Adsorption-capacitive deionization hybrid system with activated carbon of modified potential of zero charge.

In this study water solutions are desalinated with carbon electrodes of modified surface charges. The idea is to endow the electrodes with the ability to physically adsorb salt ions without applying potential so as to save energy. The modification enhanced to decrease the energy consumption of a newly invented adsorption-CDI hybrid system by 19%, since modified activated carbon cell consumed 0.620 (relative error 3.00%) kWh/m3 compared to pristine activated carbon cell which consumed 0.746 (relative error 1.20%) kWh/m3. Further analysis revealed high adsorption capacity of the modified activated carbon electrode cell which exhibited 9.0 (relative error 2.22%) compared to activated carbon cell with 5.3 (relative error 5.66%) mg g-1. These results show the potential of surface modification in adding value to low cost activated carbons for application in CDI.

Sub- and Supercritical Water Gasification of Rice Husk: Parametric Optimization Using the I-Optimality Criterion.

In this study, rice husk biomass was gasified under sub- and supercritical water conditions in an autoclave reactor. The effect of temperature (350-500 °C), residence time (30-120 min), and feed concentration (3-10 wt %) was experimentally studied using the response surface methodology in relation to the yield of gasification products. The quadratic models have been suggested for both responses. Based on the models, the quantitative relationship between various operational conditions and the responses will reliably forecast the experimental outcomes. The findings revealed that higher temperatures, longer residence times, and lower feed concentrations favored high gas yields. The lowest tar yield obtained was 2.98 wt %, while the highest gasification efficiency and gas volume attained were 64.27% and 423 mL/g, respectively. The ANOVA test showed that the order of the effects of the factors on all responses except gravimetric tar yield follows temperature > feed concentration > residence time. The gravimetric tar yield followed a different trend: temperature > residence time > feed concentration. The results revealed that SCW gasification could provide an effective mechanism for transforming the energy content of RH into a substantial fuel product.