A total of 30 min of ozonation followed by grafting from a 15% NaSS solution at 70 degrees C for 90 min or more resulted in attachment of poly(NaSS) chains to the PET film surfaces.

Development and characterization of a high-throughput system for assessing cell-surface receptor-ligand engagement.

A nonfouling interfacial interpenetrating polymer network (IPN) of poly(acrylamide-co-ethylene glycol/acrylic acid) [p(AAm-co-EG/AAc)] was grafted to polystyrene for use as a novel platform for the development of high-throughput assays for screening of specific bimolecular interactions (i.e., receptor-ligand engagement). For the development of the IPN, a water-soluble hydrogen-abstracting photoinitiator was investigated: (4-benzoylbenzyl)trimethylammonium chloride. IPN-modified polystyrene surfaces were characterized using XPS, contact angle goniometry, and protein adsorption analysis. These IPN surfaces minimized fibrinogen adsorption compared to tissue culture polystyrene (>96% reduction), prevented mammalian cell adhesion, and served as nonfouling surfaces to graft biological ligands. For bimolecular interaction studies, a model peptide ligand from bone sialoprotein (Ac-CGGNGEPRGDTYRAY-NH(2)) was grafted to p(AAm-co-EG/AAc) via a 3400 M(w) linear pEG spacer. Ligand density measurements, cell culture, and a centrifugal adhesion assay were used to study cell adhesion to peptide-modified IPNs (i.e., receptor-ligand engagement). Ligand density (Gamma) was controllable from approximately 1 to 20 pmol/cm(2) by modulating the peptide input concentration (0.02-20 microM). Cell adhesion was directly dependent on the ligand density. This technology creates a powerful high-throughput system to simultaneously probe a myriad of cell-surface receptor-ligand interactions.