Photoluminescence and thermoluminescence dosimetry properties of Ag/Y co-doped ZnO nanophosphor for radiation measurements.

This work explores the thermoluminescence (TL) and photoluminescence (PL) properties of Ag/Y co-doped zinc oxide (ZnO) nanophosphor. The proposed dosimeter was prepared by the coprecipitation method and sintered at temperatures from 400°C to 1000°C in an air atmosphere. Raman spectroscopy was studied to investigate the structural features of this composition. The new proposed dosimeter revealed two peaks at 150°C and 175°C with a small shoulder at high temperature (225°C). The PL spectrum showed strong green emissions between 500 to 550 nm. The Raman spectrum showed many bands related to the interaction between ZnO, silver (Ag), and yttrium oxide (Y2 O3 ). The rising sintering temperature enhanced the TL glow curve intensity. The Ag/Y co-doped ZnO nanophosphor showed an excellent linearity index within a dose from 1 to 4 Gy. The minimum detectable dose (MDD) of the Ag/Y co-doped ZnO nanopowder (pellets) equaled 0.518 mGy. The main TL properties were achieved in this work as follows: thermal fading (37% after 45 days at 1 and 4 Gy), optical fading (53% after 1 h and 68% after 6 h by exposure to sunlight), effective atomic number (27.6), and energy response (flat behavior from 0.1 to 1.3 MeV). Finally, the proposed material shows promising results nominated to be used for radiation measurements.

Exploring the properties of Dy2O3-Y2O3 Co-activated telluro-borate glass: Structural, physical, optical, thermal, and mechanical properties.

The successful application of glass-based materials in a wide range of scientific fields depends on the associated physical, optical, thermal, and mechanical properties. This article investigate the structural, Physical, thermal, optical, and mechanical properties of Dy2O3, Y2O3 co-activated telluro-borate glass developed using the melt-quenching method. The glassy quality and the elements component of the specimens were observed using XRD and EDX analyses. The addition of Y2O3 rise the glass density from 2.956 to 3.303 g/cm3 the refractive index from 2.5 to 2.7. These changes are due to the increase in polarizability and non-bridging oxygen (NBO). The photoluminescence (PL) spectra revealed a broad peak at 550 nm and additional weak emission peaks at 573 and 664 nm, respectively. While the observed broader peak can be linked to the convolution of Bi3+ ions transitions corresponding to the non-centrosymmetric site respectively, the weak emission bands are due to 4F9/2 â†’ 6H13/2 and 4F9/2 â†’ 6H11/2 Dy3+ transitions. Hence, the low symmetrical features of both Bi3+ and Dy3+ ions were confirmed. The increase in the Vickers hardness of the glass from 536.7 to 1366.9 indicates the influence of Y2O3 addition on the mechanical properties of the glasses. The findings help to improve our understanding of the behaviour of the glass composition and its prospective applications in disciplines such as photonic, and laser optics.

Development of Ag-Doped ZnO Thin Films and Thermoluminescence (TLD) Characteristics for Radiation Technology.

This work examined the thermoluminescence dosimetry characteristics of Ag-doped ZnO thin films. The hydrothermal method was employed to synthesize Ag-doped ZnO thin films with variant molarity of Ag (0, 0.5, 1.0, 3.0, and 5.0 mol%). The structure, morphology, and optical characteristics were investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDX), photoluminescence (PL), and UV-vis spectrophotometers. The thermoluminescence characteristics were examined by exposing the samples to X-ray radiation. It was obtained that the highest TL intensity for Ag-doped ZnO thin films appeared to correspond to 0.5 mol% of Ag, when the films were exposed to X-ray radiation. The results further showed that the glow curve has a single peak at 240-325 °C, with its maximum at 270 °C, which corresponded to the heating rate of 5 °C/s. The results of the annealing procedures showed the best TL response was found at 400 °C and 30 min. The dose-response revealed a good linear up to 4 Gy. The proposed sensitivity was 1.8 times higher than the TLD 100 chips. The thermal fading was recorded at 8% for 1 Gy and 20% for 4 Gy in the first hour. After 45 days of irradiation, the signal loss was recorded at 32% and 40% for the cases of 1 Gy and 4 Gy, respectively. The obtained optical fading results confirmed that all samples' stored signals were affected by the exposure to sunlight, which decreased up to 70% after 6 h. This new dosimeter exhibits good properties for radiation measurement, given its overgrowth (in terms of the glow curve) within 30 s (similar to the TLD 100 case), simple annealing procedure, and high sensitivity (two times that of the TLD 100).

Rapid Determination of Non-steroidal Anti-inflammatory Drugs in Aquatic Matrices by Two-phase Micro-electrodriven Membrane Extraction Combined with Liquid Chromatography.

Two-phase micro-electrodriven membrane extraction (EME) procedure for the pre-concentration of selected non-steroidal anti-inflammatory drugs (NSAIDs) in aquatic matrices was investigated. Agarose film was used as interface between donor and acceptor phase in EME which allowed for selective extraction of the analytes prior to high performance liquid chromatography-ultraviolet detection. Charged analytes were transported from basic aqueous sample solution through agarose film into 1-octanol as an acceptor phase at 9 V potential. Response surface methodology in conjunction with the central composite design showed good correlations between extraction time and applied voltage (R2 > 0.9358). Under optimized extraction conditions, the method showed good linearity in the concentration range of 0.5-500 µg L-1 with coefficients of determination, r2≥ 0.9942 and good limits of detection (0.14-0.42 µg L-1) and limits of quantification (0.52-1.21 µg L-1). The results also showed high enrichment factors (62-86) and good relative recoveries (72-114%) with acceptable reproducibilities (RSDs ≤ 7.5% n = 3). The method was successfully applied to the determination of NSAIDs from tap water and river water samples. The proposed method proved to be rapid, simple and requires low voltage and minute amounts of organic solvent, thus environmentally friendly.

Ionic liquid-impregnated agarose film two-phase micro-electrodriven membrane extraction (IL-AF-µ-EME) for the analysis of antidepressants in water samples.

The aim of this study was to investigate and apply supported ionic liquid membrane (SILM) in two-phase micro-electrodriven membrane extraction combined with high performance liquid chromatography-ultraviolet detection (HPLC-UV) for pre-concentration and determination of three selected antidepressant drugs in water samples. A thin agarose film impregnated with 1-hexyl-3-methylimidazolium hexafluorophosphate, [C6MIM] [PF6], was prepared and used as supported ionic liquid membrane between aqueous sample solution and acceptor phase for extraction of imipramine, amitriptyline and chlorpromazine. Under the optimized extraction conditions, the method provided good linearity in the range of 1.0-1000µgL-1, good coefficients of determination (r2=0.9974-0.9992) and low limits of detection (0.1-0.4µgL-1). The method showed high enrichment factors in the range of 110-150 and high relative recoveries in the range of 88.2-111.4% and 90.9-107.0%, for river water and tap water samples, respectively with RSDs of ≤7.6 (n=3). This method was successfully applied to the determination of the drugs in river and tap water samples. It is envisaged that the SILM improved the perm-selectivity by providing a pathway for targeted analytes which resulted in rapid extraction with high degree of selectivity and high enrichment factor.

Puzzle task ERP response: time-frequency and source localization analysis.

Perceptual decision making depends on the choices available for the presented task. Most event-related potential (ERP) experiments are designed with two options, such as YES or NO. In some cases, however, subjects may become confused about the presented task in such a way that they cannot provide a behavioral response. This study aims to put subjects into such a puzzled state in order to address the following questions: How does the brain respond during puzzling moments? And what is the brain's response to a non-answerable task? To address these questions, ERP were acquired from the brain during a scintillation grid illusion task. The subjects were required to count the number of illusory dots, a task that was impossible to perform. The results showed the presence of N130 over the parietal area during the puzzling task. Coherency among the brain hemispheres was enhanced with the complexity of the task. The neural generators' source localizations were projected to a multimodal complex covering the left postcentral gyrus, supramarginal gyrus, and angular gyrus. This study concludes that the brain component N130 is strongly related to perception in a puzzling task network but not the visual processing network.