RESUMO
OBJECTIVE: To develop a novel delivery system by which fluoride incorporated into elastomeric rings, such as those used to ligate orthodontic wires, will be released in a controlled and constant manner. MATERIALS AND METHODS: Polyethylene co-vinyl acetate (PEVA) was used as the model elastomer. Samples (N = 3) were prepared by incorporating 0.02 to 0.4 g of sodium fluoride (NaF) into previously prepared PEVA solution. Another group of samples prepared in the same manner were additionally dip-coated in PEVA to create an overcoat. Fluoride release studies were conducted in vitro using an ion selective electrode over a period of 45 days. The amount of fluoride released was compared to the optimal therapeutic dose of 0.7 microg F(-)/ring/d. RESULTS: Only coated samples with the highest fluoride content (group D, 0.4 g of NaF) were able to release fluoride at therapeutic levels. When fluoride release from coated and uncoated samples with the same amount of NaF were compared, it was shown that the dip-coating technique resulted in a fluoride release in a controlled manner while eliminating the initial burst effect. CONCLUSIONS: This novel fluoride delivery matrix provided fluoride release at a therapeutically effective rate and profile.
Assuntos
Cariostáticos/administração & dosagem , Materiais Revestidos Biocompatíveis , Sistemas de Liberação de Medicamentos , Elastômeros/química , Aparelhos Ortodônticos , Fluoreto de Sódio/administração & dosagem , Cárie Dentária/prevenção & controle , Fluoretos/análise , Desenho de Aparelho Ortodôntico , Polietilenos , PolivinilRESUMO
Submicrometer particles of diethyl p-phenylenediacrylate (EPA) with tunable molecular adsorption characteristics were produced by solid-state photopolymerization in the presence of template molecules. EPA monomer particles were produced by rapid expansion of supercritical solutions (RESS), and deposited directly onto surface acoustic wave (SAW) resonators. The EPA particles were photopolymerized directly on the SAW devices in the presence of molecular templates, and dynamic sorption isotherms of C1- through C9-alkanes were studied to characterize the particle-vapor interaction. The mass increase due to vapor uptake into the particulate coatings was measured by monitoring the SAW resonance frequency during vapor sorption. The vapor selectivity and molecular porosity of the particulate coatings were studied in situ on the piezoelectric substrate by measuring sorption isotherms. A gradual exclusion of smaller alkane molecules from the molecularly imprinted particulate coatings was observed with decreasing template molecule size. The observed selective and reversible adsorption of alkane analytes with different molecular sizes suggest that these imprinted polymers may be categorized as organic analogues of zeolites.