Electrochemical behavior, biocompatibility and mechanical performance of biodegradable iron with PEI coating.

Coating of the biodegradable metals represents an effective way of modification of their properties. Insufficient biological, mechanical, or degradation performance of pure metals may be enhanced when the proper type of organic polymer coating is used. In our previous work, the significant effect of the polyethyleneimine (PEI) coating not only on the rate but also on the type of corrosion was discovered. To bring a comprehensive overview of the Fe-PEI system performance, iron-based biodegradable scaffolds with polyethyleneimine coating were studied and their cytocompatibility and hemocompatibility, and mechanical properties were evaluated and discussed in this work. Electrochemical impedance spectroscopy (EIS) measurements were conducted for further study of material behavior. Biological analyses (MTS assay, fluorescent imaging, hemocompatibility tests) showed better cell proliferation on the surface of Fe-PEI samples but not sufficient overall cytocompatibility. Good anti-platelet adhesion properties but higher hemolysis when compared to the pure iron was also observed for the coated samples. Mechanical properties of the prepared Fe-PEI material were enhanced after coating. These findings suggest that the Fe-PEI may be an interesting potential biomaterial after further composition optimization resulting in lower cytotoxicity and better hemocompatibility.

Degradation Performance of Open-Cell Biomaterials from Phosphated Carbonyl Iron Powder with PEG Coating.

Advances in biomedicine and development of modern technologies in the last century have fostered the improvement in human longevity and well-being. This progress simultaneously initiated the need for novel biomaterials. Recently, degradable metallic biomaterials have attracted serious attention in scientific and clinical research owing to their utilization in some specific applications. This work investigates the effect of the polyethylene glycol (PEG) coating of open-cell iron and phosphorus/iron foams on their microstructure and corrosion properties. The addition of phosphorus causes a slight increase in pore size and the deposition of a polymer coating results in a smoothened surface and a moderate decrease in pore diameter. The PEG coating leads to an increase in corrosion rates in both foams and potentially a more desirable product.

In Vitro Corrosion Behavior of Biodegradable Iron Foams with Polymeric Coating.

Research in the field of biodegradable metallic scaffolds has advanced during the last decades. Resorbable implants based on iron have become an attractive alternative to the temporary devices made of inert metals. Overcoming an insufficient corrosion rate of pure iron, though, still remains a problem. In our work, we have prepared iron foams and coated them with three different concentrations of polyethyleneimine (PEI) to increase their corrosion rates. Scanning electron microscopy (SEM) coupled with energy dispersive X-ray analysis (EDX), Fourier-transform infrared spectroscopy (FT-IR), and Raman spectroscopy were used for characterization of the polymer coating. The corrosion behavior of the powder-metallurgically prepared samples was evaluated electrochemically using an anodic polarization method. A 12 weeks long in vitro degradation study in Hanks' solution at 37 °C was also performed. Surface morphology, corrosion behavior, and degradation rates of the open-cell foams were studied and discussed. The use of PEI coating led to an increase in the corrosion rates of the cellular material. The sample with the highest concentration of PEI film showed the most rapid corrosion in the environment of simulated body fluids.

A study of cytocompatibility and degradation of iron-based biodegradable materials.

Biodegradable metallic implants are of significant importance in the replacement of bones or the repair of bone defects. Iron-phosphate-coated carbonyl iron powder (Fe/P) was prepared by the phosphating method. Moreover, Fe/P-Mn alloy was produced by sintering the Fe/P powder mixed with manganese powder. Bare carbonyl iron samples and the Fe/P and Fe/P-Mn sintered samples were evaluated for their microstructure, cytotoxicity, and hemocompatibility. The microstructure of the sintered samples was examined using an optical microscope and scanning electron microscopic analysis. Corrosion behavior was evaluated by potentiodynamic polarization in Hank's solution. The in vitro biocompatibilities were investigated by cytotoxicity and hemolysis tests. The results obtained demonstrate that the addition of Mn resulted in higher surface inhomogeneity, porosity and roughness as well as in increased cytotoxicity. The phosphate coating has a moderately negative effect on the cytotoxicity. The corrosion rates determined from Tafel diagrams were ordered in the following sequence: Fe/P-Mn, Fe, Fe/P from high to low. The hemocompatibility of experimental samples was ordered in the following sequence: Fe/P, Fe/P-Mn, Fe from high to low. All samples were found to be hemocompatible.