Single-crystalline chromium silicide nanowires and their physical properties.

In this work, chromium disilicide nanowires were synthesized by chemical vapor deposition (CVD) processes on Si (100) substrates with hydrous chromium chloride (CrCl3 · 6H2O) as precursors. Processing parameters, including the temperature of Si (100) substrates and precursors, the gas flow rate, the heating time, and the different flow gas of reactions were varied and studied; additionally, the physical properties of the chromium disilicide nanowires were measured. It was found that single-crystal CrSi2 nanowires with a unique morphology were grown at 700°C, while single-crystal Cr5Si3 nanowires were grown at 750°C in reducing gas atmosphere. The crystal structure and growth direction were identified, and the growth mechanism was proposed as well. This study with magnetism, photoluminescence, and field emission measurements demonstrates that CrSi2 nanowires are attractive choices for future applications in magnetic storage, photovoltaic, and field emitters.

Growth of single-crystalline cobalt silicide nanowires and their field emission property.

In this work, cobalt silicide nanowires were synthesized by chemical vapor deposition processes on Si (100) substrates with anhydrous cobalt chloride (CoCl2) as precursors. Processing parameters, including the temperature of Si (100) substrates, the gas flow rate, and the pressure of reactions were varied and studied; additionally, the physical properties of the cobalt silicide nanowires were measured. It was found that single-crystal CoSi nanowires were grown at 850°C ~ 880°C and at a lower gas flow rate, while single-crystal Co2Si nanowires were grown at 880°C ~ 900°C. The crystal structure and growth direction were identified, and the growth mechanism was proposed as well. This study with field emission measurements demonstrates that CoSi nanowires are attractive choices for future applications in field emitters.