An O/N/S-rich porous Fe-based metal-organic framework (MOF) for gold recovery from the aqueous phase with excellent performance.

Recovering gold from wastewater has both economic and environmental benefits. However, how to effectively recover it is challenging. In this work, a novel Fe-based metal-organic framework (MOF) was synthesized and decorated with 2,5-thiophenedicarboxylic acid to have a well-developed porous architecture to effectively recover Au(III) from water. The maximum Au(III) sorption capacity by the finally-synthesized porous material MIL-101(Fe)-TDCA reached 2350 mg/g at pH = 6.00 ± 0.15, which is one of the highest among all literature-reported relevant materials including MOFs, and high sorption strength can be maintained within a wide pH range from 2.0 to 10.0. Besides, Au(III) sorption efficiency at low concentrations (i.e., 3.5 × 104 mg/mL) reached over 99%. Mechanically, outstanding Au(III) sorption by MIL-101(Fe)-TDCA resulted from the O/N/S-containing moieties on its surface, large surface area and porosity. The N- and S-containing functionalities (CS, CONH) served as electron donors to chelate Au(III). The O-containing (FeOFe, COFe, COOH, and coordinated H2O) and N-containing (CONH) moieties on MIL-101(Fe)-TDCA interacted with OH groups on the hydrolyzed species of Au(III) (AuCl3(OH)-, AuCl2(OH)2-, and AuCl(OH)3-) by hydrogen bond, which further increased Au(III) sorption. Furthermore, about 45.71% of Au(III) was reduced to gold nanoparticles by CS groups on the decorated 2,5-dithiophene dicarboxylic acid during sorption on MIL-101(Fe)-TDCA. Over 98.35% of Au(III) was selectively sorbed on MIL-101(Fe)-TDCA at pH 4.0, much higher than that of the coexisting heavy metal ions including Cu(II), Zn(II), Pb(II), and Ni(II) (< 5%), despite their same concentration at 0.01 mg/mL. Although sorption selectivity of a noble metal Pt(IV) by MIL-101(Fe)-TDCA is relatively poor (68.23%), it could be acceptable. Moreover, reusability of MIL-101(Fe)-TDCA is also excellent, since above 90.5% Au(III) still can be sorbed after two sorption-desorption cycles. Overall, excellent sorption performance and the roughly-calculated gold recycling benefits (26.30%) highlight that MIL-101(Fe)-TDCA is a promising porous material for gold recovery from the aqueous phase.

Photoassisted degradation of 2,2',4,4'-tetrabrominated diphenyl ether in simulated soil washing system containing Triton X series surfactants.

This study aims to use ultraviolet (UV) irradiation to decompose polybrominated diphenyl ethers (PBDEs) in the elutes and then reuse the surfactants. The results indicate that UV can remove 2,2',4,4'-tetrabrominated diphenyl ether (BDE-47) from surfactant eluents and Triton X series surfactants also can remove BDE-47 from the soil. Triton X-100 (TX-100) is the most promising surfactant during the washing and photodegradation processes. Quench experiments suggest that both 1O2 and OH• were involved in the TX-100 decomposition but only 1O2 is responsible for the degradation of BDE-47. In analysis of the photoproducts of BDE-47 by Gas Chromatography Mass Spectrum (GC-MS) and Liquid Chromatography High Resolution Mass Spectrometry (LC-HRMS), BDE-47 was mainly debrominated to the lower-brominated BDEs and then oxidized to ring-opening products. The little loss of TX-100 can mainly be attributed to the breakage of polyethylene oxide (PEO) chain. Nevertheless, the washing wastes treated by UV light can exhibit higher solubility for BDE-47 than before, indicating they can be reused for BDE-47 removal from soil. The toxicity assessment experiments were performed using Escherichia coli (E.coli) as an indicator. The results indicate that the removal of BDE-47 by UV irradiation can reduce the toxicity of eluent.

Photonic nanowires directly drawn from bulk glasses.

High-uniform nanowires with diameters down to 50 nm are directly taper-drawn from bulk glasses. Typical loss of these wires goes down to 0.1 dB/mm for single-mode operation. Favorable photonic properties such as high index for tight optical confinement in tellurite glass nanowires and photoluminescence for active devices in doped fluoride and phosphate glass nanowires are observed. Supporting high-index tellurite nanowires with solid substrates (such as silica glass and MgF2 crystal) and assembling low-loss microcoupler with these wires are also demonstrated. Photonic nanowires demonstrated in this work may open up vast opportunities for making versatile building blocks for future micro- and nanoscale photonic circuits and components.

High-temperature sustainability of strong fiber Bragg gratings written into Sb-Ge-codoped photosensitive fiber: decay mechanisms involved during annealing.

An antimony--germanium- (Sb--Ge-) codoped fiber specially designed for the fabrication of fiber Bragg gratings (FBGs) with high temperature sustainability has been developed. The photosensitivity and the high-temperature sustainability of FBGs that have been written into this fiber were tested. The results obtained showed that the FBG written into this fiber has a very high temperature sustainability of 900 degrees C. A decay mechanism that involves cation hopping is presented to explain the observed high temperature sustainability of the grating written into this fiber.