RESUMO
Unlike ferromagnetic materials, ferrimagnetic metals have recently received considerable attention due to their bulk perpendicular magnetic anisotropy, low net magnetization and tunable magnetic properties. This makes them perfect candidates for the research of recently discovered spin-torque related phenomena. Among other ferrimagnetic metals, GdFe has an advantage in relatively large magnetic moments in both sublattices and tunability of compensation point above the room temperature by small changes in its composition. We present a systematic study of optical and magneto-optical properties of amorphous GdxFe(100-x) thin films of various compositions (x = 18.3, 20.0, 24.7, 26.7) prepared by DC sputtering on thermally oxidized SiO2 substrates. A combination of spectroscopic ellipsometry and magneto-optical spectroscopy in the photon energy range from 1.5 to 5.5 eV with advanced theoretical models allowed us to deduce the spectral dependence of complete permittivity tensors across the compensation point. Such information is important for further optical detection of spin related phenomena driven by vicinity of compensation point in nanostructures containing GdFe.
RESUMO
Optical and magneto-optical properties of amorphous Gd22Fe78 (GdFe) thin films prepared by direct current (DC) sputtering on thermally oxidized substrates were characterized by the combination of spectroscopic ellipsometry and magneto-optical spectroscopy in the photon energy range from 1.5 to 5.5 eV. Thin SiNx and Ru coatings were used to prevent the GdFe surface oxidation and contamination. Using advanced theoretical models spectral dependence of the complete permittivity tensor and spectral dependence of the absorption coefficient were deduced from experimental data. No significant changes in the optical properties upon different coatings were observed, indicating reliability of used analysis.
RESUMO
Two-phase nanocomposite films consisting of metallic Co nanoparticles below 50 nm diameter in a perovskite matrix were grown by pulsed laser deposition onto (LaAlO3)0.3(Sr2AlTaO6)0.7 (LSAT) and silicon substrates from a target of SrGa0.73Co0.27O3. The particles made up about 6% by volume of the film and were present within the film and at the substrate interface. The saturation magnetization of the film was up to 85 emu cm(-3) at 80 nm thickness and the Faraday rotation (FR) tracked the out-of-plane hysteresis loop, reaching 3000 deg cm(-1) at 10 kOe for 1550 nm wavelength. The magneto-optical figure of merit defined as FR divided by optical absorption was 0.04-0.06 deg dB(-1) due to the high optical absorption of the Co particles.