Optimizing Crystal Orientation and Defect Mitigation in Antimony Selenide Thin-Film Solar Cells through Buffer Layer Energy Band Adjustment.

Antimony selenide (Sb2Se3) has sparked significant interest in high-efficiency photovoltaic applications due to its advantageous material and optoelectronic properties. In recent years, there has been considerable development in this area. Nonetheless, defects and suboptimal [hk0] crystal orientation expressively limit further device efficiency enhancement. This study used Zinc (Zn) to adjust the interfacial energy band and strengthen carrier transport. For the first time, it is discovered that the diffusion of Zn in the cadmium sulfide (CdS) buffer layer can affect the crystalline orientation of the Sb2Se3 thin films in the superstrate structure. The effect of Zn diffusion on the morphology of Sb2Se3 thin films with CdxZn1-xS buffer layer has been investigated in detail. Additionally, Zn doping promotes forming Sb2Se3 thin films with the desired [hk1] orientation, resulting in denser and larger grain sizes which will eventually regulate the defect density. Finally, based on the energy band structure and high-quality Sb2Se3 thin films, this study achieves a champion power conversion efficiency (PCE) of 8.76%, with a VOC of 458 mV, a JSC of 28.13 mA cm-2, and an FF of 67.85%. Overall, this study explores the growth mechanism of Sb2Se3 thin films, which can lead to further improvements in the efficiency of Sb2Se3 solar cells.

Enhancement in the Efficiency of Sb2 Se3 Solar Cells by Triple Function of Lithium Hydroxide Modified at the Back Contact Interface.

The efficiency of antimony selenide (Sb2 Se3 ) solar cells is still limited by significant interface and deep-level defects, in addition to carrier recombination at the back contact surface. This paper investigates the use of lithium (Li) ions as dopant for Sb2 Se3 films, using lithium hydroxide (LiOH) as a dopant medium. Surprisingly, the LiOH solution not only reacts at the back surface of the Sb2 Se3 film but also penetrate inside the film along the (Sb4 Se6 )n molecular chain. First, the Li ions modify the grain boundary's carrier type and create an electric field between p-type grain interiors and n-type grain boundary. Second, a gradient band structure is formed along the vertical direction with the diffusion of Li ions. Third, carrier collection and transport are improved at the surface between Sb2 Se3 and the Au layer due to the reaction between the film and alkaline solution. Additionally, the diffusion of Li ions increases the crystallinity, orientation, surface evenness, and optical electricity. Ultimately, the efficiency of Sb2 Se3 solar cells is improved to 7.57% due to the enhanced carrier extraction, transport, and collection, as well as the reduction of carrier recombination and deep defect density. This efficiency is also a record for CdS/Sb2 Se3 solar cells fabricated by rapid thermal evaporation.