Volume Deformation and Hydration Behavior of Ordinary Portland Cement/Calcium Sulfoaluminate Cement Blends.

Blends of ordinary Portland cement (OPC) and calcium sulfoaluminate (CSA) cement can be used to adjust the properties of cement for specific applications. In this study, CSA cement was used as a shrinkage-compensating admixture to improve the hydration behavior and performance (compressive strength and drying shrinkage) of OPC; the expansion behavior of the blended cement mortar was evaluate based on the saturation index of ettringite. The experimental results showed that incorporating CSA cement resulted in a delayed effect on the hydration of C3S, shortened the induction periods of the blended cement and decreased the setting time. The CSA cement also improved the early compressive strength and drying shrinkage of the OPC due to its compact microstructure. The drying shrinkage of the OPC mortar decreased by 27.8% when 6% CSA cement was used, but the formation of microcracks due to expansion could negatively impact its late compressive strength development and associated pore structures of the blends when the replacement content of CSA cement exceeded 6 wt.%. The results relevant to the expansion behavior of the CSA cements could induce crystallization stress, enhancing its resistance against shrinkage cracking.

Quantitative Evaluation of Carbon Fiber Dispersion in Amorphous Calcium Silicate Hydrate-Based Contact-Hardening Composites.

Carbon fiber dispersion has a substantial influence on the properties of amorphous calcium silicate hydrate-based contact-hardening composites. In this study, a mixture of carbon fiber and calcium silicate hydrate powder was compressed into solid composites at 40 MPa for one minute. The mechanical properties and electrical resistivity of the solid materials were measured, and the dispersion of carbon fibers was quantitatively evaluated by digital image processing technology. The Taipalu model was used to build the correlation between the electrical resistivity of the composites and the carbon fiber dispersion. The results of the electrical resistivity showed that the down threshold of carbon fiber content in the contact-hardening composites was 1.0 wt.% and the electrical resistivity was 30,000 Ω·cm. As the fiber content increased to 2.0 wt.%, the electrical resistivity dropped to 2550 Ω·cm, which was attributed to the increase in fiber dispersion uniformity in the solid composites, and the value of the fiber distribution coefficient reached a maximum value of 0.743. A subsequent decrease in the uniformity of the fiber dispersion was observed at a high fiber content. In addition, the carbon fiber content showed a slight influence on the fiber orientation in the contact-hardening composites.