RESUMO
The areal density of hard disk drives increases every year. Increasing the areal density has limitations. Therefore, heat-assisted magnetic recording (HAMR) technology has been the candidate for increasing the areal density. At ultrahigh areal density, the main problem of the magnetic recording process is noise. Transition jitter is noise that affects the read-back signal. Hence, the performance of the magnetic recording process depends on the transition jitter. In this paper, the transition jitter of L10-FePt-based HAMR technology was simulated at the ultrahigh areal density. The micromagnetic simulation was used in the magnetic recording process. The average grain size was 5.1 nm, and the standard deviation was 0.08 nm. The recording simulation format was five tracks in a medium. It was found that a bit length of 9 nm with a track width of 16.5 nm at the areal density of 4.1 Tb/in2 had the lowest transition jitter average of 1.547 nm. In addition, the transition jitter average decreased when increasing the areal density from 4.1 to 8.9 Tb/in2. It was found that the lowest transition jitter average was 1.270 nm at an 8 nm track width and a 9 nm bit length, which achieved an ultrahigh areal density of 8.9 Tb/in2.
RESUMO
In this work, we propose exchange-coupled-composite-bit-patterned media (ECC-BPM) with microwave-assisted magnetic recording (MAMR) to improve the writability of the magnetic media at a 4 Tb/in2 recording density. The suitable values of the applied microwave field's frequency and the exchange coupling between magnetic dots, Adot, of the proposed media were evaluated. It was found that the magnitude of the switching field, Hsw, of the bilayer ECC-BPM is significantly lower than that of a conventional BPM. Additionally, using the MAMR enables further reduction of Hsw of the ECC-BPM. The suitable frequency of the applied microwave field for the proposed media is 5 GHz. The dependence of Adot on the Hsw was additionally examined, showing that the Adot of 0.14 pJ/m is the most suitable value for the proposed bilayer ECC-BPM. The physical explanation of the Hsw of the media under a variation of MAMR and Adot was given. Hysteresis loops and the magnetic domain of the media were characterized to provide further details on the results. The lowest Hsw found in our proposed media is 12.2 kOe, achieved by the bilayer ECC-BPM with an Adot of 0.14 pJ/m using a 5 GHz MAMR.
RESUMO
Azulene samples in ethanol/distilled water (1, 10 and 100 µm) were irradiated with a 638 nm red laser (0.5 watts, light-to-target distance 2 cm, energy density 4 or 40 J cm-2 ) by either continuous, fractionation or pulse mode. Singlet oxygen in the samples was measured using 10 µm 9,10-dimethyl anthracene (positive control 10 µm erythrosine) and relative fluorescence intensities were measured at 375/436 nm excitation/emission. Peripheral blood mononuclear cells (PBMCs, 1 × 105 cells/well) preincubated with 0.01 µg mL-1 rhTNF-α for 6 h were cultured with irradiated azulene samples in RPMI-1640 under standard conditions. PGE2 was quantified by rhPGE2 ELISA kit using a Varioscan® microplate reader at an excitation wavelength of 420 nm. Kruskal Wallis with Dunn`s test was performed at a significance level of P < 0.05. The highest singlet oxygen amount was found in 10 µm azulene samples irradiated at 40 J cm-2 under continuous mode (P = 0.001 when compared with 10 µm erythrosine). PGE2 expression in rhTNF-α-induced PBMCs was reduced to 45% of control by 1 µm azulene irradiated at 40 J cm-2 under fractionation mode. Fractionation mode with intermediate laser energy density in the presence of low concentration of azulene could increase singlet oxygen and tend to reduce PGE2 .