Vat photopolymerization (VP) is a high-throughput additive manufacturing modality that also offers exceptional feature resolution and surface finish; however, the process is constrained by a limited selection of processable photocurable resins. Low resin viscosity (<10 Pa·s) is one of the most stringent process-induced constraints on resin processability, which in turn limits the mechanical performance of printed resin systems. Recently, the authors created a VP-processable photosensitive latex resin, where compartmentalization of the high molecular weight polymer chains into discrete particles resulted in the decoupling of viscosity from molecular weight. However, the monomers used to form the hydrogel green body resulted in decreased ultimate material properties due to the high cross-link density. Herein, we report a novel scaffold that allows for facile UV-based AM and simultaneously enhances the final part's material properties. This is achieved with a chemically labile acetal-containing cross-linker in conjunction with N-vinylpyrrolidone, which forms a glassy polymer after photocuring. Subsequent reactive extraction cleaves the cross-links and liberates the glassy polymer, which provides mechanical reinforcement of the geometrically complex VP-printed elastomer. With only a 0.1 wt % loading of photoinitiator, G'/G'' crossover times of less than 1 s and green body plateau moduli nearing 105 Pa are obtained. In addition, removal of the hydrophilic and thermally labile scaffold results in decreased water uptake and increased thermal stability of the final printed part. Ultimate strain and stress values of over 650% and 8.5 MPa, respectively, are achieved, setting a new benchmark for styrene-butadiene VP elastomers.
RESUMO
Vat photopolymerization (VP) additive manufacturing fabricates intricate geometries with excellent resolution; however, high molecular weight polymers are not amenable to VP due to concomitant high solution and melt viscosities. Thus, a challenging paradox arises between printability and mechanical performance. This report describes concurrent photopolymer and VP system design to navigate this paradox with the unprecedented use of polymeric colloids (latexes) that effectively decouple the dependency of viscosity on molecular weight. Photocrosslinking of a continuous-phase scaffold, which surrounds the latex particles, combined with in situ computer-vision print parameter optimization, which compensates for light scattering, enables high-resolution VP of high molecular weight polymer latexes as particle-embedded green bodies. Thermal post-processing promotes coalescence of the dispersed particles throughout the scaffold, forming a semi-interpenetrating polymer network without loss in part resolution. Printing a styrene-butadiene rubber latex, a previously inaccessible elastomer composition for VP, exemplified this approach and yielded printed elastomers with precise geometry and tensile extensibilities exceeding 500%.